硫酸盐还原菌生物膜下Cu-Zn合金的腐蚀研究

中国腐蚀与防护学报

2001, Vol. 21

Issue (6): 345-351

研究报告

本期目录 | 过刊浏览

硫酸盐还原菌生物膜下Cu-Zn合金的腐蚀研究

刘靖;许立铭;郑家shen

武汉市华中科技大学化学系

A STUDY ON CORROSION BEHAVIOR UNDER THE BIOFILM OFSULFATE-REDUCING BACTERIA ON Cu-Zn ALLOY

;;

武汉市华中科技大学化学系

全文: PDF(182 KB)

摘要: 从中原油田污水中分离提纯出硫酸盐还原菌(SRB)菌株，采用API RP-38推荐使用的培养基在铜材料上形成生物膜.结果表明，随着细菌的生长，细菌的代谢产物改变了黄铜的电极电位.用电子探针( EPMA)、X射线衍射(XRD)对生物膜形貌和成分进行了分析.生物膜中腐蚀产物成分主要有硫化亚铜(Cu2S)等硫化物，用交流阻抗(EIS)技术对生物膜结构进行了分析.

关键词 ： SRB, 黄铜, 腐蚀, 交流阻抗

Abstract：In this paper，the biofilm of sulfate-reducing bact eria (SRB) which plays an important role in corrosion of 70/30 Cu-Zn alloy under anaerobic condition has been studied.The API medium was used to culture the SR B in Zhongyuan oilfield.Potential/time measurement showed that the presence of SRB makes the corrosion protential more active with SRB growth metabolite.Elect rochemical impedance spectroscopy (EIS) was used to analyse the electrode proces s of 70/30 Cu-Zn alloy with SRB biofilm.X-ray diffraction and EPMA were used to analyse the corrosion products.The results show that the variation of activity of the SRB biofilm with SRB growth can be found from the EIS in inoculated medi a.The crystal of sub-copper sulfide (Cu2S) exists in the SRB biofilm.

Key words： SRB Cu-Zn alloy corrosion EIS

收稿日期: 2000-09-06

ZTFLH:

Q939.98

通讯作者: 刘靖

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	刘靖
	许立铭
	郑家shen
44.8K

引用本文:

刘靖; 许立铭; 郑家shen . 硫酸盐还原菌生物膜下Cu-Zn合金的腐蚀研究[J]. 中国腐蚀与防护学报, 2001, 21(6): 345-351 .

链接本文:

https://www.jcscp.org/CN/Y2001/V21/I6/345

[1] Tiller A K. Aspects of Microbiological Corrosion, "in Corrosion Processes" [M]. Pakins R N, ed. England, London; Applied Sci-
ence, 1982, 115
[2] Lutey R W, Norgan D E, Smith R W, Kennedy L A. Microbial Corrosion - A review of the Art for the Pulp and Paper Industry
[C]. New Zealand:Proc. Australian Corrosion Association Conference 24,Rotoura, 1984.
[3] Kuenen J G, Tuovinen O H. The Prokaryotes, A Handbook on Habitats Isolation and Identification of Bacteria [M]. Springer
Verlag, New York, 1981, 1023.
[4] Shalaby H M, Hasan A A, Al-Sabti F. Effect of inorganic sulfide and bacterial microfouling on corrosion of 70/30 copper/nick-
el alloy in seawater[J]. Corrosion 98',1998,295:2
[5] Shalaby H M, Hasan A A, Al- Sabti F.The effect of sulfate- reducing bacteria on the electrochemical behavior of highly alloyed
stainless steel in seawater[A]. Taiwan :Proc. 9th Asian - Pacific Corrosion Control Conference, R. O. C. 1995, 423.
[6] Postgate J R.The sulfate- reducing bacteria[M] . Cambridge:Cambridge University Press, 1979,9-23
[7] Liu Hongfang, Xu Liming, Zheng Jiashen. Influence of SRB biofilm on corrosion of carbon steel[J] .Journal of Chinese Society
for Corrosion and Protection, 2000, 20 (1) : 41
(刘宏芳,许立铭,郑家(?).SRB生物膜与碳钢腐蚀的关系[Ｊ]．中国腐蚀与防护学报、２０００,２０(１):４１)
[8] Liu Hongfang, Xu Liming, Zheng Jiashen. Effects of biofilm on corrosion of carbon steel[J].Journal of Chinese Society for Cor-rosion and Protection, 1999, 19(5) :291
(刘宏芳,许立铭,郑家(?).生物膜对碳钢腐蚀的影响[Ｊ]．中国腐蚀与防护学报,1999,19(5):291)
[9] Cao Chu' nan. Electrochemical studies on corroding metallic electrodes in frequency domain[J]. Electrochemistry, 1996, 2(1) :1.
(曹楚南．腐蚀金属电极的电化学频域测量研究进展[Ｊ]．电化学．１９９６．２(１):１)

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed