微液滴现象与大气腐蚀—— Ⅰ. 微液滴的形成与扩展

张际标;王燕华;姜应律;王佳

广东海洋大学海洋资源与环境监测中心

MICRO-DROPLETS PHENOMENON AND ATMOSPHERIC CORROSION—— Ⅰ. Formation and spreading of micro-droplets

;;;

广东海洋大学海洋资源与环境监测中心

全文: PDF(263 KB)

摘要: 采用改变相对湿度、无机盐粒/金属组合和环境气氛等参数的方法研究了微液滴形成、生长的特征及其与大气腐蚀过程的关系.结果表明，微液滴形成和生长与气氛中氧和相对湿度及盐粒/金属组合密切相关.在大气环境中，微液滴形成和生长需要两个前提条件：第一，环境相对湿度须高于盐粒水解液滴液面的饱和蒸气压；第二，水解液滴下的金属应能被液滴腐蚀.

关键词 ：微液滴现象, 形成与扩展, 环境参数, 大气腐蚀

Abstract：he formation of the electrolyte droplet due to the deliquescence of soluble salt particles is one of the cause for the acceleration of atmospheric corrosion.A lot of micro-droplets,1 μm～10 μm in diameter,were observed around the edge of the main-droplet formed by the deliquescence of salt particles deposited on metal surface in atmosphere.In this paper,the characteristics of the formation and spreading of the micro-droplets were investigated in detail in a humidity-controlled chamber.The results showed that oxygen,relative humidity and a combination of salt particles and metals played important role in the formation of micro-droplets.Two premises were necessary for the formation of micro-droplets in atmosphere.First,the relative humidity should exceed the saturated relative humidity of the main-droplet.Another was that the metal substrate could be eroded under the main-droplet.

Key words： micro-droplets phenomenon formation and spreading environment parameters atmospheric corrosion

收稿日期: 2005-05-18

ZTFLH:

TG172.3

通讯作者: 张际标 E-mail: zhangjb@gdou.edu.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张际标
	王燕华
	姜应律
	王佳
44.8K

引用本文:

张际标; 王燕华; 姜应律; 王佳 . 微液滴现象与大气腐蚀—— Ⅰ. 微液滴的形成与扩展[J]. 中国腐蚀与防护学报, 2006, 26(4): 207-210 .
. MICRO-DROPLETS PHENOMENON AND ATMOSPHERIC CORROSION—— Ⅰ. Formation and spreading of micro-droplets. J Chin Soc Corr Pro, 2006, 26(4): 207-210 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2006/V26/I4/207

[1]Evens U R.Hua B D Trans.Corrosion and Oxidation of Metals[M].Beijing:Mechanical Industry Press,1976:401-430(Evens U R.华保定译.金属的腐蚀与氧化[M].北京:机械工业出版社,1976:401-430)
[2]Trethewey K P,Chamberlain J.Corrosion for Science and Engineer-ing[M].Second Edition,London:Pearson Education Ltd.,1995:280-284
[3]Skerry B S,Johnson J B,Wood G C.Corrosion in smoke,hydrocar-bon and SO2polluted atmospheres—Ⅰ.General behavior of iron[J].Corros.Sci.,1988,28(7):657-695
[4]Stratmann M,Streeckel H.On the atmospheric corrosion of metalswhich are covered with thin electrolyte layers[J].Corros.Sci.,1990,30:681-714
[5]Zakipour S,Leygraf C.Quartz crystal microbalance applied to stud-ies of atmospheric corrosion of metals[J].Br.Corros.J.,1992,27(4):295-298
[6]Neufeld A K,Cole I S,Bond A M,et al.The initiation mechanism ofcorrosion of zinc by sodium chloride particle deposition[J].Corros.Sci.,2002,44:555-572
[7]Wang J,Tsuru T.Potential distribution and micro-droplets forma-tion on the metal with salt particle deposition[A].The 204thMeet-ing of the Electrochemical Society[C].Orlando,2003:472
[8]Tsuru T,Tamiya K I,Nishikata A.Formation and growth of micro-droplets during the initial stage of atmospheric corrosion[J].Elec-trochi.Acta,2004,49:2709-2715
[9]Wexler A,Hasagawa S.Relative humidity-temperature relation-ships of some saturated salt solutions in the temperature range 0 to50℃[J].Research of the National Bureau of Standards,1954,53:19-26

[1]	陈旭, 李帅兵, 郑忠硕, 肖继博, 明男希, 何川. X70管线钢在大庆土壤环境中微生物腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 175-181.
[2]	范益,陈林恒,蔡佳兴,代芹芹,马宏驰,程学群. 热轧AH36船板钢在室内仓储条件下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[3]	潘成成,马超,夏大海. EBSD技术研究金属材料晶体取向对大气腐蚀萌生的影响机理[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[4]	赵晋斌,赵起越,陈林恒,黄运华,程学群,李晓刚. 不同表面处理方式对300M钢在青岛海洋大气环境下腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 504-510.
[5]	邓俊豪,胡杰珍,邓培昌,王贵,吴敬权,王坤. 氧化皮对SPHC热轧钢板在热带海洋大气环境中初期腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 331-337.
[6]	孙永伟,钟玉平,王灵水,范芳雄,陈亚涛. 低合金高强度钢的耐模拟工业大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 274-280.
[7]	王力, 郭春云, 肖葵, 吐尔逊·斯拉依丁, 董超芳, 李晓刚. Q235和Q450钢在吐鲁番干热大气环境中长周期暴晒时的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[8]	王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO₃溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[9]	张新新,高志明,胡文彬,伍志鹏,韩连恒,卢丽花,修妍,夏大海. Q235钢在薄液膜下腐蚀行为与图像信息的相关性研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 444-450.
[10]	张鑫,戴念维,杨燕,张俊喜. 模拟工业环境下直流电场对金属Zn腐蚀机理的影响[J]. 中国腐蚀与防护学报, 2017, 37(5): 451-459.
[11]	孟晓波,蒋武斌,廖永力,李锐海,郑志军,高岩. 输电杆塔材料在模拟工业环境中的大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 460-466.
[12]	孙霜青,郑弃非,李春玲,王秀民,胡松青. 腐蚀产物对纯Al 8A06长期大气腐蚀行为影响的研究[J]. 中国腐蚀与防护学报, 2017, 37(2): 110-116.
[13]	白子恒,黄运华,李晓刚,杨浪,董超芳,颜利丹,肖葵. 硫硼酸阳极氧化处理的7050铝合金在工业海洋大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(6): 580-586.
[14]	李东亮,付贵勤,朱苗勇. 湿热工业海洋大气中Si对桥梁钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(5): 433-440.
[15]	刘艳洁,王振尧,柯伟. 纯Al在3种典型沿海,工业和乡村大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(1): 47-51.

Viewed

Full text

Abstract

Cited

Shared

Discussed