从三元混合气氛腐蚀相图到四元热腐蚀相图

李陵川

清华大学材料科学与工程系;北京100084

CONSTRUCTION OF PHASE STABILITY DIAGRAMS OF QUATERNARY HOT CORROSION TYPE BASED ON CALCULATION OF TERNARY MIXED ENVIRONMENT TYPE

LI Lingchuan (Dept. of Materials Science & Engineering; Tsinghua University; Beijing 100084)

全文: PDF(341 KB)

摘要: 三元混合气氛腐蚀相图和四元热腐蚀相图的计算具有相通性。三元体系中,将一凝聚相视为由单质金属和气相中两个组元反应生成,而在四元体系内把凝聚相设为由单质金属、Na-O-S体系中一凝聚相和气相中的两个组元反应而成。通过其反应自由能的变化来衡量判断相图中凝聚相西两组合的平衡线和叁叁组合的三相点。

关键词 ：混合气氛腐蚀, 热腐蚀, 稳定区相图

Abstract：Phase stability diagrams of quaternary hot corrosion type could be constructed on the basis of calculations of ternary mixed environment type diagrams. For both systems the condensed phases were considered to be the reaction products of the metal with two components in the gas phases, while for the hot corrosion type a condensed phase of the Na-O-S system was regarded as the reactant. The equilibrium lines and the triple points in the phase stability diagrams were calculated and selected by the free energy changes associated with the assumed reactions.

Key words： Mixed environment corrosion Hot corrosion Phase stability diagram

收稿日期: 1997-02-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李陵川
44.8K

引用本文:

李陵川. 从三元混合气氛腐蚀相图到四元热腐蚀相图[J]. 中国腐蚀与防护学报, 1997, 17(1): 58-62.
. CONSTRUCTION OF PHASE STABILITY DIAGRAMS OF QUATERNARY HOT CORROSION TYPE BASED ON CALCULATION OF TERNARY MIXED ENVIRONMENT TYPE. J Chin Soc Corr Pro, 1997, 17(1): 58-62.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1997/V17/I1/58

1 Gesmundo F, Young D J, Roy S K. High Temperature Materials and Processes, 1989, 8: 149
2 Natesam K. In: Rapp R A Ed., High Temperature Corrosion, NACE, Houston, 1983. 336
3 Giggins C S, Pettit F S. Oxidation of Metals, 1980, 14: 363
4 Meier G H, Birks N, Petter F S, Giggins C S. Oxidation of Metals, 1987, 27: 199
5 Harshe G, Venkatachalam S. Journal of Metals, 1984, 36: 34
6 Wang W C, Zhao Z B, Xia S K, Zhang W Q, Zhu R Z. Calphad, 1990, 14: 257
7 Connolly J A D, Kerriek D M, Calphad, 1987, 11: 1
8 Li L C, Gesmundo F, Viani F. Material Enginerring, 1993, 4(1): 133
9 Li L C, Gesmundo F, Viani F. Oxidation of Metals, 1993, 4(5/6): 395

[1]	陈超,梁艳芬,梁天权,满泉言,罗毅东,张修海,曾建民. 稀土复合掺杂ZrO₂陶瓷涂层抗Na₂SO₄+NaVO₃热腐蚀性能的研究进展[J]. 中国腐蚀与防护学报, 2019, 39(4): 291-298.
[2]	虞礼嘉,梁文萍,林浩,缪强,黄彪子,崔世宇. 激光重熔YSZ热障涂层950 ℃的热腐蚀行为[J]. 中国腐蚀与防护学报, 2019, 39(1): 77-82.
[3]	陈浩,陈庆,辛丽,时龙,朱圣龙,王福会. DD98M纳米晶AlSi渗层制备及抗高温腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 59-67.
[4]	王希靖, 王博士, 杨超, 杨艳, 沈斌. 纯Ni母材及焊缝在熔融Na₂SO₄-K₂SO₄中热腐蚀研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 495-501.
[5]	王喜忠,吴建颢,彭徽,郭洪波,宫声凯. 电子束物理气相沉积La₂Ce₂O₇热障涂层的高温燃气热腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(1): 36-40.
[6]	刘光明,刘康生,毛晓飞,万中平,黄健航,于明明,汪元奎. T91钢在KCl+Na₂SO₄+K₂SO₄熔融盐中的热腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(1): 23-28.
[7]	杨波,李茂东,刘光明,汪元奎,刘康生,翟伟,黄健航. 超音速喷涂Inconel 625/NiCr合金涂层的热腐蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(5): 483-488.
[8]	吴多利, 张洪宇, 韦华, 郑启, 金涛, 孙晓峰. 4种改性的铝化物涂层对DZ38G合金热腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2014, 34(6): 502-506.
[9]	王理,刘春阳,韩振宇,佟文伟. 燃气轮机涡轮零部件及材料热腐蚀行为与评价方法研究[J]. 中国腐蚀与防护学报, 2011, 31(5): 399-403.
[10]	徐仰涛,夏天东,闫健强. 合金元素对新型Co-Al-W合金热腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2010, 30(6): 457-464.
[11]	韦华;黄粮;梁静静;孙晓峰;管恒荣;胡壮麒. Re对NiCrAlY涂层热腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2010, 30(2): 150-154.
[12]	朱明李美栓周延春. Ti₃Al基合金表面两种Cr_1-xAl_xN（x=0.18, 0.47）涂层热腐蚀性能[J]. 中国腐蚀与防护学报, 2009, 29(4): 306-311.
[13]	于忠锋; 郑志; 刘恩泽; 于永泗; 朱耀宵 . 两种低偏析镍基高温合金抗热腐蚀性能的研究[J]. 中国腐蚀与防护学报, 2008, 28(5): 277-281 .
[14]	田秀娟; 王福会; 李庆芬 . 搪瓷／NiCrAlY复合涂层的抗高温氧化及热腐蚀行为[J]. 中国腐蚀与防护学报, 2005, 25(6): 344-350 .
[15]	李云; 郭建亭; 袁超; 杨洪才; 方龙; 刘学贵 . 镍基铸造高温合金K35的热腐蚀行为[J]. 中国腐蚀与防护学报, 2005, 25(4): 250-255 .

Viewed

Full text

Abstract

Cited

Shared

Discussed