模数对水性硅酸钾富锌涂层电化学行为的影响

中国腐蚀与防护学报

2008, Vol. 28

Issue (6期): 359-362

研究报告

本期目录 | 过刊浏览

模数对水性硅酸钾富锌涂层电化学行为的影响

王石青¹;何德良¹;丁庆云²;徐以兵^1;高娟¹;区永康¹

1.湖南大学化学化工学院长沙 410082
2.长沙市环境监测中心站长沙 410001

INFLUENCE OF THE MOLAR RATIO ON THE ELECTROCHEMICAL BEHAVIOR OF WATERBORNE POTASSIUM SILICATE ZINC-RICH COATING

WANG Shiqing¹;HE Deliang¹;DING Qingyun²;XU Yibing¹;GAO Juan¹;OU Yongkang¹

1.College of Chemistry and Chemical Engineering; Hunan University; Changsha 410082
2.Environmental Monitoring Center of Changsha; Changsha 410001

全文: PDF(1081 KB)

摘要:

通过测量涂层腐蚀电位与涂层电化学交流阻抗，研究了水溶性K2SiO3溶液的模数（SiO2 /K2O摩尔比）对水性无机富锌涂层电化学行为的影响。结果表明，水性无机富锌涂料随着水基模数的增加，涂层腐蚀电位增高，涂层对腐蚀介质的屏蔽性能增强，涂层中锌粉颗粒的活性溶解阻力增大。用扫描电子显微镜（SEM）观测不同模数水性无机富锌涂层的结构表明，水性无机富锌涂料水基模数的增加使涂层中锌粉颗粒之间充分交联，涂膜强度增大，涂层中锌粉颗粒之间的缝隙减小，涂层的致密性增强。

关键词 ：模数, 水性无机富锌涂料, 硅酸钾, 电化学行为, 电化学阻抗谱

Abstract：

The influence of the molar ratio （SiO2/K2O molar ratio） of potassium silicate solution on the electrochemical behavior of waterborne zinc-rich coating were studied by monitoring the variation of the corrosion potential （Ecorr） of the coatings and the electrochemical impedance spectroscopy （EIS）. With the promotion of SiO2/K2O molar ratio, the results showed that the shield effect of impenetration of corrosion medium to substrate was enhanced and the dissolution resistance of zinc particles in the coatings was increased with the Ecorr of the coatings. Besides, scanning electron microscope（SEM）was used to characterize the surface structure of the coatings with different SiO2/K2O molar ratio. While the SiO2/K2O molar ratio of waterborne inorganic potassium silicate zinc-rich paint increasing, the binding among Zn particles was reinforced, the intensity of the coatings was strengthened and gaps among the coatings decreased to form denser coating structure.

收稿日期: 2007-03-15

ZTFLH:

TG174.461

通讯作者: 何德良 delianghe@163.com

Corresponding author: WANG Shiqing delianghe@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王石青
	何德良
	徐以兵
	高娟
44.8K

引用本文:

王石青何德良丁庆云徐以兵高娟区永康. 模数对水性硅酸钾富锌涂层电化学行为的影响[J]. 中国腐蚀与防护学报, 2008, 28(6期): 359-362.
YU Shi-Jing, HE De-Liang, XU Si-Bing, GAO Juan. INFLUENCE OF THE MOLAR RATIO ON THE ELECTROCHEMICAL BEHAVIOR OF WATERBORNE POTASSIUM SILICATE ZINC-RICH COATING. J Chin Soc Corr Pro, 2008, 28(6期): 359-362.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2008/V28/I6期/359

[1]Xie D M,Hu J M,Tong S P,et al.Progress in Zn-rich paint[J].J.Chin.Soc.Corros.Prot.,2004,24(5):314-320(谢德明,胡吉明,童少平等.富锌漆研究进展[J].中国腐蚀与防护学报,2004,24(5):314-320)
[2]Xi S J.Evaluation of Zn-rich primer[J].Chin.Paint,2002,(2):23-25(席时俊.富锌底漆评价[J].中国涂料,2000,(2):23-25)
[3]Du C S.Precautions for construction of waterborne inorganic zinc-rich paint[J].Paint Coat.Ind.,2003,33(6):30-31(杜存山.水性无机富锌涂料施工时注意事项[J].涂料工业,2003,33(6):30-31)
[4]Liu H W,Shao G H,Tu D R.Waterborne inorganic zinc-rich primer[J].Fine Spec.Chem.,2002,(2):10-11(刘红伟,邵国环,屠德容.水性无机富锌底漆[J].精细与专用化学品,2002,(2):10-11)
[5]Xie D M,Wang J M,Hu J M,et al.Electrochemical behavior of organic and inorganic zinc-rich coatings in3.5%NaCl solution[J].Trans.Nonferrous.Met.Soc.Chin.,2003,13(2):421-425
[6]Xie D M,Tong S P,Feng H,et al.Influence of the pigment shape on the electrochemical behaviors of zinc-rich paint coatings in3.5%NaCl solution[J].Acta Metall.Sin.,2005,41(7):769-774(谢德明,童少平,冯海等.锌粒形态对富Zn涂层在3.5%NaCl溶液中的电化学行为的影响[J].金属学报,2005,41(7):769-774)
[7]Xie D M,Wang J M,Hu J M,et al.Influence of surface rough-ness on performance of zinc-rich paint coatings[J].Trans.Non-ferrous.Met.Soc.Chin.,2002,12(6):1036-1039
[8]Lin B,Li Y,Wang F H.Study on the effect of zinc pigment size on the electrochemical behavior of organic zinc-rich coatings[J].J.Chin.Soc.Corros.Prot.,2003,23(6):350-354(刘斌,李瑛,王福会.锌粉颜料尺寸对有机富锌涂层电化学行为的影响[J].中国腐蚀与防护学报,2003,23(6):350-354)
[9]He D L,Wang S P,Xu Y B,et al.A SEM/EDS study on the wa-terborne silicate zinc-rich coatings[J].J.Hunan Univ.,(Nat.Sci.)2007,(9):53-56(何德良,王石青,徐以斌等.水性硅酸盐富锌涂层的SEM/EDS研究[J].湖南大学学报(自然科学版),2007,(9):53-56)
[10]John B Schutt,Silver Spring Md.Potassium silicate coatings[P].U.S Pat.,3620784,1971
[11]John B Schutt,Silver Spring Md.Alkali-metal silicate binders and methods of manufacture[P].U.S Pat.,4162169,1979

[1]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[2]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[3]	达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[4]	达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[5]	邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[6]	邓三喜, 闫小宇, 柴柯, 吴进怡, 史洪微. 假单胞菌对聚硅氧烷树脂清漆涂层分解及防腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 326-332.
[7]	曹海娇, 魏英华, 赵洪涛, 吕晨曦, 毛耀宗, 李京. Q345钢预热时间对熔结环氧粉末涂层防护性能的影响II：涂层体系失效行为分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.
[8]	张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[9]	梅朦, 郑红艾, 陈惠达, 张鸣, 张大全. 硫酸盐还原菌对Cu在循环冷却水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 533-539.
[10]	孟凡帝, 刘莉, 李瑛, 王福会. 用于原位检测在深海并压力交变环境中有机涂层电化学阻抗的预埋微电极研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 561-566.
[11]	王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO₃溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[12]	王佳, 贾梦洋, 杨朝晖, 韩冰. 腐蚀电化学阻抗谱等效电路解析完备性研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 479-486.
[13]	陈振宁,陈日辉,潘金杰,滕艳娜,雍兴跃. L921A钢在3.5%NaCl溶液中的有机/无机复配缓蚀剂研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 473-478.
[14]	冯立, 张立功, 李思振, 郑大江, 林昌健, 董士刚. 柠檬酸铁浓度对镁合金微弧氧化黑色膜层微观结构及耐蚀性的影响[J]. 中国腐蚀与防护学报, 2017, 37(4): 360-365.
[15]	高洪扬,王巍,许立坤,马力,叶章基,李相波. 改性环氧防腐涂层在模拟深海高压环境的失效行为[J]. 中国腐蚀与防护学报, 2017, 37(3): 247-263.

Viewed

Full text

Abstract

Cited

Shared

Discussed