在600℃～700℃固态NaCl和水蒸气综合作用下K38G及其纳米晶涂层的腐蚀行为

中国腐蚀与防护学报

2003, Vol. 23

Issue (4): 193-197

研究报告

本期目录 | 过刊浏览

在600℃～700℃固态NaCl和水蒸气综合作用下K38G及其纳米晶涂层的腐蚀行为

耿树江;朱圣龙;王福会

中科院金属所;金属腐蚀与防护国家重点实验室

THE SYNERGETIC EFFECT OF NaCl AND WATER VAPORON THE CORROSION BEHAVIOR OF K38G ALLOYAND ITS NANOCRYSTALLINE COATING AT 600℃-700℃

Shujiang Geng;Shenglong Zhu;Fuhui Wang

中科院金属所;金属腐蚀与防护国家重点实验室

全文: PDF(192 KB)

摘要: 用磁控溅射方法在K38G合金上溅射了一层与其成分相同的纳米晶涂层，研究了铸态合金及其纳米晶涂层在600℃～700℃固态NaCl 和水蒸气综合作用下的腐蚀行为.结果表明，纳米晶涂层的腐蚀增重比铸态合金的大，抗腐蚀能力反而下降.讨论了铸态合金和纳米晶涂层的腐蚀机理.

关键词 ： K38G合金, 溅射, 纳米晶涂层, 盐水, 腐蚀

Abstract：The sputtered nanocrystalline coating of K38G alloy was obtained by means of magnetron sputtering.The corrosion behavior of cast K3 8G alloy and its sputtered nanocrystalline coating with a solid NaCl deposit in dry air or in wet oxygen at 600℃～700℃ was studied.The results indicated that the mass gain of the coating was higher than that of the cast alloy.Nanocrystall ization reduced corrosion resistance of the K38G alloy.The relevant corrosion me chanisms were discussed.

Key words： K38G sputtered nanocrystalline coating NaCl water vapo r corrosion

收稿日期: 2001-11-26

ZTFLH:

TG174.4

通讯作者: 耿树江

Corresponding author: Shujiang Geng

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	耿树江
	朱圣龙
	王福会
44.8K

引用本文:

耿树江; 朱圣龙; 王福会 . 在600℃～700℃固态NaCl和水蒸气综合作用下K38G及其纳米晶涂层的腐蚀行为[J]. 中国腐蚀与防护学报, 2003, 23(4): 193-197 .
Shujiang Geng, Shenglong Zhu, Fuhui Wang. THE SYNERGETIC EFFECT OF NaCl AND WATER VAPORON THE CORROSION BEHAVIOR OF K38G ALLOYAND ITS NANOCRYSTALLINE COATING AT 600℃-700℃. J Chin Soc Corr Pro, 2003, 23(4): 193-197 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I4/193

[1]HossainMK ,SaundersSRJ .Conf.HighTemperatureAlloysGasTurbines,1978:239
[2]ShinataY ,TakahashiF ,HashiuraK .NaCl-inducedhotcorrosionofstainlesssteels[J].Mater.Sci.Eng.,1987,87:399
[3]ShuY ,WangF ,WuW .CorrosionbehaviorofpureCrwithasolidNaCldepositinO2 pluswatervapor[J].Oxid.Met.,2000,54:457
[4]ShuY ,WangF ,WuW .SynergeticeffectofNaClandwatervaporonthecorrosionofTi60alloyat500～700℃[J].Oxid.Met.,1999,52:463
[5]ShuY ,WangF ,WuW .SynergeticeffectofNaClandwatervaporonthecorrosionof1Cr11Ni2W 2MoVsteelat500～700℃[J].Ox id.Met.,1998,51:97
[6]LouH ,WangF ,XiaB ,ZhangL .High-temperatureoxidationre sistanceofsputteredmicro-grainsuperalloyK38G [J].Oxid.Met.,1992,38:299
[7]LouH ,WangF ,ZhuS ,XiaB ,ZhangL .OxideformationofK38Gsuperalloyanditssputteredmicrograinedcoating[J].Surf.Coat.Tech.,1994,63:105
[8]WangF .TheeffectofnanocrystallizationontheselectiveoxidationandadhesionofAl2O3 scales[J].Oxid.Met.,1997,48:215
[9]WangF ,YoungDJ .EffectofnanocrystallizationonthecorrosionresistanceofK38GsuperalloyinCO +CO2 atmospheres[J].Oxid.Met.,1997,48:497
[10]GengS ,WangF ,ZhuS ,WuW .Hotcorrosionresistanceofasput teredK38Gnanocrystallinecoatinginmoltensulfateat900℃[J].Oxid.Met.,(accepted)
[11]HiramatsuN ,UematsuY ,TanakaT ,KinugasaM .Effectsofalloy ingelementsonNaCl-inducedhotcorrosionofstainlesssteel[J].Mater.Sci.Eng.,1989,A120:3190

[1]	骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[2]	史昆玉,张进中,张毅,万毅. Nb₂N涂层制备及其耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[3]	陈浩,陈庆,辛丽,时龙,朱圣龙,王福会. DD98M纳米晶AlSi渗层制备及抗高温腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 59-67.
[4]	孙超, 杨潇, 文玉华. 表面溅射高含铝奥氏体不锈钢合金涂层对316不锈钢抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 590-596.
[5]	杨甜甜,徐敬军,钱余海,李美栓. 石墨基体上ZrC/MoSi₂微叠层涂层的制备及抗超高温氧化性能[J]. 中国腐蚀与防护学报, 2016, 36(5): 476-482.
[6]	晏敏胜, 何进, 冒守栋, 杨丽景, 聂霞, 宋振纶, 詹肇麟. NiCrAlY薄膜对Sm₂Co₁₇磁体高温抗氧化性的影响[J]. 中国腐蚀与防护学报, 2015, 35(2): 183-188.
[7]	蒋穹,缪强,姚正军,魏小昕. 水性Al-Zn-Si合金涂层微观组织及腐蚀性能研究[J]. 中国腐蚀与防护学报, 2012, 32(4): 311-316.
[8]	崔玉卉,胡锐,张铁邦,李健,寇宏超,李金山. Fe基非晶/纳米晶涂层的微结构及其在H₂O₂溶液中的腐蚀性能[J]. 中国腐蚀与防护学报, 2012, 32(4): 317-321.
[9]	余建飞;江莉;甘复兴. 3-氨基-5-巯基-1,2,4-三唑在除盐水中对Cu的缓蚀作用[J]. 中国腐蚀与防护学报, 2010, 30(1): 21-24.
[10]	任鑫; 汪信; 王福会 . 溅射NiCrAlY渗铝涂层的高温氧化行为[J]. 中国腐蚀与防护学报, 2006, 26(6): 365-370 .
[11]	吕海波; 李瑛; 王福会 . 纳米化对Cu-20Zr合金腐蚀行为的改善[J]. 中国腐蚀与防护学报, 2006, 26(3): 171-175 .
[12]	吕海波; 李瑛; 王福会 . Cu-20Zr合金在盐酸溶液中的脱合金腐蚀历程[J]. 中国腐蚀与防护学报, 2006, 26(2): 75-79 .
[13]	孟国哲; 李瑛; 王福会 . Fe-20Cr纳米涂层的电化学行为[J]. 中国腐蚀与防护学报, 2006, 26(1): 11-18 .
[14]	田秀娟; 王福会; 李庆芬 . 搪瓷／NiCrAlY复合涂层的抗高温氧化及热腐蚀行为[J]. 中国腐蚀与防护学报, 2005, 25(6): 344-350 .
[15]	席艳君; 贺连龙; 王福会 . 纳米化对Ti48Al8Cr2Ag合金抗氧化和抗腐蚀[J]. 中国腐蚀与防护学报, 2005, 25(3): 135-141 .

Viewed

Full text

Abstract

Cited

Shared

Discussed