十二烷基硫醇在Fe表面自组装成膜及对其的腐蚀保护

王静,李德刚,于先进,董云会,张丽鹏

山东理工大学化学工程学院淄博 255049

SAMS OF DODECYL MERCAPTAN AND ITS CORROSION PROTECTION ON IRON SURFACE

WANG Jing, LI Degang, YU Xianjin, DONG Yunhui, ZHANG Lipeng

School of Chemical Engineering, Shandong University of Technology,Zibo 255049

全文: PDF(770 KB)

摘要:

应用自组装技术在Fe电极表面制备正、叔十二烷基硫醇自组装膜，用反射傅立叶红外光谱（FT-IR）、电化学阻抗谱（EIS）和Tafel极化曲线对正、叔十二烷基硫醇自组装膜进行表征，结果表明，正、叔十二烷基硫醇都能在Fe表面形成自组装膜；设计了自组装膜的等效电路，并对EIS数据进行拟合；EIS拟合结果和Tafel极化曲线均表明，正、叔十二烷基硫醇自组装膜对Fe电极在 0.5 mol/L NaCl溶液中均具有较好的缓蚀作用，并且前者的缓蚀作用强于后者。

关键词 ： Fe, 正、叔十二烷基硫醇, 自组装膜, 缓蚀效率

Abstract：

Self-assembled monolayers (SAMs) of n-and t-dodecyl mercaptan were prepared on iron surface by self-assembly methods. From the results of FT-IR, it can be found that both the n-and t-dodecyl mercaptan can self-assemble on the surface of iron. Then the electrochemical impedance spectroscopy (EIS) and the Tafel polarization curves were performed to characterize the anticorrosion capability of the SAMs in 0.5 mol/L NaCl solution. The general equivalent circuits for the n-and t-dodecyl mercaptan SAMs were established. Based on the results of the EIS, proper equivalent circuit was chosen to fit the Nyquist impedance plots. The inhibition efficiency (IE) of the SAMs on iron corrosion have been calculated according to the fitted results and the Tafel polarization curves. When the iron electrode self-assembled in the n-and t-dodecyl mercaptan for 3h, the IE of the SAMs can reach about 89% and 80% respectively. Comparing with the SAMs of the t-dodecyl mercaptan, the SAMs of n-dodecyl mercaptan have more effective corrosion inhibition for iron as indicated by the high charge-transfer resistance shown in EIS and the positive corrosion potential in the Tafel polarization curves. It is quite possible that the steric hindrance of t-dodecyl mercaptan is bigger than that of n-dodecyl mercaptan. Therefore, it is easy to understand that the quality of the n-dodecyl mercaptan SAMs is better than that of the t-dodecyl mercaptan.

Key words： Fe n-and t-dodecyl mercaptan self-assembled monolayer(SAM) inhibitor efficiency

收稿日期: 2009-01-06

ZTFLH:

O646.6

基金资助:

山东省自然科学基金资助（Y2007F60）项目

通讯作者: 李德刚 E-mail: ldg@sdut.edu.cn

Corresponding author: LI Degang E-mail: ldg@sdut.edu.cn

作者简介: 王静，女，1983年生，硕士生，研究方向为应用电化学

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王静
	李德刚
	于先进
	董云会
	张丽鹏
44.8K

引用本文:

王静,李德刚,于先进,董云会,张丽鹏. 十二烷基硫醇在Fe表面自组装成膜及对其的腐蚀保护[J]. 中国腐蚀与防护学报, 2010, 30(3): 207-212.
YU Jing, LI De-Gang, YU Xian-Jin, DONG Yun-Hui, ZHANG Li-Peng. SAMS OF DODECYL MERCAPTAN AND ITS CORROSION PROTECTION ON IRON SURFACE. J Chin Soc Corr Pro, 2010, 30(3): 207-212.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2010/V30/I3/207

