真空热处理对镍基单晶高温合金溅射NiCrAlY涂层抗氧化性能的影响

中国腐蚀与防护学报

2002, Vol. 22

Issue (3): 153-157

研究报告

本期目录 | 过刊浏览

真空热处理对镍基单晶高温合金溅射NiCrAlY涂层抗氧化性能的影响

李美恒;张重远;孙晓峰

中科院金属所

EFFECT OF VACUUM HEAT TREATMENT ON OXIDATION RESISTANCE OF SPUTTERED NiCrAlY COATING ONA Ni-BASE SINGLE-CRYSTAL SUPERALLOY

Meiheng Li;Zhongyuan Zhang;Xiaofeng Sun

中科院金属所

全文: PDF(254 KB)

摘要: 用磁控溅射法在镍基单晶高温合金基体上沉积NiCrAlY涂层，研究了真空热处理对涂层组织结构及抗氧化性能的影响.结果表明，溅射NiCrAlY涂层主要由γ-Ni和β-NiAl两相组成，元素分布均匀；经真空热处理后，涂层主要由γ′-Ni3Al 、β-NiAl相和极少量的α-Al2O3相组成，元素分布变得不均匀，最外层富Al贫Cr.真空热处理可使溅射NiCrAlY涂层表面较早生成保护性能良好的α-Al2O3.1000℃氧化200 h ，溅射涂层氧化膜有较大部分已经剥落，但真空热处理涂层的氧化膜仍较好地粘附在涂层基体上.真空热处理使溅射NiCrAlY涂层表面生成的氧化膜粘附性更好，提高了溅射NiCrAlY涂层的抗氧化性能.

关键词 ：溅射, NiCrAlY涂层, 真空热处理, 抗氧化性

Abstract：The influence of vacuum heat treatment on NiCrAlY c oating,which was deposited on a Ni-base superalloy substrate by magnetron sputte ring was investigated.It was shown that the sputtered NiCrAlY coating,which cons isted of a two-phase mixture:γ-Ni and β-NiAl phase,had a homogeneous elemental distribution.After vacuum heat treatment,the sputtered NiCrAlY coating mainly c onsisted of γ′-Ni3Al,β-NiAl,and trace of α-Al2O3 phases and the outerm ost layer of the sputtered NiCrAlY coating riched in Al and depleted in Cr.The s puttered NiCrAlY coating after vacuum heat treatment formed α-Al2O3 much ea rlier and the α-Al2O3 scale had a better adherence to the NiCrAlY coating.T herefore vacuum heat treatment improved the oxidation resistance of sputtered Ni CrAlY coating.

Key words： sputtering NiCrAlY coating vacuum heat treatment oxida tion resistance

收稿日期: 2000-11-29

ZTFLH:

TG174.451

通讯作者: 李美恒

Corresponding author: Meiheng Li

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李美恒
	张重远
	孙晓峰
44.8K

引用本文:

李美恒; 张重远; 孙晓峰 . 真空热处理对镍基单晶高温合金溅射NiCrAlY涂层抗氧化性能的影响[J]. 中国腐蚀与防护学报, 2002, 22(3): 153-157 .
Meiheng Li, Zhongyuan Zhang, Xiaofeng Sun. EFFECT OF VACUUM HEAT TREATMENT ON OXIDATION RESISTANCE OF SPUTTERED NiCrAlY COATING ONA Ni-BASE SINGLE-CRYSTAL SUPERALLOY. J Chin Soc Corr Pro, 2002, 22(3): 153-157 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2002/V22/I3/153

