湖北枣阳九连墩战国楚墓青铜器铅锡焊料的腐蚀机理探讨

中国腐蚀与防护学报

2007, Vol. 27

Issue (3): 162-166

研究报告

本期目录 | 过刊浏览

湖北枣阳九连墩战国楚墓青铜器铅锡焊料的腐蚀机理探讨

金普军;秦颖;龚明

中国科学技术大学科技史与科技考古系

Research on Corrosive Mechanism of Lead-Tin Based Alloy Cultural Relics of Warring States in Hubei Province

;;;

中国科学技术大学科技史与科技考古系

全文: PDF(283 KB)

摘要: 用能谱、X射线衍射、X射线荧光光谱和金相等分析手段，研究了九连墩楚墓出土的战国青铜文物的铅锡焊料的基体和锈蚀产物、发现产物致密、均匀，主要由PbCO3、Pb和SnO2组成，整个埋藏环境相对密闭，总体呈中性，HCO3-浓度较高。这些因素共同作用，减缓了铅锡焊料的腐蚀，使用大部分青铜器完好地保存了下来。

关键词 ：金属文物, 土壤腐蚀, 铅锡合金, 铅的腐蚀, 锡的

Abstract：The alloys and corrosion products of the Pb - Sn alloy solders, existing in bronxes excavated from Jiuliandu site during Warring States Period, were analyzed by using techniques of energy spectrum, X- ray powder diffraction, X - ray fluorescence spectrometry and metallurgical analysis , etc. The analysis indicated that corrosive products that were composed of PbCO3, Pb and SnO2 were compact and firm, and the buried circumstance, with the neutral pH and the high content of HCO3-,was relatively isolated, which had cooperated to hinder the corrosion of Pb - Sn solders to keep bronzes in good figure.

Key words： Metallic cultural relics soil corrosion Pb-Sn alloy Pb corrosion Sn corrosion

收稿日期: 2005-12-12

ZTFLH:

TG146.1+2

通讯作者: 金普军 E-mail: jinpj2003@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	金普军
	秦颖
	龚明
44.8K

引用本文:

金普军; 秦颖; 龚明 . 湖北枣阳九连墩战国楚墓青铜器铅锡焊料的腐蚀机理探讨[J]. 中国腐蚀与防护学报, 2007, 27(3): 162-166 .
. Research on Corrosive Mechanism of Lead-Tin Based Alloy Cultural Relics of Warring States in Hubei Province. J Chin Soc Corr Pro, 2007, 27(3): 162-166 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2007/V27/I3/162

[1]Li HX,Li Y D,Zhang S Q,Gao Y.Research on rusts of lead cablesunder soil corrosion[J].Corros.Sci.Prot.Technol.,1992,4(2):117-119(李洪锡,银耀德,张淑泉,高英.铅电缆土壤腐蚀产物研究[J].腐蚀科学与防腐技术,1992,4(2):117-119)
[2]Lu Y K.Surface corrosion kinetics of the solid lead,tin and their al-loy[J].J.University of Science and Technology Beijing,1991,13(5):493-497(鲁永奎.固态铅、锡及其铅锡焊料表面腐蚀动力学[J].北京科技大学学报,1991,13(5):493-497)
[3]K S S,V S S,ME,et al.Water contamination:impact of tin-leadsolder[J].Wat.Res.,1995,29(8):1827-1836
[4]Wang C S,Lu B,Zuo J,et al.Structural and elemental analysis onthe nanocrystalline SnO2in the surface of ancient Chinese black mir-rors[J].Nanostructured Materials,1995,5(4):486-496
[5]S H,K S,J C H.Quantitative determination of cerussite(lead car-bonate)by X-ray powder diffraction and inferences for lead specia-tion and transport in streamsediments froma former lead mining areain Scotland[J].Appl.Geochemistry,2001(16):597-608
[6]Yao W Y,Peng K,Tang MK,et al.Corrosion mechanism of lead in-got[J].J.Cent.South Univ.,(Natural Science)2004,35(1):54-58(姚维义,彭可,唐谟堂等.铅锭白锈形成机理[J].中南大学学报(自然科学版),2004,35(1):54-58)
[7]Xu P D,Zhao X P,Ya Y.Influence of Sn on electrochemical behav-ior of lead alloy electrodes in sulfuric acid[J].Battery Industry,1999,3(5):165-166(徐品弟,赵小佩,夏晔.锡对铅合金电极在硫酸溶液中的电化学行为影响的研究[J].电池工业,1999,3(5):165-166)
[8]Herrera-Urbina R,et al.The effect of Pb(II)species,pH anddissolved carbonate on the zeta potential at the quartz aqueous solu-tion interface[J].Colloids and Surfaces A:Physicochem.Eng.As-pects,1995,(98):25-33
[9]Xia Z D,Mu N,Shi YW.Corrosion behavior of tin-zinc based alloysolder[J].Corros.Sci.Prot.Technol.,2003,23(4):234-238(夏志东,穆南,史耀武.锡锌钎料的腐蚀行为[J].腐蚀科学与防护技术,2003,23(4):234-238)
[10]Lu Y H,Wang Y H,Wang J.Research on corrosive behavior of Pbunder acid soil[J].Modern Lineate Transmission,2002(2):14-17(鹿中晖,王永红,文杰.铅在酸性土壤中的腐蚀行为研究[J].现代有线传输,2002(2):14-17)
[11]S H,MA.Effects of temperature and r.f.power sputtering on elec-trical and optical properties of SnO2[J].Appl.Energy.,2000,(65):19-28
[12]Wang YH,Lu Z H,Li YZ.Research on corrosion behavior of cable'metal materials in soil[J].Modern Cable Transmission,2004,(4):79-83(王永红,鹿中晖,李英志.线缆金属材料在土壤中腐蚀行为研究[J].现代有线传输,2004,(4):79-83)
[13]Wang Y H,Wen J,Lu Y H.Research on accelerated corrosive ex-periment of Pb、Al by anions in the soil[J].Modern Lineate Trans-mission,2000,(2):28-30(王永红,文杰,鹿中晖.土壤中阴离子对铅、铝腐蚀的加速试验研究[J].现代有线传输,2000,(2):28-30)

[1]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[2]	朱亦晨,刘光明,刘欣,裴锋,田旭,师超. 红壤地区接地材料现场埋样与加速腐蚀实验的相关性研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 550-556.
[3]	于利宝, 闫茂成, 王彬彬, 舒韵, 许进, 孙成. 酸性土壤环境中Q235钢的微生物腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 10-17.
[4]	黄涛,陈小平,王向东,米丰毅,刘芮,李向阳. pH值对Q235钢在模拟土壤中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(1): 31-38.
[5]	么惠平, 闫茂成, 杨旭, 孙成. X80管线钢红壤腐蚀初期电化学行为[J]. 中国腐蚀与防护学报, 2014, 34(5): 472-476.
[6]	聂向晖, 李晓刚,李云龙,李记科, 张鸿博. 土壤腐蚀加速试验的加速比与动力学相关性研究[J]. 中国腐蚀与防护学报, 2011, 31(3): 208-213.
[7]	黄家怿邱于兵郭兴蓬. 采用聚类分析研究X70钢在库尔勒土壤中初期电化学噪声特征[J]. 中国腐蚀与防护学报, 2009, 29(6): 453-458.
[8]	王永红; 章钢娅; 鹿中晖; 李英志; 孙慧珍 . 铅、铝、铜土壤腐蚀随季节变化规律研究[J]. 中国腐蚀与防护学报, 2007, 27(6): 326-328 .
[9]	许述剑; 翁永基; 李相怡 . 图像分维对腐蚀坑分布特征的表征[J]. 中国腐蚀与防护学报, 2007, 27(2): 109-113 .
[10]	王荣; 介燕妮 . 陕京管线典型土壤环境的腐蚀性研究[J]. 中国腐蚀与防护学报, 2006, 26(4): 211-215 .
[11]	王永红; 鹿中晖; 李英志 . 西部内陆盐土中铜、铝的腐蚀行为[J]. 中国腐蚀与防护学报, 2005, 25(5): 303-306 .
[12]	翁永基; 李相怡 . 土壤中碳钢平均腐蚀速度统计特征的分形研究[J]. 中国腐蚀与防护学报, 2005, 25(4): 200-204 .
[13]	武俊伟; 李晓刚; 杜翠薇; 汪崧; 宋义全 . X70钢在库尔勒土壤中短期腐蚀行为研究[J]. 中国腐蚀与防护学报, 2005, 25(1): 15-19 .
[14]	孙成; 韩恩厚; 李洪锡 . 原位测试研究土壤环境因素对碳钢的腐蚀影响[J]. 中国腐蚀与防护学报, 2002, 22(4): 207-210 .
[15]	李谋成; 林海潮; 郑立群 . 土壤腐蚀性检测器的研制[J]. 中国腐蚀与防护学报, 2000, 20(3): 161-166 .

Viewed

Full text

Abstract

Cited

Shared

Discussed