[1]	Cometto F P, Paredes-Olivera P, Macagno V A, et al. Density functional theory study of the adsorption of alkanethiols on Cu(111), Ag(111), and Au(111) in the low and high coverage regimes [J]. J. Phys. Chem., 2005, 109(46): 21737-21748
[2]	Muller-Meskamp L, Lussem B, Muller L, et al. A new phase of the c(4~2) superstructure of alkanethiols grown by vapor phase deposition on gold [J]. Langmuir, 2005, 21(12):5256-5258
[3]	Kong D S, Wan L J, Chen S H, et al. Progress in STM study of corrosion inhibitor self-assembled monolayers (SAMs) on metals II. corrosion inhibitor SAMs on engineering metals [J]. Corros. Prot.,2003, 24(12): 507-512
	(孔德生, 万立骏, 陈慎豪等. 金属表面缓蚀剂自组装单分子膜的STM研究进展. Ⅱ. 常用金属表面的缓蚀剂自组装单分子膜 [J]. 腐蚀与防护, 2003,24(12): 507-512
[4]	Bain C D, Troughton E B, Tao Y T, et al. Formation of monolayer films by the spontaneous assembly of organic thiols from solution onto gold [J]. J. Am. Chem. Soc, 1989, 111(1):321-335
[5]	Finklea H O, Avery S, Lynch M, et al. Blocking oriented monolayers of alkyl mercaptans on gold electrodes [J]. Langmuir, 1987, 3(22):409-413
[6]	Laibinis P E, Whitesides G M, Allara D L, et al. Comparison of the structures and wetting properties of self-assembled monolayers of n-alkanethiols on the coinage metal surfaces, copper, silver, and gold [J]. J. Am. Chem. Soc, 1991, 113(19):7152-7167
[7]	Li D G, Yu X J, Dong Y H. The different self-assembled way of n-and t-dodecyl mercaptan on the surface of copper [J]. Appl. Surf. Sci, 2007, 253:4182-4187
[8]	Shimazu K, Yagi I, Sato Y, et al. Packing state and stability of self-assembled monolayers of 11-ferrocenyl-1-undecanethiol on platinum electrodes [J]. Chem. Soc.Jpn, 1994, 67(3):863-865
[9]	Volmer-Uebing M, Reynders B,Stratmann M. Anbindungsverhalten organischer monomere auf eisenoberfl chen und korrosion der durch die anbindung chemisch modifizierten oberfl chen [J]. Werkst. Korros, 1991, 42(1):19-34
[10]	Nozawa K, Nishihara H, Aramaki K. Chemical modification of alkanethiol monolayers for protection iron against corrosion [J]. Corros. Sci, 1997, 39(9):1625-1639
[11]	Barcia O E, Mattos O R,Pebere N, et al. Mass-transport study for the electrodissolution of copper in 1M hydrochloric acid solution by impedance [J]. J.Electrochem. Soc, 1993, 140(10):2825-2833
[12]	Ma H Y, Chen S H, Niu L, et al. Studies on electrochemical behavior of copper in aerated NaBr solutions with Schiff base N,N'-o-phenylen-bis(3-methoxysalicylidenimine) [J]. J. Electrochem.Soc., 2001, 148(5): B208-B216
[13]	Ma H Y, Yang C, Chen S H, et al. Electrochemical investigation of dynamic interfacial processes at 1-octadecanethiol-modified copper electrodes in halide-containing solutions [J]. Electrochim. Acta, 2003, 48(28):4277-4289
[14]	Zamborini F P, Crooks R M. Corrosion passivation of gold by n-alkanethiol self assembled monolayers: effect of chain length and end group [J]. Langmuir, 1998, 14(12):3279-3286
[15]	Li J H. Electrochemistry of Self-assembled Monolayers [M].Beijing: Higher Education Press, 1996
[16]	(李景虹. 自组装膜电化学 [M]. 北京: 高等教育出版社, 1996)
[17]	Cao C N. Corrosion Electrochemistry [M]. Beijing:Chemical Industry Press, 2004
[18]	(曹楚南. 腐蚀电化学原理 [M]. 北京: 化学工业出版社, 2004)
[19]	Jenings G K, Munro J C, Yong T H, et al. Effect of chain length on the protection of copper by n-alkanethiols [J]. Langmuir, 1998, 14(21):6130-6139
[20]	Deflorian F, Fedrizzi L, Locaspi A, et al. Testing of corrosion resistant fluoropolymer coatings [J]. Electrochim. Acta, 1993, 38(14):1945-1950
[21]	Quan Z L, Chen S H, Li Y, et al. Adsorption behaviour of Schiff base and corrosion protection of resulting films to copper substrate [J]. Corros. Sci, 2002, 44:703-715

