氢致裂纹扩展的分形研究进展

中国腐蚀与防护学报

2001, Vol. 21

Issue (3): 188-192

综述

本期目录 | 过刊浏览

氢致裂纹扩展的分形研究进展

董绍华;吕英民;李启楷

北京石油大学

FRACTAL STUDY DEVELOPMENTS OF HYDROGEN INDUCED CRACKIN G

;;

北京石油大学

全文: PDF(144 KB)

摘要: 阐述了分形断裂的发展及应用，指出分形应用于材料的断口分析，可从实验方面和理论方面得出分维D与材料特性、物理量的关系.总结了国内外氢致裂纹扩展的分形研究成果，表明了分形断裂力学引入可为环境断裂研究提供新思路.

关键词 ：氢致开裂, 分形, 分维, 断口分析

Abstract：Developments and applications of fractal fracture a re illustrated,for the fracture analysis applied by fractal,fractal dimension and material properties and physical relationships are given by experiments or theory.Many progress made for the fractal of hydrogen-induced cracking are summ arized,and it showed that fractal fracture mechanics can supply a new method fo r environment fracture research.

Key words： hydrogen induced cracking fractal fractal dimension fracture

收稿日期: 2000-01-03

ZTFLH:

O346.2+2/TG172.2

通讯作者: 董绍华

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	董绍华
	吕英民
	李启楷
44.8K

引用本文:

董绍华; 吕英民; 李启楷 . 氢致裂纹扩展的分形研究进展[J]. 中国腐蚀与防护学报, 2001, 21(3): 188-192 .

链接本文:

https://www.jcscp.org/CN/Y2001/V21/I3/188

[1]MandebrotBB ,PassojaDE ,PaullayAJ .Fractalcharacteroffracturesurfacesofmetals[J].Nature,1984,308:721-723
[2]FalconerJ.Fractals[M].NewYork:PlenumPress,1988
[3]PanaglotopoulosPD ,etal.Fractalgeometryandfractalmaterialbehaviourinsolidsandstructures[J].ArchieveofAppl.Mech.1993,63:1-24
[4]AlbertoCarpinteri.Fractalnatureofmaterialmicrostructureandsizeeffectsonapparentmechanicalproperties[J].MechanicsandMaterials,1994,18:89-101
[5]CharkalukE ,BigerelleM ,LostA .FractalsandFracture[J].Eng.Frac.Mech.,1998,61:119-139
[6]PandeCS ,RichardLR .Fracturecharacterizationoffracturesurface[J].J.Mater.Sci.Lett.,1987,6:295-297
[7]XieHeping.MathematicalBasicandApplicationonFractalGeometry[M ].Chongqing:ChongqingUniversityPress,1991(谢和平.分形几何的数学基础和应用[M].重庆:重庆大学出版社,1991)
[8]LiQK .Onedimensionfractalscurvesanddeterminationoffractaldimension[J].J .UniversityofSci&TechBeijing,1998,3:163-166
[9]DebucB ,QuiniouJF ,Rouques-CarmesC ,etal.Evaluatingthefractaldimensionofprofiles[J].Phys.Rev.,1989,39(3):1500-1512
[10]MuZK ,LungCW .Studiesonthefractaldimensionandfractaltoughnessofsteels[J].J.PhysD .,1988,21:848-850
[11]SuH ,ZhangY ,YanZ .Fractalanalysisofmicrostructureandpropertiesinferrite-martensitesteels[J].ScriptaMetallMater,1991,25:651-654
[12]SaonmaVE ,BartonC .Fractals、fractureandsizeeffectsinconcrete[J].J .Engng.Mech.,1994,120(4):835-854
[13]WangZG ,ChenDL ,JiangXX ,AiSH ,ShihCH .Relationshipbetweenfractaldimensionandfatiguethresholdvalueindual-phasesteels[J].ScriptaMet.,1988,22:827-832
[14]LinGM ,LaiJKL .Fractalcharacterizationoffracturesurfaceinaresin-basedcomposite[J].J.Mater.Sci.Lett.,1993,12:470-472
[15]HiroyukiNagahama.Afractalcriterionforductileandbrittlefracture[J].J.Appl.Phys.,1994,75:3220-3222
[16]ZhangGuanren.Fractaldimensionofductileandbrittlefracture[J].ExplosionandShockWaves,1996,16(2):117-122(章冠人.韧性和脆性断裂的分形维数[J].爆炸与冲击,1996,16:117-122)
[17]PandeCS ,RichardsLR ,SmithS .Fractalcharacteristicsoffracturedsurfaces[J].J.Mater.Sci.Lett.,1987,6:295-297
[18]PandeCS ,RichardsLR ,LouatN ,DempseyBD ,SchwoebleAJ.Fractalcharacterizationoffracturedsurfaces[J].Acta.Met all,1987,35(7):1633-1637
[19]RichardsLR ,DempseyBDFractalcharacterizationoffracturedsurfacesinTi-4.5Al-5.0Mo-1.5[J].Scripta.Met.,1988,22:687-689
[20]RayKK ,MandalG .Studyofcorrelationbetweenfractaldimensionandimpactenergyinahighstrengthlowalloysteel[J].Acta.Metall.Mater.,1990,24:967-972
[21]BorodichFW .Somefractalmodeloffracture[J].J.Mech.Phy.Solids.,1997,45:239-259
[22]GenadyPCherepanov.Fractalfracturemechanics-Areview[J].Eng.Frac.Mech.,1995,51:997-1033
[23]MosolovAB .Mechanicsoffractalcracksinbrittlesolids[J].EurophysicsLetters,1993,24:673-678
[24]BoGong,Zuhanlai.FractalcharacteristicsofJ-RresistancecurvesofTi-6Al-4Valloys[J].Eng.Frac.Mech.,1993,44:991-995
[25]HisiungJC ,ChouYC .Fractalcharacterizationofthefracturesurfaceofahigh-strengthlow-alloysteel[J].J .Mater.Sci.,1998,33:2949-2953
[26]JiangXG ,ChuWY ,XiaoJM .FractalanalysisoforientationeffectonKIC[J].Engng.FractureMech.,1995,51:805-808
[27]LongQY ,ChenJ,MuZK ,LungCW .Astudyonfractaldimensionoffracturesurfacecreatedbystresscorrosioncrackinginhighstrengthsteels[J].ScriptaMetallMater,1992,27:1319-1324
[28]LongQiyi,etal.Fractaldimensionanalysisforslow propagationzoneofhydrogeninducedcracking[J].MaterialSciencePer formance,1990,4:241-246(龙起易等.氢致裂纹慢扩展区断裂表面的分维研究[J].材料科学进展,1990,4:241-246)
[29]ZhangYue.Investigationoffractaldimensionofhydrogen-inducedbrittlefracturetitaniumaluminide[J].MaterialsScienceandEngineering,1994,177A :L1-L5
[30]JiangXingang,etal.Fractalanalysisforhydrogeninducedductilitylosses[J].ActaMetallurgicaSinica,1994,30(6):A265-269(蒋兴钢等.氢致塑性损失的分形研究[J].金属学报,1994,30:A265-269)
[31]MasashiKurose,YukioHirose,ToshihikoSasaki.FractalcharacteristicsofstresscorrosioncrackinginSNCM 439steeldiffer entsprior-austenitegrainsizes[J].Eng.Frac.Mech.,1996,53:279-288
[32]XiaoRuozhenlun(Janpanese).MetallicCorrosionCracksandTechnologyofCorrosionPrevention[M ].Beijing:ChemicalIn dustryPress,1988(小若正伦(日).金属的腐蚀破坏与防蚀技术[M ].北京:化学工业出版社,1988)
[33]DongShaohua,etal.Fractalmodelofhydrogeninducedcracking[J].J .Chin.Soc.Corrosion&Prot.,2001,21(2):106-111(董绍华等.氢致裂纹扩展的分形模型[J].中国腐蚀与防护学报,2001,21(2):106-111)

[1]	王保杰,栾吉瑜,王士栋,许道奎. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.
[2]	郭强, 陈长风, 李世瀚, 于浩波, 李鹤林. 冷焊修复层在H₂S环境下的开裂行为研究[J]. 中国腐蚀与防护学报, 2018, 38(2): 167-173.
[3]	史显波, 王威, 严伟, 单以银, 杨柯. M/A组元对高强度管线钢抗H₂S性能的影响[J]. 中国腐蚀与防护学报, 2015, 35(2): 129-136.
[4]	王斌, 周翠, 李良君, 胡红梅, 朱加祥. X100管线钢焊接接头抗HIC性能研究[J]. 中国腐蚀与防护学报, 2014, 34(3): 237-242.
[5]	董希青,黄彦良. 不锈钢在海洋环境中的环境敏感断裂研究进展[J]. 中国腐蚀与防护学报, 2012, 32(3): 189-194.
[6]	姚学军,王俭秋,左景辉,韩恩厚,柯伟. 微观组织对X52钢抗H₂S腐蚀和开裂性能的影响[J]. 中国腐蚀与防护学报, 2012, 32(2): 95-101.
[7]	翁永基. 腐蚀预测和计量学基础[J]. 中国腐蚀与防护学报, 2011, 31(4): 245-249.
[8]	饶思贤,万章,宋光雄,张铮,钟群鹏. 基于规则的晶间腐蚀和氢致开裂的失效模式诊断[J]. 中国腐蚀与防护学报, 2011, 31(4): 260-264.
[9]	镇凡;刘静;黄峰;程吉浩;李翠玲;郭斌;徐进桥. 夹杂物对X120管线钢氢致开裂的影响[J]. 中国腐蚀与防护学报, 2010, 30(2): 145-149.
[10]	邵绪分 . X70管线钢近中性环境氢致开裂与阳极溶解的关系[J]. 中国腐蚀与防护学报, 2008, 28(2): 76-80 .
[11]	许述剑; 翁永基; 李相怡 . 图像分维对腐蚀坑分布特征的表征[J]. 中国腐蚀与防护学报, 2007, 27(2): 109-113 .
[12]	翁永基; 许述剑; 边丽 . 腐蚀和腐蚀模型研究中的分形方法[J]. 中国腐蚀与防护学报, 2006, 26(5): 315-320 .
[13]	翁永基; 李相怡 . 土壤中碳钢平均腐蚀速度统计特征的分形研究[J]. 中国腐蚀与防护学报, 2005, 25(4): 200-204 .
[14]	董绍华; 吕英民 . 氢致裂纹扩展的分形模型[J]. 中国腐蚀与防护学报, 2001, 21(2): 106-111 .
[15]	王燕斌; 王胜; 颜练武 . 塑性变形在氢致断裂中的作用[J]. 中国腐蚀与防护学报, 2000, 20(4): 248-252 .

Viewed

Full text

Abstract

Cited

Shared

Discussed