CYCLIC OXIDATION OF ALUMINIDE COATINGS ON 16Mn STEELUNDER THE CONDITION OF QUENCHING IN SEA WATER

J Chin Soc Corr Pro

2002, Vol. 22

Issue (1): 44-47 DOI:

Research Report

Current Issue | Archive | Adv Search

CYCLIC OXIDATION OF ALUMINIDE COATINGS ON 16Mn STEELUNDER THE CONDITION OF QUENCHING IN SEA WATER

Yaming Zhang;Meishuan Li

中科院金属所

Download:

PDF(174KB)
Export: BibTeX | EndNote (RIS)

Abstract The cyclic oxidation of aluminide coatings on 16Mn s teel under the condition of quenching in water containing 3.5% NaCl has been stu died.The oxidation was carried out at 600℃ and 800℃ in air.The aluminide coati ngs remarkably improve the oxidation resistance of 16Mn steel.Increasing of the oxidation temperature or existing of NaCl in quenching water causes more severe corrosion.After cyclic test,the aluminide coatings happen to crack.However,these cracks just exist in the surface layer of the coatings.

Key words: 16Mn Steel aluminide coating oxidation exhaust tube

Received: 20 October 2000

ZTFLH:

TG172.82

Corresponding Authors: Yaming Zhang

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Yaming Zhang
	Meishuan Li

Cite this article:

Yaming Zhang; Meishuan Li. CYCLIC OXIDATION OF ALUMINIDE COATINGS ON 16Mn STEELUNDER THE CONDITION OF QUENCHING IN SEA WATER. J Chin Soc Corr Pro, 2002, 22(1): 44-47 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2002/V22/I1/44

[1]WarrenNG .CorrosionofMetalsinShips[M ].Beijing:NationalDefenceIndustryPress,1987
(奈杰尔·沃伦著,吴敏,张义译.船舶中的金属腐蚀[M ].北京:国防工业出版社,1987)
[2]LuYanpng,YuFuzhou.Metallizing[M].Beijing:MechanicalIndus tryPress,1985,56
(卢燕平,于福洲编.渗镀[M ].北京:机械工业出版社,1985,56)
[3]SivakumarR ,JanardhanaRaoE .Aninvestigationofpack-alu minidecoatingonsteel[J].Oxid.Met.,1982,17:391
[4]SolimanHM ,AbdEI AzimME .Perfomanceofthealuminidecoat ingofsomelowalloysteels[J].J.Mater.Sci.Technol.,1997,13:462
[5]BangaruNV ,KrutenatRC .Diffusioncoatingsofsteels:formationmechanismandmicrostructureofaluminizedheat-resistantstain lesssteels[J].J .Vac.Sci.Technol.,1984,B2:806
[6]KofstadP .HighTemperatureCorrosion[M].England:ElsevierAp pliedSciencePublishersLTD ,1988,5026

[1]	WEI Zheng, MA Baoji, LI Long, LIU Xiaofeng, LI Hui. Effect of Ultrasonic Rolling Pretreatment on Corrosion Resistance of Micro-arc Oxidation Coating of Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[2]	LIU Xiao, WANG Hai, ZHU Zhongliang, LI Ruitao, CHEN Zhenyu, FANG Xudong, XU Fanghong, ZHANG Naiqiang. Oxidation Characteristics of Austenitic Heat-resistant Steel HR3C and Sanicro25 in Supercritical Water for Power Station[J]. 中国腐蚀与防护学报, 2020, 40(6): 529-538.
[3]	XIE Dongbai, HONG Hao, WANG Wen, PENG Xiao, DUO Shuwang. Oxidation Behavior of Stainless Steel 1Cr11Ni2W2MoV in a Simulated Kerosene Combustion Environment[J]. 中国腐蚀与防护学报, 2020, 40(4): 358-366.
[4]	CAO Jingyi, FANG Zhigang, CHEN Jinhui, CHEN Zhixiong, YIN Wenchang, YANG Yange, ZHANG Wei. Preparation and Properties of Micro-arc Oxide Film with Single Dense Layer on Surface of 5083 Aluminum Alloy[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[5]	FANG Xudong, LIU Xiao, XU Fanghong, LI Ruitao, ZHU Zhongliang, ZHANG Naiqiang. Oxidation Behavior in Supercritical Water of Domestic Austenitic Steel C-HRA-5 for Uultra-supercritical Power Stations[J]. 中国腐蚀与防护学报, 2020, 40(3): 266-272.
[6]	ZHENG Yanxin, LIU Ying, SONG Qingsong, ZHENG Feng, JIA Yuchuan, HAN Peide. High-temperature Oxidation Behavior and Wear Resistance of Copper-based Composites with Reinforcers of C, ZrSiO₄ and Fe[J]. 中国腐蚀与防护学报, 2020, 40(2): 191-198.
[7]	XU Xunhu,HE Cuiqun,XIANG Junhuai,WANG Ling,ZHANG Honghua,ZHENG Xiaodong. High Temperature Oxidation Behavior of Co-20Re-25Cr-1Si Alloy in 0.1 MPa Pure Oxygen[J]. 中国腐蚀与防护学报, 2020, 40(1): 75-80.
[8]	JIANG Dongxue,FU Ying,ZHANG Junwei,ZHANG Wei,XIN Li,ZHU Shenglong,WANG Fuhui. Preparation and Properties of Alumina Ceramic Film on Ti-alloy Surface[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.
[9]	YU Chuntang,YANG Yingfei,BAO Zebin,ZHU Shenglong. Research Progress in Preparation and Development of Excellent Bond Coats for Advanced Thermal Barrier Coatings[J]. 中国腐蚀与防护学报, 2019, 39(5): 395-403.
[10]	XIAO Jintao,CHEN Yan,XING Mingxiu,JU Pengfei,MENG Yingen,WANG Fang. Effect of Process Parameters on Corrosion Resistance of Anodizing Film on 2195 Al-Li Alloy[J]. 中国腐蚀与防护学报, 2019, 39(5): 431-438.
[11]	AI Peng,LIU Lixiang,LI Xiaogang,JIANG Wentao. Influence of TiAlSiN Coatings on High Temperature Oxidation Resistance of γ-TiAl Based Alloys[J]. 中国腐蚀与防护学报, 2019, 39(4): 306-312.
[12]	Yunhai MA. Effect of Shot Peening on Oxidation Resistance of Super 304H Steel in Supercritical Steam[J]. 中国腐蚀与防护学报, 2019, 39(3): 245-252.
[13]	Junjie XIA,Hongzhi NIU,Min LIU,Huazhen CAO,Guoqu ZHENG,Liankui WU. Enhancement of High Temperature Oxidation Resistance of Ti48Al5Nb Alloy via Anodic Anodization in NH₄F Containing Ethylene Glycol[J]. 中国腐蚀与防护学报, 2019, 39(2): 96-105.
[14]	Dongbai XIE,Youyu ZHOU,Jintao LU,Wen WANG,Shenglong ZHU,Fuhui WANG. Effect of Al/Si Content on Corrosion of Ni-based Alloys in Supercritical Water[J]. 中国腐蚀与防护学报, 2019, 39(1): 68-76.
[15]	Ling WANG,Junhuai XIANG,Honghua ZHANG,Songlin QIN. High Temperature Oxidation Behavior of Three Co-20Re-xCr Alloys in 3.04×10^-5 Pa Oxygen at 1000 and 1100 ℃[J]. 中国腐蚀与防护学报, 2019, 39(1): 83-88.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed