电化学方法检测混凝土横梁中高强钢丝的腐蚀

中国腐蚀与防护学报

2003, Vol. 23

Issue (6): 362-366

研究报告

本期目录 | 过刊浏览

电化学方法检测混凝土横梁中高强钢丝的腐蚀

赵永韬;刘昌飞;高晓健

青岛市金湖路12号甲725所青岛分部

ELECTROCHEMICAL DETERMINATION OF CORROSION FORTHE HIGH STRENGTH STEEL WIRE IN CONCRETE CROSSBEAM

Yongtao Zhao;Changfei Liu;Xiaojian Gao

青岛市金湖路12号甲725所青岛分部

全文: PDF(193 KB)

摘要: 通过测量镦头自腐蚀电位等参数，判断吊杆钢丝的腐蚀概率；以吊杆钢丝和CCMP-I检测探头分别作为研究电极，运用恒电量技术检测获得Rp值和 Tafel常数，从而计算出腐蚀速率icorr.检测结果表明：压浆对增强钢丝的保护有成效；由于锈蚀原因不同，各短吊杆位置钢丝的锈蚀速率差异很大.

关键词 ：腐蚀, 钢丝, 混凝土, 恒电量, 横梁

Abstract：Initial survey to estimate corrosion of the bridge suspender was made by measuring the potential of anchor block,and other useful r elated information such as moisture and permeation of concrete in the crossbeam were also collected.Therefore the corrosion probability of steel wire might be g ot re asonably.In addition,while the steel wire and CCMP-I probe were treated respecti vely as the working electrode in the measurement electrode system,polarization r esistance and Tafel constant could be determined by the coulostatic method,thu s corrosion current density can also be calculated,so that the corrosion state o f st eel wire would be obtained more exactly.The results showed that the suspender st eel wire was protected by grouting,the corrosion rate of the steel wire in the s horter suspender existing a great gap with different reasons.

Key words： corrosion steel wire concrete coulostatic corssbeam

收稿日期: 2002-08-15

ZTFLH:

TU503

通讯作者: 赵永韬 E-mail: ytzhao7302@sina.com

Corresponding author: Yongtao Zhao E-mail: ytzhao7302@sina.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	赵永韬
	刘昌飞
	高晓健
44.8K

引用本文:

赵永韬; 刘昌飞; 高晓健 . 电化学方法检测混凝土横梁中高强钢丝的腐蚀[J]. 中国腐蚀与防护学报, 2003, 23(6): 362-366 .
Yongtao Zhao, Changfei Liu, Xiaojian Gao. ELECTROCHEMICAL DETERMINATION OF CORROSION FORTHE HIGH STRENGTH STEEL WIRE IN CONCRETE CROSSBEAM. J Chin Soc Corr Pro, 2003, 23(6): 362-366 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I6/362

[1]RodriguezP ,etal.Methodforstudyingcorrosioninreinforcedcon crete[J].Magaz.ConcreteRes.,1994,46(167):81
[2]GlassGK ,etal.Anassessmentofthecoulostaticmethodappliedtothecorrosionofsteelinconcrete[J].Corros.Sci.,1995,37(4):597
[3]RodriguezP ,etal.Useofthecoulostaticmethodformeasuringcor rosionratesofembeddedmetalinconcrete[J].Magaz.ConcreteRes.,1994,46(167):91
[4]HassaneinAM .Theuseofsmallelectrochemicalperturbationstoassessthecorrosionofsteelinconcrete[J].NDT&EInternational,1998,31(4):265
[5]ZhaoYongtao,WuJianhua,ZhaoChangjiu.Thecoulostaticmethodforstudyingcorrosioninreinforcedconcrete[J].Electrochemistry,2001,7(3):358(赵永韬,吴建华,赵常就.评价混凝土中的钢筋腐蚀的恒电量技术[J].电化学,2001,7(3):358)
[6]AndradeC ,GonzalezJA .Quantitativemeasurementsofcorrosionrateofreinforcingsteelembeddedinconcreteusingpolarizationre sistancemeasurements[J].WerkstoffeundKorrosion,1978,29:515

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed