喷气燃料银片腐蚀抑制剂的研究

中国腐蚀与防护学报

2004, Vol. 24

Issue (6): 376-378

研究报告

本期目录 | 过刊浏览

喷气燃料银片腐蚀抑制剂的研究

刘琳;钱建华

Research on the Inhibitor of the Silver Strip Corrosion in Jet Fuel

;

全文: PDF(94 KB)

摘要: 用X-射线光电子能谱仪（XPS）分析了腐蚀银片表面的腐蚀产物。结果表明：活性硫化物是造成喷气燃料银片腐蚀不合格的主要原因。考查了添加剂的抗腐蚀性能和热稳定性以及添加剂对喷气燃料热氧化安定性、磨擦学性能和水分离指数的影响。同时对添加剂的抗腐蚀作用机理进行了研究，DMTD衍生物添加剂在油相中可捕集活性硫，生成非腐蚀性硫化物，抑制银片腐蚀。

关键词 ：喷气燃料, 银片腐蚀, 抑制剂, XPS

Abstract：The corrosion product on the surface of silver was analyzed by means of XPS. The results indicated that the unqualification of silver strip corrosion of jet fuel was caused by the active sulfides. The anticorrosion property and thermal stability of inhibitor have been investigated, the influence of the inhibitor on thermal oxidation stability of jet fuels, wear performance and water separation characteristics was investigated. The anti-corrosion mechanism for the inhibitor was studied, the reaction of DMTD derivative with the active sulfides in oil phase produce non active sulfides, thus, the silver strip corrosion was inhibited.

Key words： jet fuel silver strip corrosion inhibitor XPS

收稿日期: 2003-12-04

ZTFLH:

TQ522.63

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	刘琳
	钱建华
44.8K

引用本文:

刘琳; 钱建华 . 喷气燃料银片腐蚀抑制剂的研究[J]. 中国腐蚀与防护学报, 2004, 24(6): 376-378 .
. Research on the Inhibitor of the Silver Strip Corrosion in Jet Fuel. J Chin Soc Corr Pro, 2004, 24(6): 376-378 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I6/376

[1]LiuL ,ZhaiYC ,QianJH .Studyonthemethodofsilverstripfastcorrosionforjetfuel[J].PetroleumProcessingandPetrochemicals,2001,32(5):49-51(刘琳,翟玉春,钱建华.喷气燃料银片腐蚀快速实验法的研究[J].石油炼制与化工,2001,32(5):49-51)
[2]RichardA ,WhittierC ,PeterT .Anti-oxidationandcorrosionin hibitorsforboron-containinglubricants[P].US 427560,1984-05-24
[3]AndreP .Distillatefuelcompositioncontainingcombinationofsilvercorrosioninhibitors[P].US 5653787,1997-08-05
[4]NoyesLA ,JoanCA .Additivesforfuelsandlubricants[P].US5569407,1996-11-26
[5]ZhangDQ ,GaoLX ,WangZE .Studyofinhibitioneffectsof2-n-undecylimidazoleoncopperin3%NaClsolution[J].J.Chin.Soc.Corros.Prot.,2002,22(4):237-240(张大全,高立新,汪知恩.NaCl溶液中烷基咪唑对铜的缓蚀作用研究[J].中国腐蚀与防学报,2002,22(4):237-240)
[6]PopeJM ,SatoT .Spectroscopicidentificationof2,5-dimercapto-1,3,4-thiadiazoleanditslithiumsaltanddimerforms[J].J .PowerSources,1997,68(2):739-742

[1]	张晨, 陆原, 赵景茂. CO₂/H₂S腐蚀体系中咪唑啉季铵盐与3种阳离子表面活性剂间的缓蚀协同效应[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[2]	王乐,易丹青,刘会群,蒋龙,冯春. Ru对Ti-6Al-4V合金腐蚀行为的影响及机理研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 25-30.
[3]	李兆登,崔振东,侯相钰,高丽丽,王维珍,尹建华. 核级316LN不锈钢焊接接头在高温高压水中的腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 106-113.
[4]	刘东,向红亮,刘春育. 含Ag抗菌双相不锈钢表面腐蚀产物的XPS分析[J]. 中国腐蚀与防护学报, 2018, 38(6): 533-542.
[5]	王彦亮,陈旭,王际东,宋博,范东升,何川. 316L不锈钢在不同pH值硼酸溶液中的电化学行为研究[J]. 中国腐蚀与防护学报, 2017, 37(2): 162-167.
[6]	郝永胜,Luqman Abdullahi SANI,宋立新,徐国宝,葛铁军,方庆红. 中性和酸性溶液中Q235碳钢表面沉积植酸转化膜的耐蚀行为研究[J]. 中国腐蚀与防护学报, 2016, 36(6): 549-558.
[7]	吕文静,张颖君,师超,邵亚薇,王艳秋,孟国哲. 水溶性掺杂聚苯胺的制备及其性能研究[J]. 中国腐蚀与防护学报, 2015, 35(6): 519-524.
[8]	蒋穹,缪强,丁祥,魏小昕. 片状Al-Zn-Si合金粉的析氢行为与抑制剂研究[J]. 中国腐蚀与防护学报, 2013, 33(1): 61-69.
[9]	李红; 张波; 王俭秋; 韩恩厚; 柯伟 . 合金元素Sb和Mn对Zn腐蚀的影响[J]. 中国腐蚀与防护学报, 2008, 28(5): 257-264 .
[10]	李党国; 周根树; 林冠发; 郑茂盛 . 新型铅钙板栅合金阳极腐蚀膜的性能研究[J]. 中国腐蚀与防护学报, 2005, 25(6): 340-343 .
[11]	朱小明 . 用XPS分析喷丸处理后800合金在强碱溶液中的腐蚀产物[J]. 中国腐蚀与防护学报, 2004, 24(4): 213-217 .
[12]	王周成; 张瀛洲; 周绍民 . 离子选择性涂层下碳钢表面腐蚀产物的XPS分析[J]. 中国腐蚀与防护学报, 2001, 21(5): 273-279 .
[13]	胡融刚; 林昌健 . 电化学改性不锈钢钝化膜的XPS/SERS研究[J]. 中国腐蚀与防护学报, 2000, 20(3): 149-154 .
[14]	王为;郭鹤桐;高建平;项民. 20碳钢在三元复合驱溶液中的腐蚀行为[J]. 中国腐蚀与防护学报, 1998, 18(3): 203-208.
[15]	汪鹰;史苑芗;魏宝明;林昌健. 用XPS研究钢筋钝化膜和C1~-对钝化膜的影响[J]. 中国腐蚀与防护学报, 1998, 18(2): 107-112.

Viewed

Full text

Abstract

Cited

Shared

Discussed