NaCl盐膜和水蒸气对纯Cr腐蚀行为的影响

中国腐蚀与防护学报

2000, Vol. 20

Issue (2): 88-96

研究报告

本期目录 | 过刊浏览

NaCl盐膜和水蒸气对纯Cr腐蚀行为的影响

舒勇华;王福会;吴维tao

中科院力学所高温气体动力学开放实验室

Effect of NaCl Deposit and Water Vapor on the Corrosion Behavior of Pure Cr at 500-700℃

Yonghua Shu;;

中科院力学所高温气体动力学开放实验室

全文: PDF(269 KB)

摘要: 研究了500-700℃纯Cr在NaCl盐膜及水蒸气作用下的腐蚀行为.结果表明,在单纯空气或O2+H2O混合气氛中,由于表面生成了一层连续致密的Cr2O3保护膜,即使在较高温度(700℃)下其腐蚀增重也较小,表现出良好的抗腐蚀性能.但在NaCl+空气或NaCl+O2+H2O高,Cr的腐蚀越严重.根据实验结果,讨论了NaCl加速Cr腐蚀的作用机制.

关键词 ：纯Cr, 固态NaCl, 水蒸气, 协同作用, 腐蚀

Abstract：Themogravimetric studies have been conducted on the corrosion behavior of pure chromium coated with NaCl deposit in air or oxygen containing water vapor at 500-700℃.Results indicated that in air or in oxygen plus water vapor, the weight gain of Cr sample was not detectable even at 700℃ due to the formation of a compact and uniform Cr2O3 protective scale. However, with a solid NaCl deposit on its surface, corrosion of pure Cr in the same environments was significantly accelerated because of the reaction of NaCl with the oxide and substrate metal. When testing temperature increased and approached the melting temperature of NaCl, the corrosion of pure Cr coated with NaCl in air or in oxygen plus water vapor became more severe. A mechanism to explain the syneigistic effect of water vapor and NaCl on the corrosion of pure Cr is proposed.

Key words： pure Cr NaCl water vapor synergistic effects corrosion

收稿日期: 1999-04-12

ZTFLH:

TG174.43

通讯作者: 舒勇华

Corresponding author: Yonghua Shu

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	舒勇华
	王福会
	吴维tao
44.8K

引用本文:

舒勇华; 王福会; 吴维tao . NaCl盐膜和水蒸气对纯Cr腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2000, 20(2): 88-96 .
Yonghua Shu. Effect of NaCl Deposit and Water Vapor on the Corrosion Behavior of Pure Cr at 500-700℃. J Chin Soc Corr Pro, 2000, 20(2): 88-96 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2000/V20/I2/88

[1 ]HiramatsuN ,UematsuY ,TanakaT ,KinugasaM .EffectofalloyingelementsonNaCl inducedhotcorrosionofstainlesssteels[J].MaterialsScienceandEngineering ,1 989,A1 2 0 :31 9.
[2 ]DecrescenteMA ,BornsteinNS .Formationandreactivitythermodynamicofsodiumsulfatewithgasturbinealloys [J].Corrosion ,1 96 8,2 4:1 2 7- 1 33.
[3]ShinataY ,NishiY .NaCl inducedacceleratedoxidationofchromium [J].OxidMet,1 986 ,2 6 :2 0 1 - 2 1 2 .
[4 ]谢俊泉 ,宋士晖镍铬低合金钢在水蒸汽下的氧化动力学 [J] 北京科技大学学报 ,1 996 ,1 8:5 1 8- 5 2 1
[5 ]ShenJN ,ZhouLJ,LiTF .High temperatureoxidationofFe Cralloysinwetoxygen[J].OxidMet,1 997,48:34 7-35 6 .
[6 ]EvansHE ,HiltonDA ,HolmRA ,SimpsonPWG .Theoxidationofastainlesssteelwithlimitedquantitiesofseasalt[J].OxidMet,1 981 ,1 6 :32 7- 338.
[7]OnayB ,MorimotoT ,NakamuraS .CorrosionbehaviorofsomeFe BasedalloysinH2 H2 OandH2 H2 O HClgasmixturesat 973K [J].MaterialsScienceForum ,1 997,2 5 1 :5 91 - 5 98.
[8]SpiegelM ,SchroerC ,GrabkeH .CorrosionofhighalloysteelsandFe Cralloysbeneathdepositsfromwasteincineratorplants [J].MaterialsScienceForum ,1 997,2 5 1 :5 2 7- 5 34 .
[9]BakkerWT .Theeffectofchlorineonmixedoxidation/sulfidationofstainlesssteelbelow 6 0 0℃ [J] MaterialsScienceForum ,1 997,2 5 1 :5 75 - 5 82 .
[1 0 ]SaundersSRJ ,GohilDD ,BanksJP ,SheriffMU ,TortorelliPF ,DeVanJH ,WrightIG .BehaviorofFeCralloyandironaluminidesalloysincoalgasficationatmospherescontainingHCl[J].MaterialsScienceForum ,1 997,2 5 1 :5 83- 5 90 .
[1 1 ]舒勇华 ,王福会 ,周龙江 ,吴维山文在 5 0 0 - 70 0℃水蒸气和NaCl协同作用下 1Cr1 1Ni2W2MoV钢的腐蚀 [J] 金属学报 ,1 998,34 :483- 4 88
[1 2 ]ShuYonghua ,WangFuhui,WuWeitao .CorrosionbehaviorofTi6 0alloycoatedwithasolidNaCldepositinO2 pluswatervaporat 5 0 0 - 70 0℃ [J] OxidMet.,1 999,5 2 :(tobepublished)
[1 3]舒勇华 ,王福会 ,周龙江 ,吴维山文固态NaCl和水蒸气协同作用下高纯铁的腐蚀行为 [J] 金属学报 ,1 999,35 :31 1 - 31 5
[1 4]梁英教 ,车荫昌无机物热力学数据手册 [M] 沈阳 :东北大学出版社 ,1 993 8

[1]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[2]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[3]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[4]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[5]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[6]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[7]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[8]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[9]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[10]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed