微量Ce对AZ91镁合金微观组织及耐蚀性的影响

中国腐蚀与防护学报

2008, Vol. 28

Issue (4): 205-209

研究报告

本期目录 | 过刊浏览

微量Ce对AZ91镁合金微观组织及耐蚀性的影响

杨洁;易丹青;邓姝皓;王斌;柳公器

湖南省中南大学主校区材料科学与工程学院

Effect of trace Ce on the microstructure and corrosion resistance of AZ91 alloy

湖南省中南大学主校区材料科学与工程学院

全文: PDF(1667 KB)

摘要: 用X射线衍射(XRD)､扫描电镜(SEM)､能谱分析(EDS)､析氢法､动电位极化及浸泡实验等手段研究了添加微量稀土元素Ce对AZ91镁合金微观组织及耐蚀性的影响,并从热力学角度分析了Ce对提高合金耐蚀性的影响机制｡结果表明,稀土Ce细化了合金的微观组织,使β-Mg17Al12相变得断续､弥散,成分分布更为均匀,生成了Al4Ce相及Mg-Al-Mn-Ce-Fe的金属间化合物;稀土Ce使合金在3.5%NaCl溶液中的自腐蚀电位升高,与Al､O生成了不连续的保护性氧化膜,提高了合金的耐腐蚀性能;添加0.5mass% Ce时合金的耐蚀性最佳｡

关键词 ：镁合金, Ce, 微观组织, 耐蚀性

Abstract：Abstract: The effects of rare earth Ce addition on the microstructures and corrosion resistance of AZ91 alloys were studied by XRD, SEM, EDS, potentiodynamic polarization and immersion test. The mechanics of the corrosion resistance increased with Ce was analyzed from thermodynamics point. The results showed that: the microstructure of the alloys were refined by adding Ce; β-Mg17Al12 phase was broken, dispersed and the elements distributed uniformly; The Al4Ce phase and Mg-Al-Mn-Ce intermetallics were observed by adding Ce; Anodic polarization of the alloys increased and Al-Ce-O oxidation film were obtained because of adding Ce to the AZ91 alloy; When the amount of Ce was 0.5wt% the corrosion resistant of the alloy is the best.

Key words： Magnesium alloy Ce microstructure corrosion resistance

收稿日期: 2006-09-26

ZTFLH:

TG146.2

通讯作者: 杨洁 E-mail: yangjie_001981@yahoo.com.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	杨洁
	易丹青
	邓姝皓
	王斌
	柳公器
44.8K

引用本文:

杨洁; 易丹青; 邓姝皓; 王斌; 柳公器 . 微量Ce对AZ91镁合金微观组织及耐蚀性的影响[J]. 中国腐蚀与防护学报, 2008, 28(4): 205-209 .

链接本文:

