混凝土抗氯离子渗透扩散性研究

蒋林华

河海大学材料科学与工程系

CHLORIDE PERMEABILITY TEST ON CONCRETE

Linhua Jiang

河海大学材料科学与工程系

全文: PDF(154 KB)

摘要: 采用快速氯离子渗透试验方法、稳态电迁移方法和电导方法，对普通水泥混凝土、轻骨料混凝土及掺粉煤灰、矿渣、硅粉、偏高岭土和稻壳灰的混凝土进行了氯离子渗透扩散性试验研究.结果表明，混凝土的抗氯离子渗透扩散能力随水灰比的减小而提高.粉煤灰和矿渣能提高混凝土的抗氯离子渗透扩散能力，硅粉、偏高岭土、稻壳灰和适当掺量的矿渣能大幅度提高混凝土的抗氯离子渗透扩散能力.在整个通电量范围内，通电量和初始电流之间并不存在良好的线性关系.

关键词 ：混凝土, 氯离子, 扩散性

Abstract：Three methods for measuring the chloride ion permeability were used,a nd the corresponding results were compared.The methods used were chloride perme ability test (AASHTO T227 and ASTM C1202),steady-state migration test and condu ctivity test.The concrete used in this paper included the control Portland ceme nt concrete,lightweight concrete and the concrete containing fly ash,slag,sil ica fume,metakaolin and rice husk ash.Test results indicate that the resistanc e of concrete to chloride ion penetration increases with the decrease of water-c ement ratio.Fly ash and slag can increase the resistance of concrete to chlorid e ion penetration,and silica fume,metakaolin,rice husk ash and some content s lag can increase significantly the resistance of concrete to chloride ion penetr ation.There is not a good linear relationship between the charge passed and ini tial current in the whole charge range.Three tests lead to a similar conclusion regarding the relative qualities of concretes.ASTM C1202 still can be used in many cases,and the conductivity test method appears to be better suited to the chloride permeability test.

Key words： concrete chloride ion diffusivity

收稿日期: 2001-06-29

ZTFLH:

TG174

通讯作者: 蒋林华

Corresponding author: Linhua Jiang

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	蒋林华
44.8K

引用本文:

蒋林华 . 混凝土抗氯离子渗透扩散性研究[J]. 中国腐蚀与防护学报, 2002, 22(6): 343-348 .
Linhua Jiang. CHLORIDE PERMEABILITY TEST ON CONCRETE. J Chin Soc Corr Pro, 2002, 22(6): 343-348 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2002/V22/I6/343

[1]ShiC ,etal.Effectofsupplementarycementingmaterialsonthespe cificconductivityofporesolutionanditsimplicationsontherapidchloridepermeabilitytest(AASHTOT277andASTMC1202)re sults[J].ACIMaterialsJournal,1998,95(4):389-394
[2]ZhangT ,GjrvOE .Anelectrochemicalmethodforacceleratedtestingofchloridediffusivityinconcrete[J].CementandConcreteResearch,1994,24(8):1534-1548
[3]StreicherPE ,AlexanderMG .Achlorideconductiontestforcon crete[J].CementandConcreteResearch,1995,25(6):1284-1294
[4]FeldmanRF ,etal.Investigationoftherapidchloridepermeabilitytest[J].ACIMaterialsJournal,1994,91(2):246-255
[5]FeldmanRF ,etal.Rapidchloridepermeabilitytestonblendedce mentandotherconcretes:correlationsbetweencharge,initialcur rentandconductivity[J].ConstructionandBuildingMaterials,1999,13:149-154
[6]ZhaoTJ,etal.Analternatingtestmethodforconcretepermeability[J].CementandConcreteResearch,1998,28(1):7-12

[1]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[2]	闻洋, 熊林, 陈伟, 薛刚, 宋文学. 干湿循环下聚乙烯醇纤维混凝土抗Cl^-渗透性能研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 381-388.
[3]	达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[4]	达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[5]	陈云翔, 冯丽娟, 蔡建宾, 王璇, 洪毅成, 林德源, 庄建煌, 杨怀玉. 新型复配阻锈剂在混凝土模拟液和试块中对钢筋锈蚀的抑制[J]. 中国腐蚀与防护学报, 2018, 38(4): 343-350.
[6]	田雪凯, 王海龙, 程旭东, 孙晓燕. 混凝土裂缝形态参数对Cl^-传输性能影响的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(4): 309-316.
[7]	苗伟行,胡文彬,高志明,孔宪刚,赵茹,唐军务. 304不锈钢在海洋环境混凝土模拟液中的腐蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(6): 543-548.
[8]	张建春,蒋金洋,李阳,施锦杰,左龙飞,王丹芊,麻晗. 耐海水腐蚀钢筋00Cr10MoV在模拟混凝土孔隙液中钝化膜的研究[J]. 中国腐蚀与防护学报, 2016, 36(5): 441-449.
[9]	毛江鸿,金伟良,张华,许晨,夏晋. 海砂混凝土建筑的耐久性提升技术及应用研究[J]. 中国腐蚀与防护学报, 2015, 35(6): 563-570.
[10]	冯兴国,卢向雨,左禹,陈达. 应变对混凝土孔隙液中不锈钢钝化性能影响的电化学研究[J]. 中国腐蚀与防护学报, 2015, 35(4): 372-378.
[11]	程旭东, 孙连方, 曹志烽, 朱兴吉, 赵立新. 沿海钢筋混凝土结构Cl^-侵蚀数值模拟方法研究[J]. 中国腐蚀与防护学报, 2015, 35(2): 144-150.
[12]	岳著文, 李镜培, 杨博, 邵伟, 吕韬. Cl^-在钢筋混凝土板一维双向扩散的分离变量法解答[J]. 中国腐蚀与防护学报, 2014, 34(1): 95-100.
[13]	杜雅莉, 张俊喜, 蒋俊, 原徐杰, 王灵芝, 马行驰. Cl^-浓度渐变的混凝土孔隙液中钢筋的腐蚀过程[J]. 中国腐蚀与防护学报, 2013, 33(4): 331-338.
[14]	许晨岳增国金伟良. 电化学频率调制技术在混凝土钢筋锈蚀中的应用[J]. 中国腐蚀与防护学报, 2013, 33(2): 136-140.
[15]	金伟良,岳增国,许晨,李志远. 混凝土中钢筋脱钝氯离子阈值的快速测定[J]. 中国腐蚀与防护学报, 2012, 32(3): 223-227.

Viewed

Full text

Abstract

Cited

Shared

Discussed