LC4 铝合金在模拟污染大气环境中的腐蚀行为

王振尧;马腾;韩薇;于国才

中科院金属所

Corrosion behaviors of Al alloy LC4 in simulated polluted atmospheric environments

Zhenyao Wang;Teng Ma;Wei Han;Guocai Yu

中科院金属所

全文: PDF(208 KB)

摘要: 通过干湿周浸循环加速腐蚀试验，用NaHSO3和NaCl分别模拟对大气腐蚀有明显影响的两种大气污染组分SO2和Cl-。利用失重分析、表面形貌观察和腐蚀产物分析，研究了LC4铝合金在模拟污染大气环境中的腐蚀行为和机理。研究发现，在0.02 mol/L NaHSO3和0.02 mol/L NaHSO3+0.006 mol/L NaCl两种加速腐蚀介质中，不论包铝层存在与否， LC4腐蚀失重均与腐蚀时间有线性关系；Cl- 在HSO3- 存在的情况能够更有效产生点蚀源，破坏LC4表面的氧化膜，加速LC4腐蚀；试样放置的角度对LC4腐蚀有较大的影响。

关键词 ：大气腐蚀, 铝合金, 加速腐蚀试验, 表面分析

Abstract：The corrosion behaviors of typical high-strength aluminum alloy LC4 was studied by accelerated corrosion tests of cyclic wet-dry intermittent immersion designed to simulated industrially polluted atmospheric environment, and corrosion mechanism was also discussed. The main experimental techniques include mass loss, morphological check of samples and analysis of corrosion products in different test time. The result shows that LC4, with or without cladding, has linear relationship of mass loss and test time in two chemical media, 0.02 mol/L NaHSO3 and 0.02 mol/L NaHSO3+0.006 mol/L NaCl respectively. Angle of setting samples was another important factor that can cause corrosion of aluminum alloys. Angle of setting exerts its effect by varying the wetness time of the surface of samples, longer wetness time with less angle of setting and vice versa. A layer of cladding on high-strength aluminum alloys can raise resistance of atmospheric corrosion evidently.

Key words： atmospheric corrosion aluminum alloy accelerated corrosion test surface analysis

收稿日期: 2004-07-22

ZTFLH:

TG172.3

通讯作者: 王振尧 E-mail: zhywang@imr.ac.cn

Corresponding author: Zhenyao Wang E-mail: zhywang@imr.ac.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	王振尧
	马腾
	韩薇
	于国才
44.8K

引用本文:

王振尧; 马腾; 韩薇; 于国才 . LC4 铝合金在模拟污染大气环境中的腐蚀行为[J]. 中国腐蚀与防护学报, 2005, 25(6): 321-326 .
Zhenyao Wang, Teng Ma, Wei Han, Guocai Yu. Corrosion behaviors of Al alloy LC4 in simulated polluted atmospheric environments. J Chin Soc Corr Pro, 2005, 25(6): 321-326 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I6/321

[1]Leygraf C,Graedel T.Atmospheric Corrosion[M].NewYork:JohnWiley and Sons,2000,251-260
[2]Mendoza A R,Corvo F.Outdoor and indoor atmospheric corrosionof non-ferrous metals[J].Corros.Sci.,2000,42(7):1123-1147
[3]Wood W G.Aluminum Cleaning and Finishing,Metal Handbook(V5)[M].9.Metals Park:American Society for Metals,1982,582-585
[4]Ferrer K S,Kelly R G.Comparison of methods of removal of corro-sion products from AA2024-T3[J].Corrosion,2001,57(2):110-117
[5]Neufeld A K,Cole I S.Using fourier transform infrared analysis todetect corrosion products on the surface of metals exposed to atmo-spheric conditions[J].Corrosion,1997,53(10):788-799
[6]Wang J.The influences of alloy elements on anti-atmospheric cor-rosion of steels and corrosion evaluation by identifying colors of cor-rosion products[D].Master Dissertation.Shenyang:Institute ofMetal Research,2002
[7]Graedel T E.Corrosion mechanisms for aluminum exposed to the at-mosphere[J].J.Electrochem.Soc.,1989,136(4):204-212

[1]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[2]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[3]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[4]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[5]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[6]	范益,陈林恒,蔡佳兴,代芹芹,马宏驰,程学群. 热轧AH36船板钢在室内仓储条件下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[7]	潘成成,马超,夏大海. EBSD技术研究金属材料晶体取向对大气腐蚀萌生的影响机理[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[8]	赵晋斌,赵起越,陈林恒,黄运华,程学群,李晓刚. 不同表面处理方式对300M钢在青岛海洋大气环境下腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 504-510.
[9]	邓俊豪,胡杰珍,邓培昌,王贵,吴敬权,王坤. 氧化皮对SPHC热轧钢板在热带海洋大气环境中初期腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 331-337.
[10]	任建平,宋仁国. 双级时效对7050铝合金力学性能及氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 359-366.
[11]	孙永伟,钟玉平,王灵水,范芳雄,陈亚涛. 低合金高强度钢的耐模拟工业大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 274-280.
[12]	夏俊捷,牛红志,刘敏,曹华珍,郑国渠,伍廉奎. 基于卤素效应的阳极氧化技术提高Ti48Al5Nb合金抗高温氧化性能[J]. 中国腐蚀与防护学报, 2019, 39(2): 96-105.
[13]	陈高红,胡远森,于美,刘建华,李国爱. 硫酸阳极化对2E12铝合金力学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 579-586.
[14]	王力, 郭春云, 肖葵, 吐尔逊·斯拉依丁, 董超芳, 李晓刚. Q235和Q450钢在吐鲁番干热大气环境中长周期暴晒时的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[15]	曹敏, 刘莉, 余钟芬, 李瑛, 王福会. 2A02铝合金在模拟海洋大气环境中的剥蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 502-510.

Viewed

Full text

Abstract

Cited

Shared

Discussed