除氧中性水中钨酸盐对碳钢缓蚀机理研究

李燕;张关永;陆柱

华东理工大学防腐蚀中心

CORROSION INHIBITION MECHANISM OF CARBON STEEL WITH TUNGSTATE IN DEAERATED NEUTRAL AQUATIC MEDIUM

Yan Li;;

华东理工大学防腐蚀中心

全文: PDF(157 KB)

摘要: 运用旋转圆盘电极测定碳钢的阳极极化曲线,研究了在含Cl-的中性腐蚀介质中钨酸盐对碳钢的缓蚀机理.结果表明钨酸钠对碳钢的缓蚀作用为钝化机理,但介质中Mg2+离子的存在对该钝化作用有显著影响.

关键词 ：钨酸钠, 碳钢, 缓蚀机理, 钝化

Abstract：Anodic polarization curves of carbon steel were measured using rotating disk electrode. The inhibition mechanism of carbon steel with tungstate in deaerated neutral solution was investigated. The results indicated that the passivation film formed on the surface of carbon steel during the process of anodic polarization. The existence of Mg2+ ions in solution could effected the formation of passivation film.

Key words： tungstate carbon steel passivation corrosion inhibition

收稿日期: 1999-11-05

ZTFLH:

TG174.2

通讯作者: 李燕

Corresponding author: Yan Li

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李燕
	张关永
	陆柱
44.8K

引用本文:

李燕; 张关永; 陆柱 . 除氧中性水中钨酸盐对碳钢缓蚀机理研究[J]. 中国腐蚀与防护学报, 2000, 20(6): 349-354 .
Yan Li. CORROSION INHIBITION MECHANISM OF CARBON STEEL WITH TUNGSTATE IN DEAERATED NEUTRAL AQUATIC MEDIUM. J Chin Soc Corr Pro, 2000, 20(6): 349-354 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2000/V20/I6/349

[1] Snmitomo Metal industries Ltd. Corrosion inhibitors for an acidizing Solution for petroleum or natural gas wells[ A]. Jpn. Kokai Tokkyo Koho JP 59, 228, 591 [84, 228, 591 ] 21 Dec. 1984, 4
[ 2] Sastri V S, Packwood R H, Brown J R, et al. Corrosion inhibition by some oxyanions in coal-water slurries[J]. Br. Corrosion J.,1989, 24(1 ): 30 - 35
[3]贾能铀,陆柱水煤浆系统钨酸盐的缓蚀作用[J]华东化工学院学报.1990.16(30): 309—313
[4 ] Kotaro Ogura. Toskazu Majima. Stimulation of the passivation of iron by tungstate, molybdate and chromate ions [J].Electrochimica Acta. 1979, 24(4): 325 - 329
[5] Ose E, Zimina T Yu, Fokin M N. Dissolution and inhibition of iron in a neutral solution containing nonstoichiometric surfaceoxides[J]. Zashch. Met., 1985, 21 (6): 909 - 913
[6 ] Chew K K, Gabe D R. Alternatives to chromate for inhibition in deaerated acid solutions[J]. Corrosion Prevention and Control,1979, (8): 5-10
[7] Lumsden J B, Szklarska-Smialowska Z. The properties of films formed on iron exposed to inhibitive solution [J ]. Corrosion,1978, 34(5): 169 - 176
[8] Berdzenishvili G A, Strkalov P V, Mikhailovskii Yu N. Initial stages of the interaction of aluminum with aqueous solutioncontaining different oxo. anion[J]. Zashch Met., 1985, 21 (1 ): 37 - 42
[9]Balakrishnan K,Srinivasan S.使用旋转圆盘电极、循环伏安法研究缓蚀剂[A].第八届国际金属腐蚀会议论文选集(上) [C].北京:化工部化工机械研究院、化工部防腐蚀技术咨询中心编译,1982,171-174
[ 10] John A Dean. Lange's Hadbook of Chemistry[ M]. New York: MC Graw-Hill Book Company, 1979, 3 - 121, 5- 10
[11]M A安德森,AJ鲁宾.水溶液吸附化学[M]北京:科学出版社,1989.6-92
[12] Abd EI Kader J M, EI Warraky A A, Abd EI Aziz A M. Corrosion inhibition of mild steel by sodium tungstate in neutral solution part l: Behavior in distilled water[J]. Br. Corrosion J., 1998, 33(2): 139 - 144
[13]杨熙珍,杨武.金属腐蚀电化学热力学[M]北京:化学工业出版社,1991201-202

[1]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	王亚婷, 王棵旭, 高鹏翔, 刘冉, 赵地顺, 翟建华, 屈冠伟. 淀粉接枝共聚物对Zn的缓蚀性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[3]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[4]	张晨, 陆原, 赵景茂. CO₂/H₂S腐蚀体系中咪唑啉季铵盐与3种阳离子表面活性剂间的缓蚀协同效应[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[5]	何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[6]	张瑞,李雨,关蕾,王冠,王福雨. 热处理对激光选区熔化Ti6Al4V合金电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 588-594.
[7]	孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.
[8]	严少坤,郑大江,韦江,宋光铃,周廉. 钝性纯Ti在人工海水中的电化学活化行为研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 123-129.
[9]	丰涵,宋志刚,吴晓涵,李惠,郑文杰,朱玉亮. 022Cr25Ni7Mo4N双相不锈钢选择性腐蚀行为与两相组织的关系研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 138-144.
[10]	许萍,张硕,司帅,张雅君,汪长征. EPS的主要成分-蛋白质、多糖抑制碳钢腐蚀机理研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 176-184.
[11]	刘东,向红亮,刘春育. 含Ag抗菌双相不锈钢表面腐蚀产物的XPS分析[J]. 中国腐蚀与防护学报, 2018, 38(6): 533-542.
[12]	刘明,程学群,李晓刚,卢天健. 低合金钢筋在水泥萃取液中钝化膜的耐蚀机理研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 558-564.
[13]	钟显康,扈俊颖. 恒定的pH值和Fe²⁺浓度下X65碳钢的CO₂腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(6): 573-578.
[14]	王力, 郭春云, 肖葵, 吐尔逊·斯拉依丁, 董超芳, 李晓刚. Q235和Q450钢在吐鲁番干热大气环境中长周期暴晒时的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[15]	赵小燕, 刘希武, 崔新安, 于凤昌. 304L不锈钢在稀硝酸环境下的腐蚀研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 455-462.

Viewed

Full text

Abstract

Cited

Shared

Discussed