[1]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[2]	卢爽, 任正博, 谢锦印, 刘琳. 2-氨基苯并噻唑与苯并三氮唑复配体系对Cu的缓蚀性能[J]. 中国腐蚀与防护学报, 2020, 40(6): 577-584.
[3]	郑艳欣, 刘颖, 宋青松, 郑峰, 贾玉川, 韩培德. 含铁铜基陶瓷复合材料高温氧化行为与耐磨性研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 191-198.
[4]	魏欣欣,张波,马秀良. FeCr₁₅Ni₁₅单晶600 ℃下热生长氧化膜的TEM观察[J]. 中国腐蚀与防护学报, 2019, 39(5): 417-422.
[5]	廖彤,马峥,李蕾蕾,马秀敏,王秀通,侯保荣. Fe₂O₃/TiO₂纳米复合材料对304不锈钢的光生阴极保护性能[J]. 中国腐蚀与防护学报, 2019, 39(1): 36-42.
[6]	钟显康,扈俊颖. 恒定的pH值和Fe²⁺浓度下X65碳钢的CO₂腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(6): 573-578.
[7]	谭何灵,周成,刘希辉,曹国明,张菁. Cr对Q420钢在高盐度大气环境下耐蚀性的影响[J]. 中国腐蚀与防护学报, 2017, 37(3): 267-372.
[8]	肖斌,向军淮,张洪华. 四元Fe-Cu-Ni-Al合金900 ℃下的恒温及循环氧化行为[J]. 中国腐蚀与防护学报, 2017, 37(1): 69-73.
[9]	王春霞,陈敬平,张晓红,王赪胤. 溴化N-辛烷异喹啉在盐酸溶液中对Q235碳钢的缓蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(3): 245-252.
[10]	鲁文晔,陈蝶依,陈步荣,汤涛. 十六硫醇自组装膜对Ag的防变色作用研究[J]. 中国腐蚀与防护学报, 2016, 36(2): 172-176.
[11]	沈秋燕,刘宏芳,刘烈炜. 沉积硫对FeS及FeCO₃膜结构及耐蚀性影响[J]. 中国腐蚀与防护学报, 2016, 36(1): 79-86.
[12]	方玉荣,付朝阳. 酸性FeCl₃溶液中304不锈钢的超声腐蚀和缓蚀行为[J]. 中国腐蚀与防护学报, 2015, 35(4): 305-310.
[13]	宋芳,陈友媛,常钦鹏,彭涛. 植酸自组装膜对HAl77-2黄铜缓蚀性能的影响[J]. 中国腐蚀与防护学报, 2015, 35(4): 317-325.
[14]	罗睿, 吴军, 柳鑫龙, 周学杰, 郑鹏华, 张三平. Q235和09CuPCrNi-A钢在两种不同大气环境中腐蚀早期锈层演化研究[J]. 中国腐蚀与防护学报, 2014, 34(6): 566-573.
[15]	刘兰兰, 牛焱. Fe-Si合金在600 ℃不同气氛中的腐蚀[J]. 中国腐蚀与防护学报, 2014, 34(4): 307-314.

Viewed

Full text

Abstract

Cited

Shared

Discussed