316不锈钢在F-/Cl-酸性溶液中的腐蚀行为

李谋成;曾潮流;林海潮

中科院金属腐蚀与防护研究所

CORROSION BEHAVIOR OF 316 STAINLESS STEEL IN SOLUTIONS CONTAINING F-/Cl- IONS

Moucheng Li;Chaoliu Zeng;Haichao Lin

中科院金属腐蚀与防护研究所

全文: PDF(140 KB)

摘要: 用电化学测量技术，对含F-和Cl-稀醋酸介质中316不锈钢的腐蚀行为进行了研究.结果表明，316不锈钢在低浓度F-/Cl-稀醋酸溶液中能够钝化，致密钝化膜为双层结构；F-能加速其均匀腐蚀，但加速作用不显著，浓度不同的含F -稀醋酸介质中均无点蚀.

关键词 ：不锈钢, 腐蚀, 电化学阻抗谱, 燃料电池

Abstract：The corrosion behavior of 316 stainless steel (316S S) in dilute acetic acid solutions containing fluoride/chloride ions was investi gated by using electrochemical measurement techniques.It was found that 316 coul d be passivated in 0.1 mol/L HAc solution mixed with 0.001 mol/L NaF and 0.001mo l/L NaCl or with 0～0.1 mol/L NaF.The well passivated films had an internal chro mium oxide rich layer and an external iron oxide rich layer.The results revealed that F- could increase corrosion rate slightly for 316SS in 0.1 mol/L HAc sol ution.No pitting corrosion occurred in the various tested solutions.The corrosio n rate of 316SS increased with increasing the temperature of solutions containin g F-/Cl- ions,but 316SS was still in the passive state at 80℃.

Key words： stainless steel corrosion electrochemical impedance sp ectroscopy fuel cell

收稿日期: 2000-11-14

ZTFLH:

TG172.36

通讯作者: 李谋成

Corresponding author: Moucheng Li

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李谋成
	曾潮流
	林海潮
44.8K

引用本文:

李谋成; 曾潮流; 林海潮 . 316不锈钢在F-/Cl-酸性溶液中的腐蚀行为[J]. 中国腐蚀与防护学报, 2002, 22(3): 162-166 .
Moucheng Li, Chaoliu Zeng, Haichao Lin. CORROSION BEHAVIOR OF 316 STAINLESS STEEL IN SOLUTIONS CONTAINING F-/Cl- IONS. J Chin Soc Corr Pro, 2002, 22(3): 162-166 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2002/V22/I3/162

[1]MurphyOJ ,CisarA ,ClarkeE .Low-costlightweighthighpowerdensityPEMfuelcellstack[J].Electrochim.Acta,1998,43(24):3829-3840
[2]DaviesDP ,AdcockPL ,TurpinM ,etal.Bipolarplateforsolidpolymerfuelcells[J].J.Appl.Electrochem.,2000,30:101-105
[3]HornungR ,KappeltG .BipolarplatematerialsdevelopmentusingFe-basedalloysforsolidpolymerfuelcells[J].J .PowerSources,1998,72:20-21
[4]StrehblowHH .Breakdownofpassivityandlocalizedcorrosion:theoreticalconceptsandfundamentalexperimentalresults[J].WerkstoffeundKorrosion,1984,35:437-448
[5]SekineI,UsuiH ,KitagawaS ,etal.TheeffectoffluorideionsonthecorrosionofsteelmaterialsinH2SO4 andCH3COOHsolutions[J].Corros.Sci.,1994,36(8):1411-1424
[6]MacDonaldDD ,OwenD .Theelectrochemistryofironin1Mlithi umhydroxidesolutionat22and200℃[J].J .Electrochem.Soc.,1973,120(3):317-324
[7]WuXJ,MaHY ,ChenSH ,etal.Generalequivalentcircuitsforfaradicelectrodesprocessunderelectrochemicalreactioncontrol[J].J.Electrochem.Soc.,1999,146(5):1847-1853
[8]SchultzeJW ,LohrengelMM .Stability,reactivityandbreakdownofpassivefilms[J].Electrochim.Acta,2000,45:2499-2513
[9]YangMZ ,LuoJL ,YangQ ,etal.Effectsofhydrogenonsemicon ductivityofpassivefilmsandcorrosionbehaviorof316stainlesssteel[J].J.Electrochem.Soc.,1999,146(6):2107-2112
[10]MontemorMF ,FerreiraMGS ,HakikiNE ,etal.Chemicalcom positionandelectronicstructureofoxidefilmsformedon316Lstainlesssteelandnickelbasedalloysinhightemperatureaqueousenvironments[J].Corros.Sci.,2000,42:1635-1650

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[12]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[13]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[14]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[15]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.

Viewed

Full text

Abstract

Cited

Shared

Discussed