喷丸与电泳沉积稀土薄膜复合处理提高T91钢抗水蒸气氧化性能的研究

李辛庚;王学刚;何家文

西安交通大学

THE PROPERTY OF WATER VAPOR OXIDATION RESISTANCE OF T91 STEEL TREATED BY SHOT BLASTED ANDELECTROPHORESIS DEPOSITED RE COATING

Xingeng Li;Xuegang Wang;Jiawen He

西安交通大学

全文: PDF(173 KB)

摘要: 采用喷丸与电泳沉积稀土薄膜复合处理工艺对T91钢进行表面处理.在管式高温水蒸气氧化实验装置中，以600℃脱氧水蒸气氧化300 h的试验条件评价其抗水蒸汽氧化性能.结果表明，该处理方法可以减小氧化抛物线速度常数，有效改善抗氧化性能，较单一沉积稀土薄膜效果更为显著.与原材料相比，氧化物晶粒直径可由3～5 μm 细化至约0.5 μm.分析了喷丸与沉积稀土薄膜对氧化机理的影响，并讨论了复合处理工艺对氧化过程中扩散机理的影响以及氧化膜物相组成的变化.

关键词 ：喷丸, 稀土, 水蒸气氧化, 腐蚀, 耐热钢

Abstract：T91 steels with and without the treatments,shot bla sted (shot),electrophoresis deposited RE coating (RE),and combined treatments of shot blasted and deposited RE coating (shot+RE),were oxidized at 600℃ in water vapor for 300 hours by tubing device containing high temperature deoxidizing wa ter vapor.The results show that the combined treatments can decrease the parabol ic rate constant,effectively improve the property of water vapor oxidation resis tance and be superior to deposited RE coating only.Through combined treatments,t he grain size of the oxide scale deceases from 3～5 μm to 0.5 μm.The effects o f shot blasted and electrophoresis deposition RE coating on the oxidation mechan ism are analyzed,and the effects of the combined treatments on diffusion mechani sm in the oxidation process and the oxide scale phase forms are also discussed.

Key words： shot blast rare earth(RE) water vapor oxidat ion corrosion refractory steel

收稿日期: 2001-12-03

ZTFLH:

TG174.44

通讯作者: 李辛庚 E-mail: lxgeng204@sohu.com

Corresponding author: Xingeng Li E-mail: lxgeng204@sohu.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李辛庚
	王学刚
	何家文
44.8K

引用本文:

李辛庚; 王学刚; 何家文 . 喷丸与电泳沉积稀土薄膜复合处理提高T91钢抗水蒸气氧化性能的研究[J]. 中国腐蚀与防护学报, 2002, 22(2): 101-104 .
Xingeng Li, Xuegang Wang, Jiawen He. THE PROPERTY OF WATER VAPOR OXIDATION RESISTANCE OF T91 STEEL TREATED BY SHOT BLASTED ANDELECTROPHORESIS DEPOSITED RE COATING. J Chin Soc Corr Pro, 2002, 22(2): 101-104 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2002/V22/I2/101

[1]XuDL ,etal.PropertyofT91steelandprospectofitsapplicationinboilersofpowerplantsinChina[J].ElectricPowerConstructionofChina,1999,12(2):22.(徐德录等.T91钢的性能及在我国电站锅炉中的应用前景[J].电力建设,1999,12(2):22)
[2]WuFW .PropertyofT91andP91steelandprospectofitsapplica tion.RestrictedPublicationofTPRI,1992(吴非文.T91、P91钢的性能及其使用前景,内部资料,1992)
[3]DongDJ,XuJH .Researchonthenewferriticheat-resistantsteelswithhighstrength[J].JournalofIronandSteelResearch,1997,9(Suppl):52-55(董德俊等.新型铁素体热强钢的研究[J].钢铁研究学报,1997,9:52-55)
[4]HeY ,QiH ,BaiX ,WangD ,etal,Synergisticeffectsofsurfacemi cro-crystallisationandCeadditiononselectiveoxidationofNi-20Cralloy[J].HighTemperatureMaterialsandProcesses,2000(2),71:77
[5]MinamiYusuke,TooyamaAkira,SekiMikihito,NonakaKazuo,Ko gaKunitoshi.Steam-oxidationresistanceofshotblastedstainlesssteeltubingafter10-yearservice[J].NKKTechnicalReview,1996,1(75):10
[6]WhittleDP ,StringerJ.Improvementinproperties:additivesinoxi dationresistance[J].London:Phil.Trans.R .Soc.,1980(A ),295:309
[7]MoonDP .Roleofreactiveelementsinalloyprotection[J].Mater.Sci.Technol.,1989,5(8),754,764
[8]BirksN ,MeierGH .Introductiontohightemperatureoxidationofmetals[M ].EdwardArnoldLtd41BedtordSquare,LondonWCIB3DQ ,1983,40:51
[9]QHuibin,LoesDG ,HeYedong.EffectofsurfaceappliedrareearthcontainingthinoxidefilmsonhightemperatureoxidationofFe25Cr[J].CorrosionSci.andProtectionTech.,1999,(11):4
[10]StringerJ ,WilcoxBA .Thehightemperatueroxidationofnickel-20wt%chromiumalloyscontainingdispersedoxide phase[J].Oxid.Met.,1972,5(1):11
[11]CotellCM ,YurekGJ,HusseyRJ .Theinfluenceofgrain-boundarysegregationofYinCr2O3 ontheoxidationofCrmetal[J].Oxid.Met.,1990,(34):173
[12]PintBA .Experimentalobservationsinsupportofthedynamic-segregationtheorytoexplainthereactive-elementeffect[J].Oxid.Met.,1996,45(1):37
[13]GeorgeYLai.High-temperaturecorrosionofengineeringalloys[A ].ASMInternationalMaterialsParkOH 44073[C ],USA1996,21:23
[14]ZhuRZ ,HeYD ,QiHB .HighTemperatureCorrosionandHighTemperatureCorrosionResistantMaterials[M ].Shanghai:Shang haiScienceandTechnologyPress,1995,172:174(朱日彰,何业东,齐慧滨.高温腐蚀及耐高温腐蚀材料[M].上海:上海科学技术出版社,1995,172:174)

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed