化学沉积Ni-Zn-P合金制备和腐蚀性能研究

中国腐蚀与防护学报

2004, Vol. 24

Issue (5): 297-300

研究报告

本期目录 | 过刊浏览

化学沉积Ni-Zn-P合金制备和腐蚀性能研究

王森林

华侨大学材料科学与工程学院

Preparation and Corrosion properties of Electroless Ni-Zn-P Alloy Deposits

Senlin Wang

华侨大学材料科学与工程学院

全文: PDF(121 KB)

摘要: 采用柠檬酸钠为络合剂，在氨性缓冲介质中化学镀Ni-Zn-P合金。考察了工艺参数（pH、ZnSO4.7H2O浓度和温度）对沉积速度和镀层组成的影响。发现Zn离子在沉积过程中起阻碍作用，致使镀层中Zn含量不高（最多含16.0mass%）。采用差示扫描量热（DSC）和X射线衍射（XRD）技术研究所得化学镀Ni-Zn-P合金（Ni=78.7mass%,Zn=11.7mass%)的晶化行为和结构。结果表明，镀态Ni-Zn-P合金主要由非晶相和少量立言镍两相构成。热处理至384.8℃时出现四方Ni3P相，到580.7℃时出现Ni5Zn21相。镀态及热处理后的Ni-Zn-P合金（Ni=78.7mass%,Zn=11.7mass%)在3.5%NaCl中（pH=7.0）的腐蚀失重及阳极极化测量。结果表明，该合金的耐腐蚀性能优良，特别是镀态Ni-Zn-P合金。

关键词 ：化学镀, Ni-Zn-P合金, 晶化, 腐蚀

Abstract：Electroless Ni-Zn-P alloy deposits from an alkaline bath cntaining NH4Cl as a buffer agent and sodium citrate as a complexing agent was investigated. The effects of deposition parameters9pH,concentration of ZnSO4.7H2O and temperature)on the plating rate and the deposit composition was examined respectively. It was found that the presence of zinc in the bath has an inhibitory effect n the alloy deposition. As a consequence, the percentage of zinc in the electroless Ni-Zn-P alloys never reaches high values. The structure and the crystallization behavior of the deposit has been characterized by XRD and DSC. The results show that the as-plated deposits consist of mainly an amorphous structure together with some cubic phase Ni. The deposits crystallized into Ni3P at 384.8℃ and transformed into Ni5Zn21 at 580.7℃. The weight loss test and the anodic polarization measurements of the as-plated and the heat-treated deposits in 3.5mass% NaCl solution(pH7.0) indicate that the two deposits show good corrosion resistance, especially the as-plated deposit.

Key words： electroless plating Ni-Zn-P alloy crystallization corrosion

收稿日期: 2003-05-12

ZTFLH:

O646

通讯作者: 王森林

Corresponding author: Senlin Wang

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王森林
44.8K

引用本文:

王森林 . 化学沉积Ni-Zn-P合金制备和腐蚀性能研究[J]. 中国腐蚀与防护学报, 2004, 24(5): 297-300 .
Senlin Wang. Preparation and Corrosion properties of Electroless Ni-Zn-P Alloy Deposits. J Chin Soc Corr Pro, 2004, 24(5): 297-300 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I5/297

[1]SchlesingerM ,MengXY ,SnyderDD .ElectrolessNiZnPfilms[J]J .Electrochem.Soc.,1990,137(6):1858-1859
[2]SchlesingerM ,MengXY ,SnyderDD .ThemicrostructureandelectrochemicalpropertiesofelectrolessZnNiPalloy[J].J.Elec trochem.Soc.,1991,138(2):406-410
[3]BouananiM ,CherkaouiF ,CherkaouiM ,etal.NiZnPalloydeposi tionfromsulfatebath:inhibitoryeffectofzinc[J].J.Appl.Elec trochem.,1999,29:1171-1176.
[4]OulladjM ,SaidiD ,ChassaingE ,etal.PreparationandpropertiesofelectrolessNiZnPalloyfilms[J].J .Mater.Sci.,1999,34:2437-2439
[5]ValovaE ,GeorgievI ,ArmyanovS ,etal.Incorporationofzincinelectrolessdepositednickel-phosphorusalloy(Ⅰ)[J].J .Elec trochem.Soc.,2001,148(4):C266-C273.
[6]ValovaE ,ArmyanovS ,FranquetA ,etal.Incorporationofzincinelectrolessdepositednickel-phosphorusalloy(Ⅱ)[J].J .Elec trochem.Soc.,2001,148(4):C274-C279

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed