XPS AND AES STUDIES OF ANTICORROSIVE COLOUR FILM ON ZINC

HAN Keping FANG Jingli(Department of Chemistry; Applied Chemistry Institute; Nanjing University)

Download:

PDF(357KB)
Export: BibTeX | EndNote (RIS)

Abstract Colourful conversion films were formed on zinc surface with cathodic polarization method from a molybdate-phosphate type aqueous solution. It was found from the results of salt spray corrosion tests that the golden film exhibited excellent anticrrosive performance. The results of XPS and AES analyses showed that the thickness of the golden film was about 75nm and Mo existed as Mo(VI) in the outer layer of the film. The relative atomic percent contents (A.C.%) of the golden film calculated at the constant elemental composition section on the AES profile curves were O 56.9%; Mo 26.8%; P 11.0%; Zn 5.3%.

Key words: Anticorrosive film Zinc surface Cathodic polarization XPS AES

Received: 25 February 1997

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

HAN Keping FANG Jingli(Department of Chemistry; Applied Chemistry Institute; Nanjing University). XPS AND AES STUDIES OF ANTICORROSIVE COLOUR FILM ON ZINC. J Chin Soc Corr Pro, 1997, 17(1): 41-45.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y1997/V17/I1/41

1 Wilcox G D, Gabe D R. Br. Corros. J., 1987, 22:254
2 Clayton C R, Lu Y C. Corros. Sci., 1989, 29:881
3 方景礼,刘琴,韩克平,陈耀辉.应用化学,1995,12:1
4 方景礼,韩克平,刘琴.应用科学学报,待发表
5 Biestek T, Weber J. Electrolytic and Chemical Conversion Coatings-Concise Survey of their Production, Properties and Testing, Portcullis Press Ltd., Redhill, 1976
6 Urgen M, Stole U, Kirchheim R. Corros. Sci., 1990, 30:377
7 Wagner C D, Riggs W M, Davis L E, Moulder J E, Muilenberg G E. Handbook of X-ray Photoelectron Spectroscopy, Perkin-Elmer Corporation, Eden Prairie, MN, 1978
8 Briggs D, Seah M P. Practical Surface Analysis by Auger and X-ray Photoelectron Spectroscopy, John Wiley & Sons Ltd, New York, 1983
9 Rachinskas V, Orlovskaya L, Matulis J. Leit TSR Mokslu Akad Darb, 1972, 6:73
10 Wanklyn J N. Corros. Sci., 1981, 21:211
11 Wilcox G D, Gabe D R. Br. Corros. J., 1984, 19:196
12 Servais J P, Lempereur J, Renard J, Leroy V. Br. Corros. J., 1979, 14:126
13 Azzerri A, Splendorini L, Battistoni C, Paparazzo E. Surf. Technol., 1982, 15:255

[1]	ZHANG Chen, LU Yuan, ZHAO Jingmao. Synergistic Inhibition Effect of Imidazoline Ammonium Salt and Three Cationic Surfactants in H₂S/CO₂ Brine Solution[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[2]	WANG Le,YI Danqing,LIU Huiqun,JIANG Long,FENG Chun. Effect of Ru on Corrosion Behavior of Ti-6Al-4V Alloy and Its Mechanism[J]. 中国腐蚀与防护学报, 2020, 40(1): 25-30.
[3]	Zhaodeng LI,Zhendong CUI,Xiangyu HOU,Lili GAO,Weizhen WANG,Jianhua YIN. Corrosion Property of Nuclear Grade 316LN Stainless Steel Weld Joint in High Temperature and High Pressure Water[J]. 中国腐蚀与防护学报, 2019, 39(2): 106-113.
[4]	Dong LIU,Hongliang XIANG,Chunyu LIU. XPS Analysis of Corrosion Product Scale on Surface of Silver-bearing Antibacterial Duplex Stainless Steel[J]. 中国腐蚀与防护学报, 2018, 38(6): 533-542.
[5]	Ming LIU,Xuequn CHENG,Xiaogang LI,Tianjian LU. Corrosion Resistance Mechanisms of Passive Films Formed on Low Alloy Rebar Steels in Liquor of Cement Extract[J]. 中国腐蚀与防护学报, 2018, 38(6): 558-564.
[6]	Zheng LIU, Haiying LI, Hao WANG, Yong ZHAO, Siwei XIE, Shufen ZHANG. Molecular Dynamics Simulation of Adsorption Behavior of Schiff Base Surfactants on Zn Surface in Aqueous Solution[J]. 中国腐蚀与防护学报, 2018, 38(4): 381-390.
[7]	Qi GUI, Dajiang ZHENG, Guangling SONG. Electrochemically Accelerated Evaluation of Protectiveness for an Alkyd Varnish Coating[J]. 中国腐蚀与防护学报, 2018, 38(3): 274-282.
[8]	Fang GUAN, Xiaofan ZHAI, Jizhou DUAN, Baorong HOU. Progress on Influence of Cathodic Polarization on Sulfate-reducing Bacteria Induced Corrosion[J]. 中国腐蚀与防护学报, 2018, 38(1): 1-10.
[9]	Teng LI, Weiliang JIN, Chen XU, Jianghong MAO. Determination of Steady Critical Current Density of Hydrogen Evolution During Electrochemical Repair Process of Reinforced Concrete[J]. 中国腐蚀与防护学报, 2017, 37(4): 382-388.
[10]	Yanliang WANG,Xu CHEN,Jidong WANG,Bo SONG,Dongsheng FAN,Chuan HE. Electrochemical Behavior of 316L Stainless Steel in Borate Buffer Solution with Different pH[J]. 中国腐蚀与防护学报, 2017, 37(2): 162-167.
[11]	Yongsheng HAO,Abdullahi SANI Luqman,Lixin SONG,Guobao XU,Tiejun GE,Qinghong FANG. Corrosion Inhibition Effect of Phytic Acid Conversion Coating Formed on Q235 Carbon Steel in Acidic and Neutral Solutions[J]. 中国腐蚀与防护学报, 2016, 36(6): 549-558.
[12]	Shenggang WANG, Miao SUN, Kang LONG. Progress in Characterization of Metallic Materials Corrosion by Ultraviolet Photoelectron Spectroscopy and X-ray Photoelectron Spectroscopy[J]. 中国腐蚀与防护学报, 2016, 36(4): 287-294.
[13]	Wenjing LV,Yingjun ZHANG,Chao SHI,Yawei SHAO,Yanqiu WANG,Guozhe MENG. Synthesis and Corrosion Inhibition Performance of Polyatyrolsulfon-acid Doped Polyaniline[J]. 中国腐蚀与防护学报, 2015, 35(6): 519-524.
[14]	Wang GUO,Weimin ZHAO,Timing ZHANG,Tianhai DU,Yong WANG. Hydrogen Permeation Behavior of X80 Steel under Cathodic Polarization and Stress[J]. 中国腐蚀与防护学报, 2015, 35(4): 353-358.
[15]	ZHANG Timing, ZHAO Weimin, GUO Wang, WANG Yong. Susceptibility to Hydrogen Embrittlement of X65 Steel Under Cathodic Protection in Artificial Sea Water[J]. 中国腐蚀与防护学报, 2014, 34(4): 315-320.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed