CORROSION BEHAVIOUR OF MILD STEEL IN TRIAXIAL COMPOSITE FLOODING SOLUTION

J Chin Soc Corr Pro

1998, Vol. 18

Issue (3): 203-208 DOI:

Current Issue | Archive | Adv Search

CORROSION BEHAVIOUR OF MILD STEEL IN TRIAXIAL COMPOSITE FLOODING SOLUTION

WANG Wei GUO He-tong GAO Jian-ping (Tianjin University; Tianjin 300072)XIANG Min (Zhengzhou Light Industry College; Zhengzhou 450002)

Download:

PDF(410KB)
Export: BibTeX | EndNote (RIS)

Abstract Mild steel (0.24wt% C) can be passivated in triaxial composite flooding solution containing 1.2% NaCl+ 0.6% petroleum sulfonate + 0.12% polyacrylamide(wt%). The composition and structure of passive film formed on the steel were investigated by XPS. The results showed that the passive film was composed of Fe3O4, FeOOH, Fe2O3 and Fe(OH)2, and its thickness was about 7nm. The valence of elemental iron varied at different depth of the passive film. At the outer surface of the passive film, the valence of iron was +3, and at the interface near the matrix, +3 and +2 iron were detected.

Key words: Mild steel Triaxial composite flooding solution Passive film XPS

Received: 25 June 1998

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

WANG Wei GUO He-tong GAO Jian-ping (Tianjin University; Tianjin 300072)XIANG Min (Zhengzhou Light Industry College; Zhengzhou 450002). CORROSION BEHAVIOUR OF MILD STEEL IN TRIAXIAL COMPOSITE FLOODING SOLUTION. J Chin Soc Corr Pro, 1998, 18(3): 203-208.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y1998/V18/I3/203

1 唐纳林EC著,童育英等译.提高石油采收率.北京:石油工业出版社,1989.1
2 Hawkins B F, Taylor K C. J. Canadian Petroleum Technology, 1994, 3(4): 52
3 Saleem S M. J. Surface Science and Technology, 1987, 3(1): 1
4 吴文祥,康万利.大庆石油学院学报,1995,19:119
5 Wagner C D, Riggs W M, Davis L E. Handbook of X-ray Photoelectron Spectroscopy. Perkin-Elmer Corporation, 1992
6 项民.天津大学硕士学位论文,1996

[1]	SHI Kunyu, WU Weijin, ZHANG Yi, WAN Yi, YU Chuanhao. Electrochemical Properties of Nb Coating on TC4 Substrate in Simulated Body Solution[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[2]	ZHANG Chen, LU Yuan, ZHAO Jingmao. Synergistic Inhibition Effect of Imidazoline Ammonium Salt and Three Cationic Surfactants in H₂S/CO₂ Brine Solution[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[3]	WANG Le,YI Danqing,LIU Huiqun,JIANG Long,FENG Chun. Effect of Ru on Corrosion Behavior of Ti-6Al-4V Alloy and Its Mechanism[J]. 中国腐蚀与防护学报, 2020, 40(1): 25-30.
[4]	ZHANG Rui,LI Yu,GUAN Lei,WANG Guan,WANG Fuyu. Effect of Heat Treatment on Electrochemical Corrosion Behavior of Selective Laser Melted Ti6Al4V Alloy[J]. 中国腐蚀与防护学报, 2019, 39(6): 588-594.
[5]	Zhaodeng LI,Zhendong CUI,Xiangyu HOU,Lili GAO,Weizhen WANG,Jianhua YIN. Corrosion Property of Nuclear Grade 316LN Stainless Steel Weld Joint in High Temperature and High Pressure Water[J]. 中国腐蚀与防护学报, 2019, 39(2): 106-113.
[6]	Shaokun YAN,Dajiang ZHENG,Jiang WEI,Guangling SONG,Lian ZHOU. Electrochemical Activation of Passivated Pure Titanium in Artificial Seawater[J]. 中国腐蚀与防护学报, 2019, 39(2): 123-129.
[7]	Dong LIU,Hongliang XIANG,Chunyu LIU. XPS Analysis of Corrosion Product Scale on Surface of Silver-bearing Antibacterial Duplex Stainless Steel[J]. 中国腐蚀与防护学报, 2018, 38(6): 533-542.
[8]	Ming LIU,Xuequn CHENG,Xiaogang LI,Tianjian LU. Corrosion Resistance Mechanisms of Passive Films Formed on Low Alloy Rebar Steels in Liquor of Cement Extract[J]. 中国腐蚀与防护学报, 2018, 38(6): 558-564.
[9]	Zihan LIAO, Bo SONG, Ze REN, Chuan HE, Xu CHEN. Electrochemical Corrosion Behavior of Matrix and Weld Seam of X70 Steel in Na₂CO₃+NaHCO₃ Solutions[J]. 中国腐蚀与防护学报, 2018, 38(2): 158-166.
[10]	Bei QIAN, Chengbao LIU, Zuwei SONG, Junfeng REN. Anticorrosion Performance of Epoxy Coating Modified with Nanocontainers[J]. 中国腐蚀与防护学报, 2018, 38(2): 133-139.
[11]	Guangyu LI, Mingkai LEI. Composition and Semi-conductive Characteristic of Passive Film Formed on γ_Ν-phase in a Borax Buffer Solution[J]. 中国腐蚀与防护学报, 2018, 38(1): 47-53.
[12]	Yanliang WANG,Xu CHEN,Jidong WANG,Bo SONG,Dongsheng FAN,Chuan HE. Electrochemical Behavior of 316L Stainless Steel in Borate Buffer Solution with Different pH[J]. 中国腐蚀与防护学报, 2017, 37(2): 162-167.
[13]	Tianyi ZHANG,Junsheng WU,Hailong GUO,Xiaogang LI. Influence of HSO₃^- on Passive Film Composition and Corrosion Resistance of 2205 Duplex Stainless Steelin Simulated Seawater[J]. 中国腐蚀与防护学报, 2016, 36(6): 535-542.
[14]	Yongsheng HAO,Abdullahi SANI Luqman,Lixin SONG,Guobao XU,Tiejun GE,Qinghong FANG. Corrosion Inhibition Effect of Phytic Acid Conversion Coating Formed on Q235 Carbon Steel in Acidic and Neutral Solutions[J]. 中国腐蚀与防护学报, 2016, 36(6): 549-558.
[15]	Jianchun ZHANG,Jingyang JIANG,Yang LI,Jinjie SHI,Longfei ZUO,Danqian WANG,Han MA. Passive Films Formed on Seawater Corrosion Resistant Rebar 00Cr10MoV in Simulated Concrete Pore Solutions[J]. 中国腐蚀与防护学报, 2016, 36(5): 441-449.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed