氢对2(1/4)Cr-1Mo钢力学性能的影响

钟曼英

中国计量学院机电学院杭州 310018

EFFECT OF HYDROGEN ON MECHANICAL PROPERTIES FOR 2(1/4)Cr-1Mo STEEL

ZHONG Manying

School of Mechanical and Electronic Engineering, China Institute of Metrology, Hangzhou 310018

全文: PDF(1056 KB)

摘要: 在模拟加氢反应器工况条件下，研究氢对加氢反应器器壁材料2(1/4)Cr-1Mo钢的力学性能的影响。采用低周疲劳实验计算原始状态和渗氢试样的裂纹扩展速率da/dN及门槛值Δ_th；并测试裂纹尖端附近的氢分布。结果表明，氢含量与应力场有关，应力越大氢含量就越高。假设在反应器壁内存在表面裂纹的情况下，估算了加氢反应器的剩余寿命。

关键词 ： 2(1/4)Cr-1Mo钢, 力学性能, 裂纹扩展速率da/dN, 氢分布, 剩余寿命

Abstract：The effect of hydrogen on the mechanical properties for 2(1/4)Cr-1Mo steel for hydrogenation reactor wall-materials was investigated at the simulated service condition of hydrogenation reactor. The crack propagation rate da/dN and the threshold value Δ_th at low frequency fatigue were calculated. Hydrogen distribution of crack tip were measured. The results showed that hydrogen content related to stress field. The higher the stress, the higher the hydrogen content. The residual cycle life for hydrogenation reactor was calculated, supposing surface crack exists in reactor.

Key words： 2(1/4)Cr-1Mo steel mechanical properties crack propagation rate da/dN hydrogen distribution residual life

收稿日期: 2010-04-06

ZTFLH:

TG113.25

通讯作者: 钟曼英 E-mail: xuzg2002@hzcnc.com

Corresponding author: ZHONG Manying E-mail: xuzg2002@hzcnc.com

作者简介: 钟曼英，女，1956年生，副教授，学士，研究方向为材料的力学行为及构件的失效

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	钟曼英
44.8K

引用本文:

钟曼英. 氢对2(1/4)Cr-1Mo钢力学性能的影响[J]. 中国腐蚀与防护学报, 2011, 31(3): 236-239.
ZHONG Man-Yang. EFFECT OF HYDROGEN ON MECHANICAL PROPERTIES FOR 2(1/4)Cr-1Mo STEEL. J Chin Soc Corr Pro, 2011, 31(3): 236-239.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2011/V31/I3/236

[1] Han G W，Song Y J. Effects of hydrogen atoms on initiation and propagation of cracks under slow loading [J]. Acta Metall. Sin., 1994, 30(10): A448-452

    (韩光炜, 宋余九. 慢加载条件下氢对裂纹萌生与扩展的作用 [J]. 金属学报, 1994, 30(10): A448-452)

[2] Li J L, Li X G, Xie G S, et al. Fatigue properties for 20 g and 2.25Cr-1Mo steels after hydrogen attack [J]. Acta Metall. Sin., 1995, 31(1): B26-30

    (郦建立, 李晓钢, 谢根栓等, 20 g和2.25Cr-1Mo钢氢腐蚀后的疲劳性能 [J]. 金属学报, 1995, 31(1): B26-30)

[3] Xu J, Hardie D, Zhong M Y. Effect of hydrogen on the behaviour of stainless steel weld overlay cladding applied to low alloy steel [J]. J. China Inst.Metrol., 2000, (1): 16-21

    (徐坚, Hardie D, 钟曼英. 氢对低合金钢上不锈钢堆焊层性能的影响 [J]. 中国计量学院学报, 2000, (1): 16-21)

[4] Pan C, Li Z B, Tian Z L. Hydrogen embrittlement of weld metal of austenitic stainless steels [J].Acta Metall. Sin., 2001, 37(9): 985-990

    (潘川, 李正邦, 田志凌. 不锈钢堆焊层金属的氢脆 [J]. 金属学报, 2001, 37(9): 985-990)

[5] Pan C, Li Z B, Liang D T. The threshold stress intensities for hydrogen-induced delayed failure of weld metal of austenitic stainless steel [J].Acta Metall. Sin., 2001, 37(3): 296-300

    (潘川, 李正邦, 梁东图. 奥氏体不锈钢焊缝金属氢致滞后断裂[J]. 金属学报, 2001, 37(3): 296-300)

[6] Zhong M Y, Wang X L. Characteristics of low frequency fatigue with short-cracks for 16Mng steel in hydrogen [J]. J. Chin. Soc. Corros. Prot., 1996, 16(2): 59-63

    (钟曼英, 王晓林. 在氢环境中16Mng钢的短裂纹低频疲劳特性 [J]. 中国腐蚀与防护学报, 1996, 16(2): 59-63)

[7] Zhong M Y, Xu J. Calculation of stress distribution for add-hydrogen reactor [J]. J. China Inst.Metrol., 2001, (1): 83-86

    (钟曼英, 徐坚. 加氢反应器的应力分布计算 [J]. 中国计量学院学报, 2001, (1): 83-86)

[8] Zhong M Y. Fracture properties of 2(1/4)Cr-1Mo steel in hydrogen [J]. J. Chem. Ind. Eng., (China), 2008, 59(2): 426-430

    (钟曼英. 在氢环境中2(1/4)Cr-1Mo钢的断裂特性 [J]. 化工学报, 2008, 59(2): 426-430)

[9] Wang Z G. Fatigue of Materials [M]. Bejing: National Industry Press, 1993

    (王中光. 材料的疲劳 [M]. 北京: 国防工业出版社, 1993)

[10] Wang Y L, Shao B Q. Fracture Mechanics Applications in Select Materials [M]. Beijing: Metallurgy Industry Press, 1992

     (汪一麟, 邵本逑. 断裂力学在选材方面的应用 [M]. 北京: 冶金工业出版社, 1992)

[1]	陈磊,裴志亮,肖金泉,宫骏,孙超. 磁过滤电弧离子镀制备TiAlN涂层的结构与性能表征[J]. 中国腐蚀与防护学报, 2017, 37(3): 241-246.
[2]	张新生,曹乃宁,李亚云. 基于Gumbel极值I型分布埋地油气管道的剩余寿命预测[J]. 中国腐蚀与防护学报, 2016, 36(4): 370-374.
[3]	吴进怡,罗琦,肖伟龙,柴柯,曹阳. 海水环境中弧菌对45钢腐蚀行为及力学性能的影响[J]. 中国腐蚀与防护学报, 2012, 32(4): 343-348.
[4]	赵羽习,任海洋. 基于固结试验和接触理论分析的铁锈力学性能[J]. 中国腐蚀与防护学报, 2010, 30(5): 383-390.
[5]	肖伟龙,柴柯,杨雨辉,吴进怡. 25钢在热带海洋环境下海水中的微生物腐蚀及其对力学性能的影响[J]. 中国腐蚀与防护学报, 2010, 30(5): 359-363.
[6]	薛艳;赵国仙;董会;赵大伟. 5Cr油管电化学充氢后的力学行为[J]. 中国腐蚀与防护学报, 2010, 30(1): 89-92.
[7]	俞芳高克玮路民旭. 流动状态下X65管线钢CO₂腐蚀产物膜结构和力学性能的评价[J]. 中国腐蚀与防护学报, 2009, 29(6): 401-404.
[8]	孙霜青郑弃非李德富陈杰温军国. LY12铝合金的长期大气腐蚀行为[J]. 中国腐蚀与防护学报, 2009, 29(6): 442-446.
[9]	李美姮; 管恒荣 . 热障涂层的性能评价[J]. 中国腐蚀与防护学报, 2007, 27(5): 309-314 .
[10]	汪淑英; 李具仓; 赵爱民 . 含铬高硅铁基合金组织和性能的研究[J]. 中国腐蚀与防护学报, 2007, 27(5): 292-295 .
[11]	罗天元 . 高比重钨合金材料的腐蚀特性[J]. 中国腐蚀与防护学报, 2004, 24(6): 356-359 .
[12]	孙广平; 贾树盛; 朱先勇; 郝博; 于妍 . 热固性丙稀酸酯类-壳结构互穿网络水性阻尼涂料的动态力学性能[J]. 中国腐蚀与防护学报, 2004, 24(1): 41-44 .
[13]	徐颖;袁路平;林栋梁;林建鸿;王正东;吴东棣. 堆焊结构的氢浓度分布及其对剥离断裂的影响[J]. 中国腐蚀与防护学报, 1995, 15(2): 112-118.

Viewed

Full text

Abstract

Cited

Shared

Discussed