Effect of Flow Velocity on Flow Accelerated Corrosion Rate of Carbon Steel Elbow |
PAN Dailong, SI Xiaodong( ), LV Jinhong |
School of Energy and Power, Jiangsu University of Science and Technology, Zhenjiang 212100, China |
|
|
Abstract Carbon steel is the main material for power plants, oil and gas pipelines. Flow accelerated corrosion is the main factor causing pipeline failure in power plants, especially the secondary circuit pipeline system of the pressurized water reactor (PWR) nuclear power plant. In this paper, a home-made flow accelerated corrosion test rig and array electrode technology was used to study the effect of different flow rates on the flow accelerated corrosion rate distribution of 20# carbon steel elbow at 120 °C. The correlation between hydrodynamic parameters and corrosion rate was analyzed based on hydrodynamic simulation. The results show that the maximum corrosion current density is located at the external bending side of the elbow at different flow rates. With the increase of flow velocity, the flow accelerated corrosion rate increased significantly. In addition, the comparison of experimental data and simulation results show that the radial local velocity component can be used as an important parameter to predict the flow accelerated corrosion rate of carbon steel elbow. The empirical formula between the radial local velocity component and the corrosion rate was obtained by fitting based on the least square method. This research can be applied to design optimization, operation monitoring and maintenance strategy formulation of carbon steel elbow transport lines in thermal power, nuclear power and chemical industries.
|
Received: 17 October 2022
32134.14.1005.4537.2022.319
|
|
Fund: Innovation and Entrepreneurship Program of Jiangsu Province(JSSCBS20210994) |
Corresponding Authors:
SI Xiaodong, E-mail: Xiaod_Si@163.com
|
1 |
Zhang G J. Research on the mechanism of flow accelerated corrosion and its countermeasures of water-steam system in power station [D]. Baoding: North China Electric Power University, 2014
|
|
张国军. 电站汽水系统流动加速腐蚀机理及对策研究 [D]. 保定: 华北电力大学, 2014
|
2 |
Lu X F, Zhu X L, Ling X. A novel model for predicting flow accelerated corrosion rate in reducer [J]. J. Chin. Soc. Corros. Prot., 2011, 31: 431
|
|
陆晓峰, 朱晓磊, 凌 祥. 一种预测异径管流动加速腐蚀速率的新模型 [J]. 中国腐蚀与防护学报, 2011, 31: 431
|
3 |
Jiang S, Chai F, Su H, et al. Influence of chromium on the flow-accelerated corrosion behavior of low alloy steels in 3.5% NaCl solution [J]. Corros. Sci., 2017, 123: 217
doi: 10.1016/j.corsci.2017.04.024
|
4 |
Yang X Y, Guan L, Li Y, et al. Numerical simulation and experimental study on erosion-corrosion of square elbow based on orthogonal test [J]. J. Chin. Soc. Corros. Prot., 2022, 42: 979
|
|
杨湘愚, 关 蕾, 李 雨 等. 基于正交实验的90°弯管冲刷腐蚀数值模拟及实验研究 [J]. 中国腐蚀与防护学报, 2022, 42: 979
doi: 10.11902/1005.4537.2021.325
|
5 |
Kim S, Kim J W, Kim J H. Enhancement of corrosion resistance in carbon steels using nickel-phosphorous/titanium dioxide nanocomposite coatings under high-temperature flowing water [J]. J. Alloy. Compd., 2017, 698: 267
doi: 10.1016/j.jallcom.2016.12.027
|
6 |
Ge P L, Zeng W G, Xiao W W, et al. Effect of applied stress and medium flow on corrosion behavior of carbon steel in H2S/CO2 coexisting environment [J]. J. Chin. Soc. Corros. Prot., 2021, 41: 271
|
|
葛鹏莉, 曾文广, 肖雯雯 等. H2S/CO2共存环境中施加应力与介质流动对碳钢腐蚀行为的影响 [J]. 中国腐蚀与防护学报, 2021, 41: 271
doi: 10.11902/1005.4537.2020.025
|
7 |
Lin T, Zhou K Y, Si X D. Research progress on flow-accelerated corrosion of power plant and contermeasures [J]. Corros. Sci. Prot. Technol., 2018, 30: 543
|
|
林 彤, 周克毅, 司晓东. 电厂机组流动加速腐蚀研究进展及防护措施 [J]. 腐蚀科学与防护技术, 2018, 30: 543
|
8 |
Wang K, Nan C H, Lu J L. Mechanism of hydrodynamic process in flow corrosion behavior [J]. Chem. Ind. Eng. Prog., 2020, 39(suppl. 2) : 8
|
|
王 凯, 南翠红, 卢金玲. 流体动力学过程在流动腐蚀行为中的作用机制 [J]. 化工进展, 2020, 39(): 8
|
9 |
Pan D L, Si X D, Zhang J, et al. Experimental study on flow-accelerated corrosion at elbow of carbon steel at different temperatures [J]. Therm. Power Gener., 2022, 51(7): 110
|
|
潘代龙, 司晓东, 张 静 等. 碳钢弯管段在不同温度下流动加速腐蚀性能实验研究 [J]. 热力发电, 2022, 51(7): 110
|
10 |
Dooley R B. Flow-accelerated corrosion in fossil and combined cycle/HRSG plants [J]. Power Plant Chem., 2008, 10: 68
|
11 |
Chen H L, Ma L, Huang G S, et al. Effect of dissolved oxygen and flow rate of seawater on film formation of B30 Cu-Ni alloy [J]. J. Chin. Soc. Corros. Prot., 2022, 42: 724
|
|
陈翰林, 马 力, 黄国胜 等. 溶解氧和流速对B30铜镍合金在海水中成膜的影响 [J]. 中国腐蚀与防护学报, 2022, 42: 724
doi: 10.11902/1005.4537.2021.260
|
12 |
Zhang G Y, Gu Y, Shao J. Cause analysis on FAC failures of steam/water piping in secondary loop of PWR power plants and the countermeasures [J]. J. Chin. Soc. Power Eng., 2012, 32: 170
|
|
张桂英, 顾 宇, 邵 杰. 核电站汽水管道流动加速腐蚀的影响因素分析及对策 [J]. 动力工程学报, 2012, 32: 170
|
13 |
Fujiwara K, Domae M, Yoneda K, et al. Model of physico-chemical effect on flow accelerated corrosion in power plant [J]. Corros. Sci., 2011, 53: 3526
doi: 10.1016/j.corsci.2011.06.027
|
14 |
Talaat K, Hassan M M, Cakez C, et al. Design of specimen holders for flow accelerated corrosion experiments in molten lead with numerical evaluation of pressure losses [J]. Nucl. Eng. Des., 2021, 385: 111522
doi: 10.1016/j.nucengdes.2021.111522
|
15 |
Bandeira R M, van Drunen J, Garcia A C, et al. Influence of the thickness and roughness of polyaniline coatings on corrosion protection of AA7075 aluminum alloy [J]. Electrochim. Acta, 2017, 240: 215
doi: 10.1016/j.electacta.2017.04.083
|
16 |
Liu H W, Gu T Y, Asif M, et al. The corrosion behavior and mechanism of carbon steel induced by extracellular polymeric substances of iron-oxidizing bacteria [J]. Corros. Sci., 2017, 114: 102
doi: 10.1016/j.corsci.2016.10.025
|
17 |
Zeng L, Zhang G A, Guo X P. Erosion–corrosion at different locations of X65 carbon steel elbow [J]. Corros. Sci., 2014, 85: 318
doi: 10.1016/j.corsci.2014.04.045
|
18 |
Si X D, Si H T, Li M Y, et al. Investigation of corrosion behavior at elbow by array electrode and computational fluid dynamics simulation [J]. Mater. Corros., 2020, 71: 1637
|
19 |
Utanohara Y, Murase M. Influence of flow velocity and temperature on flow accelerated corrosion rate at an elbow pipe [J]. Nucl. Eng. Des., 2019, 342: 20
doi: 10.1016/j.nucengdes.2018.11.022
|
20 |
Dean W R. Fluid motion in a curved channel [J]. Proc. Roy. Soc. Lond., 1928, 121A: 402
|
21 |
Si X D, Zhang R, Xu Q, et al. Effects of local velocity components on flow-accelerated corrosion at 90° elbow [J]. Mater. Res. Express, 2019, 6: 016557
|
No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|