溅射纳米晶IN738合金的恒温氧化行为

耿树江;王福会;朱圣龙

中科院金属所;金属腐蚀与防护国家重点实验室

ISOTHERMAL OXIDATION BEHAVIOR OF SPUTTERED IN738 NANOCRYSTALLINE COATING

Shujiang Geng;Fuhui Wang;Shenglong Zhu

中科院金属所;金属腐蚀与防护国家重点实验室

全文: PDF(329 KB)

摘要: 利用磁控溅射方法在IN738合金上制备了同成分的纳米晶涂层，研究了该合金与纳米晶涂层在800℃、900℃和1000℃的恒温氧化行为.结果表明：纳米晶涂层在900℃和1000℃氧化时能形成双层的外氧化膜，表层为TiO2和Cr2O3为主的混合氧化物层，内层为连续的Al2O3层，没有内氧化及氮化，但在800℃氧化却不能形成连续的Al2O3内层.讨论了纳米晶的氧化机理.

关键词 ：溅射, IN738合金, 纳米晶, 氧化

Abstract：A sputtered nanocrystalline coating of IN738 alloy was obtained by means of magnetron sputtering.The isothermal oxidation behavior of the bulk alloy and nanocrystalline coating of IN738 in air was studied.The r esults indicated that a double external oxide scale was formed on the nanocrysta lline coating at 900℃ and 1000℃ without internal oxidation and nitridation.Th e scale consisted of an outer part of main Cr2O3 and an inner part of a cont inuous Al2O3 scale,which offered good adhesive and protectiveness.However, at 800℃ the inner continuous Al2O3 scale was not formed on the coating.Th e oxidation mechanism of the nanocrystalline coating was also discussed.

Key words： sputtering IN738 alloy nanocrystalline oxidation

收稿日期: 2000-12-30

ZTFLH:

TG172.82

通讯作者: 耿树江

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	耿树江
	王福会
	朱圣龙
44.8K

引用本文:

耿树江; 王福会; 朱圣龙 . 溅射纳米晶IN738合金的恒温氧化行为[J]. 中国腐蚀与防护学报, 2001, 21(3): 137-143 .
Shujiang Geng, Fuhui Wang, Shenglong Zhu. ISOTHERMAL OXIDATION BEHAVIOR OF SPUTTERED IN738 NANOCRYSTALLINE COATING. J Chin Soc Corr Pro, 2001, 21(3): 137-143 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2001/V21/I3/137

[1]WhittleDP .HighTemp.AlloysforGasTurbines[M].London:Appl.Sci.Pub.,1978,109
[2]FelixP .In:HartAB ,CutlerJBeds,DepositionandCorrosioninGasTurbines[M],.London:ApplSciPub.,1972,331
[3]LouHY ,WangFH ,XiaBJ,etal.OxidationbehaviorofcastsuperalloyK38Ganditsmicrocrystallinecoating[J].CorrosionScienceandProtectionTtechnique,1993,5(2):101(楼翰一,王福会,夏邦杰等.K38G合金及其溅射微晶层的高温氧化[J].腐蚀科学与防护技术.1993,5(2):101)
[4]LouH ,WangF ,XiaB .etal.Hightemperatureoxidationresistanceofsputteredmicro-grainsuperalloyK38G [J].Oxid.Met.,1992,38:299
[5]ChenGF ,LouHY .HightemperatureoxidationbehaviorofthesputteredNi-8Cr-3.5Alnanocrystallinecoating[J].ActaMetallurgicaSinica,2000,36(1):59(陈国锋,楼翰一.溅射Ni-8Cr-3.5Al纳米晶涂层的抗高温氧化行为[J].金属学报,2000,36(1):59)
[6]XiaB ,LouH ,ZhangL .Morphologyandmicrostructureofsputteredsuperalloycoating[J].J .Mater.Sci.Technol.,1993,9:116
[7]BouihisY ,St.JohnC .,Na2SO4andNaClinducedhotcorrosionofsixNi-basesuperalloy[J].Oxid.Met.,1975,9:507
[8]BennettMJ ,TusonAT ,KnightsCF ,etal.OxidationprotectionofalloyIN738LCbyplasmaassistedsilicacoating[J].Mater.Sci.Technol.,1989,5:841
[9]AbeF ,ArakiH ,YoshidaH ,etal.Theroleofaluminumandtitaniumontheprocessofanickel-basesuperalloyinsteamat800℃[J].Oxid.Met.,1987,27:21
[10]WagnerC .Typesofreactionintheoxidationofalloys[J].Z .Elektrochem.,1959,63:772
[11]WangF ,YoungDJ .EffectofnanocrystallizationonthecorrosionresistanceofK38GsuperalloyinCO +CO2 atmospheres[J].Oxid.Met.,1997,48:497
[12]WangF .TheeffectofnanocrystallizationontheselectiveoxidationandadhesionofAl2O3scale[J].Oxid.Met.,1997,48:215
[13]KvernesIA ,KofstadP .TheoxidationbehaviorofsomeNi-Cr-AlAlloysathightemperatures[J].Metall.Trans.,1972,3:1511

[1]	陈嘉晨,王忠维,乔利杰,岩雨. 机械摩擦磨损与电化学腐蚀在特殊环境中的作用机制[J]. 中国腐蚀与防护学报, 2019, 39(5): 404-410.
[2]	骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[3]	史昆玉,张进中,张毅,万毅. Nb₂N涂层制备及其耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[4]	陈浩,陈庆,辛丽,时龙,朱圣龙,王福会. DD98M纳米晶AlSi渗层制备及抗高温腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 59-67.
[5]	孙超, 杨潇, 文玉华. 表面溅射高含铝奥氏体不锈钢合金涂层对316不锈钢抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 590-596.
[6]	杨甜甜,徐敬军,钱余海,李美栓. 石墨基体上ZrC/MoSi₂微叠层涂层的制备及抗超高温氧化性能[J]. 中国腐蚀与防护学报, 2016, 36(5): 476-482.
[7]	晏敏胜, 何进, 冒守栋, 杨丽景, 聂霞, 宋振纶, 詹肇麟. NiCrAlY薄膜对Sm₂Co₁₇磁体高温抗氧化性的影响[J]. 中国腐蚀与防护学报, 2015, 35(2): 183-188.
[8]	崔玉卉,胡锐,张铁邦,李健,寇宏超,李金山. Fe基非晶/纳米晶涂层的微结构及其在H₂O₂溶液中的腐蚀性能[J]. 中国腐蚀与防护学报, 2012, 32(4): 317-321.
[9]	杨青松,李纯,王杰,杨仲年,张昭,张鉴清. 阳极电沉积制备CeO₂薄膜[J]. 中国腐蚀与防护学报, 2012, 32(1): 34-38.
[10]	沈长斌,杨怀玉,王胜刚,龙康,王福会. 稀硫酸中丙烯基硫脲对纳米工业纯铁腐蚀作用[J]. 中国腐蚀与防护学报, 2010, 30(6): 433-436.
[11]	孟国哲; 李瑛; 王福会 . 纳米Fe－10Cr涂层电化学腐蚀行为影响研究 I钝化性能[J]. 中国腐蚀与防护学报, 2007, 27(1): 35-42 .
[12]	孟国哲; 李瑛; 王福会 . 纳米Fe－10Cr涂层电化学腐蚀行为影响研究 Ⅱ点蚀性能[J]. 中国腐蚀与防护学报, 2007, 27(1): 43-47 .
[13]	任鑫; 汪信; 王福会 . 溅射NiCrAlY渗铝涂层的高温氧化行为[J]. 中国腐蚀与防护学报, 2006, 26(6): 365-370 .
[14]	吕海波; 李瑛; 王福会 . 纳米化对Cu-20Zr合金腐蚀行为的改善[J]. 中国腐蚀与防护学报, 2006, 26(3): 171-175 .
[15]	吕海波; 李瑛; 王福会 . Cu-20Zr合金在盐酸溶液中的脱合金腐蚀历程[J]. 中国腐蚀与防护学报, 2006, 26(2): 75-79 .

Viewed

Full text

Abstract

Cited

Shared

Discussed