CORROSION BEHAVIOR OF ATMOSPHERIC ENVIRONMENT AND CORROSION FEATURE OF MATERIALS IN OUR WESTERN AREA

J Chin Soc Corr Pro

2003, Vol. 23

Issue (4): 248-255 DOI:

Review

Current Issue | Archive | Adv Search

CORROSION BEHAVIOR OF ATMOSPHERIC ENVIRONMENT AND CORROSION FEATURE OF MATERIALS IN OUR WESTERN AREA

Yide Xiao;Guangyong Wang;Xiaogang Li

武汉材料保护研究所

Download:

PDF(324KB)
Export: BibTeX | EndNote (RIS)

Abstract The topography,geomorphy and climate in western are a in our country are complex and multivariate.According to climatic factors and environmental conditions,there are approximately four types of typical atmospher ic environment,namely acid rain environment,desert environment,plateau environme nt and tropical rainforest environment.The atmospheric corrosion degrees of all types of environment are different,as well as are the corrosion failure features of materials under different environment conditions.The acid rain atmospheric e nvironment aggravates the corrosion failure of metals,protective coatings on met als and building materials,etc.Although the climate is dry and there is little r ain in the desert atmospheric environment,owning to the high salt content in air sediment,the corrosion failure of copper,zinc,aluminum,stainless steel and meta l coatings in Takelamagan area located in Talimu basin is severer than that in e astern moist hot or semi-moist hot city environment.Under plateau environment condition,the significant feature is that macromolecular materials will fail rap idly.The feature of tropical rainforest atmospheric environment is mainly that o ptical instrument,leather,fabric and timber will be severely moulded.

Key words: western area atmospheric corrosion corrosion investiga tion

Received: 08 May 2002

ZTFLH:

TU53

Corresponding Authors: Yide Xiao

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Yide Xiao
	Guangyong Wang
	Xiaogang Li

Cite this article:

Yide Xiao; Guangyong Wang; Xiaogang Li. CORROSION BEHAVIOR OF ATMOSPHERIC ENVIRONMENT AND CORROSION FEATURE OF MATERIALS IN OUR WESTERN AREA. J Chin Soc Corr Pro, 2003, 23(4): 248-255 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2003/V23/I4/248

[1]WangZhenyao,ZhengYiping.SurveyofeffectofacidraininSouth westofChinaonatmosphericcorrosionofmetals[J].TotalCorro sionControl,1997,11(2):45-48(王振尧,郑逸平.西南酸雨对金属腐蚀影响调查[J].全面腐蚀控制,1997,11(2):45-48)
[2]ZhengYiping,WangZhenyao,ZhangFengqiu.Influenceofacidde positiononatmosphericcorrosionofzinc[J].J .Environ.Sci.,1997,3(2):53-56
[3]HuXingjun.ThestudyofenduringperformanceofPVC[J].Cor ros.Sci.Prote.Technol.,1995,7(3):206-209(胡行俊.聚氯乙烯型材耐久性研究[J].腐蚀科学与防护技术,1995,7(3):206-209)
[4]YuGuocai,WangZhenyao,HanWei.Studyofatmosphericcorro sionofcarbonsteelandlowalloysteelsintropicalrainforestenvi ronments[J].J.IronandSteelRes.,2002,14(6):54(于国才,王振尧,韩薇.热带雨林地区碳钢,低合金钢的腐蚀规律研究[J].钢铁研究学报,2002,14(6):54)

[1]	FAN Yi,CHEN Linheng,CAI Jiaxing,DAi Qinqin,MA Hongchi,CHENG Xuequn. Corrosion Behavior of Hot-rolled AH36 Plate in Indoor Storage Environment[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[2]	PAN Chengcheng,MA Chao,XIA Dahai. Estimation for Relevance of Atmospheric Corrosion Initiation with Surface Texture of Several Metallic Materials by Electron Backscattering Diffraction[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[3]	ZHAO Jinbin,ZHAO Qiyue,CHEN Linheng,HUANG Yunhua,CHENG Xuequn,LI Xiaogang. Effect of Different Surface Treatments on Corrosion Behavior of 300M Steel in Qingdao Marine Atmosphere[J]. 中国腐蚀与防护学报, 2019, 39(6): 504-510.
[4]	DENG Junhao,HU Jiezhen,DENG Peichang,WANG Gui,WU Jingquan,WANG Kun. Effect of Oxide Scales on Initial Corrosion Behavior of SPHC Hot Rolled Steel in Tropical Marine Atmosphere[J]. 中国腐蚀与防护学报, 2019, 39(4): 331-337.
[5]	Yongwei SUN,Yuping ZHONG,Lingshui WANG,Fangxiong FAN,Yatao CHEN. Corrosion Behavior of Low-alloy High Strength Steels in a Simulated Common SO₂-containing Atmosphere[J]. 中国腐蚀与防护学报, 2019, 39(3): 274-280.
[6]	Li WANG, Chunyun GUO, Kui XIAO, Tuerxun·Silayiding, Chaofang DONG, Xiaogang LI. Corrosion Behavior of Carbon Steels Q235 and Q450 in Dry Hot Atmosphere at Turpan District for Four Years[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[7]	Jun WANG, Chao FENG, Bicao PENG, Yi XIE, Minghua ZHANG, Tangqing WU. Corrosion Behavior of Weld Joint of S450EW Steel in NaHSO₃ Solution[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[8]	Xinxin ZHANG,Zhiming GAO,Wenbin HU,Zhipeng WU,Lianheng HAN,Lihua LU,Yan XIU,Dahai XIA. Correlation Between Corrosion Behavior and Image Information of Q235 Steel Beneath Thin Electrolyte Film[J]. 中国腐蚀与防护学报, 2017, 37(5): 444-450.
[9]	Xin ZHANG,Nianwei DAI,Yan YANG,Junxi ZHANG. Effect of Direct Current Electric Field on Corrosion Mechanism of Zn Exposed to Simulated Industrial Environment[J]. 中国腐蚀与防护学报, 2017, 37(5): 451-459.
[10]	Xiaobo MENG,Wubin JIANG,Yongli LIAO,Ruihai LI,Zhijun ZHENG,Yan GAO. Investigation on Atmospheric Corrosion Behavior of Transmission Tower Materials in Simulated Industrial Environments[J]. 中国腐蚀与防护学报, 2017, 37(5): 460-466.
[11]	Shuangqing SUN,Qifei ZHENG,Chunling LI,Xiumin WANG,Songqing HU. Effect of Corrosion Products on Long-term Atmospheric Corrosion of Pure Aluminum 8A06[J]. 中国腐蚀与防护学报, 2017, 37(2): 110-116.
[12]	Ziheng BAI,Yunhua HUANG,Xiaogang LI,Lang YANG,Chaofang DONG,Lidan YAN,Kui XIAO. Environmental Corrosion in Industrial-marine Atmosphere at Qingdao of 7050 Al-alloy Anodized in Boric- and Sulfuric-acid Electrolyte[J]. 中国腐蚀与防护学报, 2016, 36(6): 580-586.
[13]	Dongliang LI,Guiqin FU,Miaoyong ZHU. Effect of Si on Corrosion Behavior of Model Bridge Steels by Alternative Wetting/drying Test in an Artificial Medium Simulated Hot and Humid Atmosphere of Marine and Industrial Area[J]. 中国腐蚀与防护学报, 2016, 36(5): 433-440.
[14]	Chuan WANG,Gongwang CAO,Chen PAN,Zhenyao WANG,Miaoran LIU. Atmospheric Corrosion of Carbon Steel and Weathering Steel in Three Environments[J]. 中国腐蚀与防护学报, 2016, 36(1): 39-46.
[15]	Yanjie LIU,Zhenyao WANG,Wei KE. Characterization of Corrosion Products on Pure Al Exposed in Atmospheres at Typical Rural, Industrial and Coastal Areas in China[J]. 中国腐蚀与防护学报, 2016, 36(1): 47-51.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed