数学统计方法在应力腐蚀噪声中的应用

乔利杰;高克玮;褚武扬

北京科技大学材料物理系;北京100083;北京科技大学材料物理系;北京100083;北京科技大学材料物理系;北京100083

APPLICATION OF MATHEMATICAL STATISTICAL METHODS TO ELECTROCHEMICAL NOISE OF STRESS CORROSIONCRACKING

QIAO Li-jie GAO Ke-wei CHU Wu-yang (Department of Materials Physics; University of Science and Technology Beijing; Beijing 100083)

全文: PDF(519 KB)

摘要: 研究了不锈钢和黄铜应力腐蚀的电化学噪声,得到了应力腐蚀的特征电位噪声谱。根据特征噪声的出现,可以监测应力腐蚀的发生。标准方差和功率谱等数学方法可以使得监测更加实用和有效,但应将直流背底扣除,否则会带来假象和错误的结论。

关键词 ：电化学噪声, 应力腐蚀, 功率谱, 标准方差, 不锈钢

Abstract：Electrochemical noises generated during stress corrosion cracking (SCC) of 304 stainless steel and α-brass were studied. SCC noise pattern showed common characteristics, i.e., the quick drop and slow recovery of the potential. The quick drop corresponded to a crack initiation and/or discontinuous propagation where fresh metal surface was exposed. The slow recovery corresponded to repassivation process of the exposed bare metal. For random noises, the rates of potential rise and drop were similar. The frequency of the noise generated during SCC increased with the increase in the applied stress. SCC initiation could be monitored and determined according to the noise characteristic and distribution. Mathematical treatments of standard deviation and power spectrum density (PSD) made the determination easier and realistic. But the background shift of the potential must be eliminated before the process. Standard deviation was more convenient and effective than PSD in the practice application.

Key words： Electrochemical noise Stress corrosion cracking Standard deviation Power spectrum density

收稿日期: 1998-08-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	乔利杰
	高克玮
	褚武扬
44.8K

引用本文:

乔利杰;高克玮;褚武扬. 数学统计方法在应力腐蚀噪声中的应用[J]. 中国腐蚀与防护学报, 1998, 18(4): 263-268.
. APPLICATION OF MATHEMATICAL STATISTICAL METHODS TO ELECTROCHEMICAL NOISE OF STRESS CORROSIONCRACKING. J Chin Soc Corr Pro, 1998, 18(4): 263-268.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1998/V18/I4/263

1 Newman R C, Sieradzki K. Scripta Metall. 1983, 17:621
2 Loto C A, Cottis R A. Corrosion 1987, 43:499
3 Loto C A, Cottis R A. Corrosion 1989, 45:136
4 Cottis R A, Loto C A. Corrosion 1990, 46:12
5 Inoue H, Iwawaki H, Yamakawa K. Mater. Sci. Eng. 1995, A198:225
6 Yamakawa K, Inoue H. Corros. Sci. 1992, 31:503
7 乔利杰,高克玮,褚武扬.金属学报,待发表
8 Wells D B, Stewart J, Davudson R, Scott P M, Willams D E. Corros. Sci. 1992, 33:39
9 Stewart J, Wells D B, Scott P M, Willams D E. Corros. Sci. 1992, 33:73
10 Gonzalez-Rodriguez J G, Salinas V M, Ramirez-Montano J M. Corros. Rev. 1996, 14:309
11 Benzaid A, Gabrielli C, Huet F, Jerome M, Wenger F. Material Science Forum 1992, 111-112:167

[1]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[3]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[4]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[5]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[6]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.
[7]	赵柏杰, 范益, 李镇镇, 张博威, 程学群. 不同类型接触面对316L不锈钢缝隙腐蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 332-341.
[8]	李清, 张德平, 李晓荣, 王薇, 孙宝壮, 艾池. TP110TS和P110钢在CO₂注入井环空环境中应力腐蚀行为比较[J]. 中国腐蚀与防护学报, 2020, 40(4): 302-308.
[9]	李清, 张德平, 王薇, 吴伟, 卢琳, 艾池. L80油管钢实际腐蚀状况评估及室内电化学和应力腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 317-324.
[10]	朱丽霞, 贾海东, 罗金恒, 李丽锋, 金剑, 武刚, 胥聪敏. 外加电位对X80管线钢在轮南土壤模拟溶液中应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 325-331.
[11]	张震, 吴欣强, 谭季波. 电化学噪声原位监测应力腐蚀开裂的研究现状与进展[J]. 中国腐蚀与防护学报, 2020, 40(3): 223-229.
[12]	胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[13]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[14]	何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[15]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.

Viewed

Full text

Abstract

Cited

Shared

Discussed