https://www.jcscp.org/CN/Y2008/V28/I4/205

[1]Shi C X,Li H D,Wang D Z,et al.A proposal on accelerating devel-opment of metallic magnesium industry in China[J].Mater.Rev.,2001,15(4):526-530(师昌绪,李恒德,王淀佐等.加速我国镁工业发展的建议[J].材料导报,2001,15(4):526-530)
[2]Diem W.Magnesium in different applications[J].Auto Technol.,2001,1:40-41
[3]Kamado S,Koike J,Kondoh K,et al.Magnesium Research Trend in Japan[J].Mater.Sci.Forum,2003,419-422:21-34
[4]Chinese Society for Corrosion and Protection.Handbook of the Cor-rosion of Metals[M].Shanghai:Shanghai Scientific and Technical Publishers,1987(中国腐蚀与防护学会.金属腐蚀手册[M].上海:上海科学技术出版社,1987)
[5]Zhu Z F.The Anticorrosion Properties and Applications of Non-ferrous Metals[M].Beijing:Chemical Industry Press,1999,5(朱祖芳.有色金属的耐腐蚀性及其应用[M].化学工业出版社,1999,5)
[6]Li Y,Zhang T,Wang F H.Corrosion behavior of AZ91D magnesiumalloy in hand sweat[J].J.Chin.Soc.Corros.Prot.,2004,24(5):276-279(李瑛,张涛,王福会.AZ91D镁合金汗腐蚀机理研究[J].中国腐蚀与防护学报,2004,24(5):276-279)
[7]Wang X F,Qi G T,Cai Q Z,et al.The effect of rare earth oncorrosion of AZ91 magnesium alloy in NaCl solution[J].Dev.Appl.Mater.,2002,17(5):34-36(王喜峰,齐公台,蔡启舟等.混合稀土对AZ91镁合金在NaCl溶液中的腐蚀行为影响[J].材料开发与应用,2002,17(5):34-36)
[8]Duan H Q,Wang L S,Cai Q Z,et al.Effects of rare earth(RE)on corrosive resistance of AZ91 magnesium alloy[J].Chin.Mech.Eng.,2003,14(20):1789-1793(段汉桥,王立世,蔡启舟等.稀土对AZ91镁合金耐腐蚀性能的影响[J].中国机械工程,2003,14(20):1789-1793)
[9]Xu Y,Chen X.Preparation and corrosion resistance of rare earthconversion coatings on AZ91 magnesium alloy[J].J.Chin.RareEarth Soc.,2005,23(1):40-43(许越,陈湘.AZ91镁合金表面稀土转化膜的制备及耐蚀性能研究[J].中国稀土学报,2005,23(1):40-43)
[10]Zhang Y,Xu Y.Effect of Ce on corrosion resistance of AZ91magnesium alloy[J].J.Harbin Inst.Technol.,2002,34(3):376-378(张勇,许越.稀土铈对AZ91镁合金表面腐蚀性能的影响[J].哈尔滨工业大学学报,2002,34(3):376-378)
[11]Xu P,Liu S F.Influence of microstructure on the corrosion ofAZ91 Mg-alloy[J].Chin.Foundry Machin.Technol.,2004,4:9-13(徐萍,刘生发.AZ91镁合金显微组织对腐蚀性能的影响[J].中国铸造装备与技术,2004,4:9-13)
[12]Sun Y,Hu J.Corrosion and Corrosion Control of Metals[M].Harbin Institute of Technology Press,2003(孙跃,胡津.金属腐蚀与控制[M].哈尔滨工业大学出版社,2003)
[13]Lunder O,Nisancioglu K,Steen Hansen R.Corrosion of die Cast Magnesium-Aluminum Alloys.SAE Technical Paper No.930755[A].International Congress and Exposition[C].Detroit,March1-5,1993
[14]Huang J Z,Zuo Y.The Corrosion Resistance and Corrosion Dataof Materials[M].Beijing:Chemical Industry Press,2002(黄建中,左禹.材料的耐蚀性和腐蚀数据[M].北京:化学工业出版社,2002)
[15]Pierre R Roberge,Translated by Wu Y S,Li J Q,Cao B,et al.Handbook of Corrosion Engineering[M].Beijing:China Petro-chemical Press,2004(Pierre R Roberge.吴荫顺,李久青,曹备等译.工程腐蚀手册[M].北京:中国石化出版社,2004)

[1]	黄鹏, 高荣杰, 刘文斌, 尹续保. 盐溶液刻蚀-氟化处理制备X65管线钢镀镍超双疏表面及其耐蚀性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[3]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[4]	包任, 周根树, 李宏伟. 恒电位脉冲电沉积高锡青铜耐蚀镀层工艺研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 585-591.
[5]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[6]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[7]	刘海霞, 黄峰, 袁玮, 胡骞, 刘静. 690 MPa级高强贝氏体钢在模拟乡村大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 416-424.
[8]	李聪玮, 杜双明, 曾志琳, 刘二勇, 王飞虎, 马付良. 电流密度对Ni-Co-B镀层微观结构及磨蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 439-447.
[9]	郏义征, 王保杰, 赵明君, 许道奎. 固溶处理制度对挤压态Mg-Zn-Y-Nd镁合金在模拟体液中腐蚀和析氢行为的影响规律研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 351-357.
[10]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[11]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[12]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[13]	王乐,易丹青,刘会群,蒋龙,冯春. Ru对Ti-6Al-4V合金腐蚀行为的影响及机理研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 25-30.
[14]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[15]	郏义征, 赵明君, 程世婧, 王保杰, 王硕, 盛立远, 许道奎. 模拟人体体液中镁合金的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.

Viewed

Full text

Abstract

Cited

Shared

Discussed