| EFFECT OF TEMPERATURE ON PROPERTIES OF CO2 CORROSION SCALE OF N80 CARBON STEEL |
| LI Dangguo1;2;FENG Yaorong2;BAI Zhenquan2;ZHENG Maosheng1 |
1.School of Materials Science and Engineering; Xi′an Jiaotong University; Xi′an 710049；
2.Tubular Goods Research Center; China National Petroleum Corporation; Xi′an 710065 |
|
|
|
|
Abstract The electrochemical properties and microstructures of CO2 corrosion scale formed on N80 carbon steel at 3 MPa and different temperatures in stratum water with saturated CO2 were investigated. The impedance results showed that the compactness of corrosion scale increased and the diffusion process decreased with increasing temperature; when temperature reached to 200 ℃, the diffusion impedance of corrosion scale decreased, indicating that the diffusion of ions in the scale became easy. electrochemical impedance spectrum (SEM) results revealed that the scale is of a double-layer structure, the length of the scale decreased with temperature increasing. Observation of the microstructure of the sample surface after removing the corrosion scale, showed that many big holes existed in the sample surface at low temperature,which became small and finally turned into uniform corrosion with temperature increasing. When temperature reached to 200 ℃ the holes became bigger again, indicating the corrosion extent promoted furthermore.
|
|
Received: 05 February 2007
|
|
|
|
Corresponding Authors:
FENG Yaorong
|
[1]Linter B R,Burstein G T.Reaction of pipeline steels in carbon dioxide solutions[J].Corros.Sci.,1999,41(2):117-139
[2]Xa Z,Chou K C,Smialowska Z S.Pitting corrosion of carbon steel in CO2-containing NaCl brine[J].Corrosion,1989,45(8):636
[3]Ikeda A,Udeda M,Mukai S.Advances in CO2corrosion[A].In:Hausler R H.Giddard H P,eds.,Corrosion/84[C].Houston,Texas:NACE,1984,1:39-143
[4]Moraes F D de,Shadley J R,Chen J F,et al.Characterization of CO2corrosion product scales related to environmental conditions[A].Corrosion/2000[C].Orlando,Florida,2000,30
[5]Zheng J S.The research situation about CO2corrosion[J].Fault-block Oil Gas Field,1996,3(1):62-65(郑家燊.二氧化碳腐蚀的研究现状[J].断块油气田,1996,3(1):62-65)
[6]Zhang X Y.A review on acid fracturing technology in carbonate-stone reservoirs[J].Oilfield Chem.,1997,14(2):190-196(张学元.油气开发中二氧化碳腐蚀的研究现状和趋势[J],油田化学,1997,14(2):190-196)
[7]Wang J,Cao C N,Lin H C.Impedance spectroscopy character of the pit corrosion development[J].J.Chin.Soc.Corros.Prot.,1989,9(4):271-276(王佳,曹楚南,林海潮.孔蚀发展期的电极阻抗谱特征[J].中国腐蚀与防护学报,1989,9(4):271-276)
[8]Zeng C L,Wang W,Wu W T.Electrochemical impedance models for molten salts induced corrosion[J].Acta Metall.Sin.,1999,35(7):751-757(曾潮流,王文,吴维(山文).熔融盐热腐蚀的电化学阻抗模型[J].金属学报,1999,35(7):751-757)
[9]Ogundele G I,White W E.Some observation on corrosion of car-bon steel in aqueous environments containing carbon dioxide[J].Corrosion,1986,42(2):71-77
[10]Nesic S,Postlethwaite J,Olsen S.An electrochemical model for prediction of corrosion of mild steel in aqueous carbon dioxide so-lutions[J].Corrosion,1996,52(4):280-294
[11]Chen C F,Lu M X,Zhao G X,et al.The EIS analysis of cathodic reactions during CO2corrosion of N80steel[J].Acta Metall.Sin.,2003,39(1):74-78(陈长风,路民旭,赵国仙等.N80油套管CO2腐蚀阴极过程电化学阻抗谱分析[J].金属学报,2003,39(1):74-78)
[12]Davies D H,Burstein G T.The effects of bicarbonate on the cor-rosion and passivation of iron[J].Corrosion,1980,36(8):416-42 |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|