[1]MillerRA .Currentstatusofthermalbarriercoatings-anoverview[J].Surf.Coat.Technol.,1987,30:1-11
[2]CzechN ,FietzekH ,Juez-LorenzoM ,KolarikV ,StammW .Stud iesofthebond-coatoxidationphasestructureofTBCs[J].Surf.Coat.Technol.,1999,113:157-164
[3]LouHY ,TangYJ,SunXF ,GuanHR .Oxidationbehaviourofsputteredmicro-grainedsuperalloyK17Fathightemperatures[J].ActaMetall.Sin.,1994,30(3):B109-115(楼翰一,唐幼军,孙晓峰,管恒荣.K17F高温合金溅射微晶层的抗高温氧化行为[J].金属学报,1994,30(3):B109-115)
[4]LeyensC ,FritscherK ,GehrlingR ,PetersM ,KaysserWA .OxidescaleformationonaMCrAlYcoatinginvariousH2-H2Oatmo spheres[J].Surf.Coat.Technol.,1996,82:133-144
[5]DoychakJ ,SmialekJL ,MitchellTE .Transientoxidationofsingle-crystal-NiAl[J].Metall.Trans.A .1989,20A(3):499-518
[6]PintBA ,TreskaM ,HobbsLW .Theeffectofvariousoxidedis persionsonthephasecompositionandmorphologyofAl2O3scalesgrownonβ-NiAl[J].Oxid.Met.,1997,47(1/2):1-20
[7]TienJK ,PettitFS .MechanismofoxidationadherenceonFe-25Cr-4Al(YorSc)alloys[J].Metall.Trans.,1972,3(6):1587-1599
[8]BrandlW ,TomaD ,GrabkeHJ .ThecharacteristicsofaluminascalesformedonHVOF -sprayedMCrAlYcoatings[J].Surf.Coat.Technol.,1998,108/109:10-15
[9]KumarA ,NasrallahM ,DouglassDL .EffectofYtandThontheoxidationbehaviourofNi-Cr-Alalloys[J].Oxid.Met.,1974,8(4):227-263
[10]ZhuRZ ,HeYD ,QiHB .HighTemperatureCorrosion&Materi alsResistanttoHighTempertureCorrosion[M ].Shanghai:Shang haiScienceandTechnologyPress,1995,192(朱日彰,何业东,齐慧滨编著.高温腐蚀及耐高温腐蚀材料[M ].上海:上海科学技术出版社,1995,192)

[1]	骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[2]	史昆玉,张进中,张毅,万毅. Nb₂N涂层制备及其耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[3]	孙超, 杨潇, 文玉华. 表面溅射高含铝奥氏体不锈钢合金涂层对316不锈钢抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 590-596.
[4]	杨甜甜,徐敬军,钱余海,李美栓. 石墨基体上ZrC/MoSi₂微叠层涂层的制备及抗超高温氧化性能[J]. 中国腐蚀与防护学报, 2016, 36(5): 476-482.
[5]	晏敏胜, 何进, 冒守栋, 杨丽景, 聂霞, 宋振纶, 詹肇麟. NiCrAlY薄膜对Sm₂Co₁₇磁体高温抗氧化性的影响[J]. 中国腐蚀与防护学报, 2015, 35(2): 183-188.
[6]	任鑫; 汪信; 王福会 . 溅射NiCrAlY渗铝涂层的高温氧化行为[J]. 中国腐蚀与防护学报, 2006, 26(6): 365-370 .
[7]	吕海波; 李瑛; 王福会 . 纳米化对Cu-20Zr合金腐蚀行为的改善[J]. 中国腐蚀与防护学报, 2006, 26(3): 171-175 .
[8]	吕海波; 李瑛; 王福会 . Cu-20Zr合金在盐酸溶液中的脱合金腐蚀历程[J]. 中国腐蚀与防护学报, 2006, 26(2): 75-79 .
[9]	孟国哲; 李瑛; 王福会 . Fe-20Cr纳米涂层的电化学行为[J]. 中国腐蚀与防护学报, 2006, 26(1): 11-18 .
[10]	田秀娟; 王福会; 李庆芬 . 搪瓷／NiCrAlY复合涂层的抗高温氧化及热腐蚀行为[J]. 中国腐蚀与防护学报, 2005, 25(6): 344-350 .
[11]	耿树江; 朱圣龙; 王福会 . 纯Ni及其溅射纳米晶的高温氧化行为[J]. 中国腐蚀与防护学报, 2003, 23(6): 335-339 .
[12]	耿树江; 朱圣龙; 王福会 . 在600℃～700℃固态NaCl和水蒸气综合作用下K38G及其纳米晶涂层的腐蚀行为[J]. 中国腐蚀与防护学报, 2003, 23(4): 193-197 .
[13]	李雪莉; 李瑛; 王福会 . Fe20Cr溅射纳米涂层腐蚀电化学性能研究[J]. 中国腐蚀与防护学报, 2003, 23(2): 84-88 .
[14]	李瑛; 耿树江; 王福会 . 磁控溅射IN738涂层耐盐水腐蚀性能研究[J]. 中国腐蚀与防护学报, 2002, 22(6): 349-354 .
[15]	张玉娟; 孙晓峰; 金涛 . 两种NiCrAlY涂层1050℃恒温抗氧化性能[J]. 中国腐蚀与防护学报, 2002, 22(6): 339-342 .

Viewed

Full text

Abstract

Cited

Shared

Discussed