腐蚀疲劳裂纹扩展的断裂模型

王荣

西安石油学院;西安710065

A FRACTURE MODEL FOR CORROSION FATIGUE CRACK PROPAGATION PROCESS

WANG Rong(Xi'an Petroleum Institute; Xi'an 710061)

全文: PDF(1193 KB)

摘要: 将修正的疲劳裂纹扩展静态断裂模型和裂尖腐蚀溶解相结合,提出了腐蚀疲劳裂纹扩展(CFCP)的腐蚀-钝化-断裂模型.根据该模型和断裂力学原理,导出了CFCP速率的定量表达式,它揭示了CFCP速率与力学条件,裂尖表面腐蚀率、加载频率、假设的裂尖材料元临界断裂应力之间的定量关系,并能说明氢脆对CFCP率的影响规律。实验结果表明,应用所提出的模型可很好地描述铝合金在35％NaCI中CFCP的一般规律。

关键词 ：腐蚀疲劳裂纹扩展, 材料元, 断裂, 腐蚀溶解, 铝合金

Abstract：Taking into simultaneous consideration of the modified static fracture model for fatigue crack propagation and the corrosion dissolution of the bare metal surface at a crack tip, a corrosion-bluntening-fracture model for corrosion fatigue crack propagation (CFCP) was proposed. According to the new model and linear elastic fracture mechanics, an expression for CFCP rate, which revealed the quantitative correlation among CFCP rate, stress intensity factor amplitude, the CFCP threshold, the corrosion rate of the bare metal at the crack tip, loading frequency and the critical fracture stress of the hypothetical material elements along the crack path, was derived. The expression could interpret the effect of hydrogen embrit-tlement on the CFCP process. The experimental results showed that the expression gave a good fit to the CFCP rates of two commercial aluminum alloys in 3.5% NaCl solution at loading frequency 10Hz.

Key words： Corrosion fatigue crack propagation Material elements Fracture Corrosion dissolution Aluminum alloy

收稿日期: 1998-04-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王荣
44.8K

引用本文:

王荣. 腐蚀疲劳裂纹扩展的断裂模型[J]. 中国腐蚀与防护学报, 1998, 18(2): 87-94.
. A FRACTURE MODEL FOR CORROSION FATIGUE CRACK PROPAGATION PROCESS. J Chin Soc Corr Pro, 1998, 18(2): 87-94.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y1998/V18/I2/87

1 Wei R P, Landes I D. Mats. Stand., 1969, 9(1):25
2 Dill H D, Saff C R. Environmental-Load Interaction Effects on Crack Growth, AFFDL-TR-78-137,1978
3 Holroyd N J H, Hardie D. Corro. Sci., 1983, 23(6):527
4 Hagn L. Mats. Sci. and Eng., 1988, A103(1):193
5 Lee U E. Corrosion fatigue and stress corrosion cracking of 7475 aluminum alloy, In: Corrosion Cracking, ASM, 1985. 123
6 Dover W D, Glinka G, Renolds A G(ed). Fatigue and Crack Growth in Offshore Structures, Conf. Proc., London, 1986
7 Zheng Xiulin, Hirt M A. Eng. Fract. Mech., 1983, 18(5): 965
8 Wanhill R J H, DeLuccia J J, Russo M T. The Fatigue in Aircraft Corrosion Testing(FACT), AGARD Rep. 713(AD-208359), 1989
9 Lai D N, Weiss V. Metall. Trans., 1978, 9A(2):413
10 萧纪美编著.金属韧性与韧化,上海科学技术出版社,1982
11 Bolton J D. Redington M L. Int. J. Fatigue, 1983, 5(3): 155
12 Lu Minxu, Zheng xiulin. Eng. Fract. Mech., 1993, 45(5): 889
13 Chen G S, Duquette D J. Metall. Trans., 1993, 23A(5): 1563
14 郑修麟著.金属疲劳的定量理论,西安:西北工业大学出版社,1994
15 路民旭,刘晓坤,王建军,郑修鳞.中国腐蚀与防护学报,1994,14(4):255
16 Chalant G, Petit J, Suyitno B. Fatigue 90, 1990. 1771
17 Dill H D, Saff C R, Enviroment-Load Interaction Effects on Crack Growth, AFFDL-TR-78-137,1979

[1]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[2]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[3]	赵东杨, 周宇, 王冬颖, 那铎. 磷化处理对核主泵螺栓断裂行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 539-544.
[4]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[5]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[6]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[7]	任建平,宋仁国. 双级时效对7050铝合金力学性能及氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 359-366.
[8]	夏俊捷,牛红志,刘敏,曹华珍,郑国渠,伍廉奎. 基于卤素效应的阳极氧化技术提高Ti48Al5Nb合金抗高温氧化性能[J]. 中国腐蚀与防护学报, 2019, 39(2): 96-105.
[9]	陈高红,胡远森,于美,刘建华,李国爱. 硫酸阳极化对2E12铝合金力学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 579-586.
[10]	曹敏, 刘莉, 余钟芬, 李瑛, 王福会. 2A02铝合金在模拟海洋大气环境中的剥蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 502-510.
[11]	马景灵, 通帅, 任凤章, 王广欣, 李亚琼, 文九巴. L-半胱氨酸/ZnO缓蚀剂对3102铝合金在碱性溶液中电化学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 351-357.
[12]	郝利新, 贾瑞灵, 张慧霞, 张伟, 赵婷, 翟熙伟. 7A52铝合金双丝MIG焊接头的不均匀性对其表面微弧氧化膜腐蚀防护作用的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 219-225.
[13]	杨钊, 时惠英, 蒋百灵, 葛延峰, 张静, 张曼玉, 李研. 脉冲电流对1050铝合金微弧氧化过程的影响[J]. 中国腐蚀与防护学报, 2018, 38(3): 283-288.
[14]	崔晓飞, 谭晓明, 王德, 钱昂. 铝合金表面聚氨酯涂层在加速实验条件下的老化机制及规律研究[J]. 中国腐蚀与防护学报, 2018, 38(1): 74-80.
[15]	孙超, 杨潇, 文玉华. 表面溅射高含铝奥氏体不锈钢合金涂层对316不锈钢抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 590-596.

Viewed

Full text

Abstract

Cited

Shared

Discussed