| The Influence of Different Enviroments on Stress Corrosion Cracking |
| 北京航空材料研究院 |
|
Cite this article:
. The Influence of Different Enviroments on Stress Corrosion Cracking. J Chin Soc Corr Pro, 2007, 27(6): 354-362 .
|
|
|
Abstract An investigation of the stress corrosion cracking resistance of high strength aluminum alloys 2A12 and 7A04 in different atmospheric environment were presented, results were compared with those obtained in laboratory accelerated tests. C-ring and direct tension stress corrosion specimens were taken from the short transverse grain and the longitudinal direction of aluminum alloy stick respectively, applied stress level were 60, 70, 80 and 90 percent of the σ0.2. The atmospheric stress corrosion tests were exposed to three different atmospheric test stations in China, one in Beijing, typical semi-rural atmosphere, others in coastal city, Qingdao (East of China) and Wanning (South of China). In the meantime, alternate immersion and direct tension stress corrosion immersion in salt solution were conducted in laboratory condition. The results showed that SCC performance of aluminum alloys could be evaluated within one year in marine atmospheric environment, otherwise, only exfoliation corrosion or pitting was observed. The alternate corrosion results showed that SCC of aluminum alloy was consistent with outdoor exposed samples in the marine atmospheric environment.
|
|
Received: 06 November 2006
|
|
|
[1]Edited by R.Winston Revie.Uhlig′s Corrosion Handbook,Second Edition[M].NewYork:John Wiley & Sons,Inc,2000
[2]TSAI T C,Chuang T H.Atmospheric stress corrosion cracking of asuperplastic 7475 aluminum alloy[J].Metall.Mater.Trans.A,1996,27A(9)2617-2627
[3]Schra L,Hart W G J.Long-term outdoor stress corrosion testing ofoveraged 7000 series aluminum alloys[A].NLR TR 88012U[C].American,1988
[4]Humphries T S,Nelson E E.Seacoast stress corrosion cracking ofaluminum alloys[A].NASA TM-82393[C].American,1981
[5]Schra L,Faber J.Influence of environments on constant displace-ment stress corrosion crack growth in high strength aluminum al-loys[A].N83-23446[C].American,1981
[6]Liu J H,Li D,Guo B L.Investigation of stress corrosion crackingof 7xxx series aluminum alloys[J].Corros.Sci.Prot.Technol.,2001,13(4):218-221(刘继华,李荻,郭宝兰.7XXX系列Al合金应力腐蚀开裂研究[J].腐蚀科学与防护技术,2001,13(4):218-221)
[7]Shen H J,Guo W L,Lu G Z.Stress corrosion cracking suscepti-bility of aluminum alloys LC9 in Na Cl solution[J].Corros.Prot.,2002,23(5):190-201(沈海军,郭万林,吕国志.Na Cl溶液中LC9铝合金应力腐蚀特性的试验研究[J].腐蚀与防护,2002,23(5):190-201)
[8]Wang Y,Wang Z H,Fu Z L,et al.Effect of scandium on the stresscorrosion cracking and exfoliation corrosion of Al-Mg alloys[J].J.Chin.Soc.Corros.Prot,2005,25(4):218-221(王月,王政红,付自来等.含钪Al-Mg合金抗应力腐蚀和剥落腐蚀性能影响[J].中国腐蚀与防护学报,2005,25(4):218-221)
[9]Sun Z H,Liu M H,Zhang X Y,et al.Effect of tempered condi-tion on the stress corrosion cracking of Al-Zn-Mg-Cu alloys[J].J.Chin.Soc.Corros.Prot,2006,26(4):232-236(孙志华,刘明辉,张晓云等.时效制度对Al-Zn-Mg-Cu铝合金应力腐蚀敏感性的影响[J].中国腐蚀与防护学报,2006,26(4):232-236)
[10]Zhang X Y,Guo Y H,Tao C H,et al.Study on the desk-top springtype stress corrosion cracking testing machine[J].Equip.Environ.Eng.,2004,1(2):18-22(张晓云,郭玉海,陶春虎等.便携式拉伸应力腐蚀试验器的研制[J].装备环境工程,2004,1(2):18-22)
[11]Desk-Top Spring Type Stress Corrosion Cracking Testing Machine[P].China,ZL 022941339,2002(便携式拉伸应力腐蚀试验装置[P].中国,ZL 022941339,2002) |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|