304不锈钢在含硼和锂的高温水中的应力腐蚀破裂和断口分析

李红梅;杨武;蔡旬;吕战鹏

上海交通大学材料学院

Fractography of the Stress Corrosion Cracking Specimens of Type 304 Stainless Steel in High Temperature Water Containing Boric Acid and Lithium Ion

Hongmei Li;Wu Yang;Xun Cai;Zhanpeng Lv

全文: PDF(276 KB)

摘要: 采用高温高压慢应变速率拉伸试验方法，考察304奥氏体不锈钢在含B和Li离子的介质中的应力腐蚀敏感性。结果显示，材料的处理方式、介质中含Cl及试验温度均影响该钢种的应力腐蚀破裂敏感性，并在断口形貌中得以反映。

关键词 ： 304不锈钢, 应力腐蚀破裂, 断口形貌

Abstract：Stress corrosion cracking (SCC) of 304 stainless steel in high temperature water media containing H3BO3 and Li+ was studied using slow stain rate test (SSRT). One group samples were annealed (heated at 1050℃ for 60 min. then water quenched) and the other group samples were sensitized (annealed sample then heated at 650℃ for 120 min. and water quenched). Temperature for SSRT is 300℃ or 250℃. Water Media contained 1200mg/L H3BO3, 2mg/L Li+, 2.5 mg/L or 5mg/L Cl- in order to simulate pressurized water reactor condition. The results proved that sensitized material, chloride concentration in the water and higher test temperature showed SCC susceptibility more severely for 304 stainless steel. The fractography proved susceptibility clearly.

Key words： 304 stainless steel stress corrosion cracking fractography

收稿日期: 2003-01-12

ZTFLH:

TG111.9

通讯作者: 李红梅

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	李红梅
	杨武
	蔡旬
	吕战鹏
44.8K

引用本文:

李红梅; 杨武; 蔡旬; 吕战鹏 . 304不锈钢在含硼和锂的高温水中的应力腐蚀破裂和断口分析[J]. 中国腐蚀与防护学报, 2004, 24(1): 16-19 .
Hongmei Li, Wu Yang, Xun Cai, Zhanpeng Lv. Fractography of the Stress Corrosion Cracking Specimens of Type 304 Stainless Steel in High Temperature Water Containing Boric Acid and Lithium Ion. J Chin Soc Corr Pro, 2004, 24(1): 16-19 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I1/16

[1]YangWu,ZhangMeijie,ZhaoGuozhen,CongletonJohn.AcomparisonofU -bendandslowstrainrateproceduresforassessingtheSCCresistanceoftype304stainlesssteelinhigh-temperaturewater[J].Corrosion,1991,47(4):226-233
[2]YangWu,ZhaoGuozhen,ZhangMeijie,CongletonJohn.AnAESinvesti gationofthesurfacefilmsformedonstresscorrosiontestspecimensoftype304stainlesssteelinhightemperaturewater[J].Corros.Sci.,1992,33(1):89-102
[3]RutherWE ,SoppetWK ,KassnerTF .EffectoftemperatureandionicimpuritiesatverylowconcentrationsonstresscorrosioncrackingofAISI304stainlesssteel[J].Corrosion,1988,44(11):791-799
[4]MacDonaldDD ,SongH ,YoshidaK .Corrosionpotentialmeasurementsontype304SSandalloy182insimulatedBWRenvironments[J].Corro sion,1993,49(1):8-16
[5]CongletonJ ,BerrisfordRA ,YangWu.Stresscorrosioncrackingofsensi tizedtype304stainlesssteelindopedhigh-temperaturewater[J].Cor rosion,1995,51(12):901-910
[6]CuiYuexian,WangChangli.AnalysisofMetalFractureSection[M].Harbin:HarbinIndustryUniversityPublishingCompany,1998(崔约贤,王长利.金属断口分析[M].哈尔滨:哈尔滨工业大学出版社,1998)
[7]HenryG ,HorstmanD .MacroscopeandMicroscopeFractography[M].Beijing:MechanicalIndustryPublishingCompany,1990(G .亨利,D .豪斯特曼.宏观断口及显微断口学[M].北京:机械工业出版社,1990)
[8]ZuoJingyi.StressCorrosionCrack[M].Xi′an:Xi′anJiaotongUniversityPublishingCompany,1985(左景伊.应力腐蚀破裂[M].西安:西安交通大学出版社,1985)
[9]ChuWuyang,QiaoLijie,Chenqizhi.FractureandEnvironmentalFrac ture[M].Beijing:SciencePress,2000(褚武杨,乔利杰,陈奇志等.断裂与环境断裂[M].北京:科学出版社,2000)

[1]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[2]	骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[3]	彭文山,侯健,丁康康,郭为民,邱日,许立坤. 深海环境中304不锈钢腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 145-151.
[4]	廖彤,马峥,李蕾蕾,马秀敏,王秀通,侯保荣. Fe₂O₃/TiO₂纳米复合材料对304不锈钢的光生阴极保护性能[J]. 中国腐蚀与防护学报, 2019, 39(1): 36-42.
[5]	刘辉,邱玮,冷滨,俞国军. 304和316H不锈钢在LiF-NaF-KF熔盐中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 51-58.
[6]	张思齐,杜楠,王梅丰,王帅星,赵晴. 阴极面积对3.5%NaCl溶液中304不锈钢稳态点蚀生长速率的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 551-557.
[7]	艾莹珺,杜楠,赵晴,黄世新,王力强,文庆杰. 温度对304不锈钢亚稳蚀孔萌生和稳态蚀孔几何特征的影响[J]. 中国腐蚀与防护学报, 2017, 37(2): 135-141.
[8]	沈杰,刘卫,王铁钢,潘太军. 304不锈钢双极板表面TiN涂层的腐蚀和导电行为研究[J]. 中国腐蚀与防护学报, 2017, 37(1): 63-68.
[9]	王永利,马利,熊良银,刘实. 夹杂对自来水环境下304不锈钢腐蚀及金属离子溶出的影响[J]. 中国腐蚀与防护学报, 2016, 36(4): 328-334.
[10]	方玉荣,付朝阳. 酸性FeCl₃溶液中304不锈钢的超声腐蚀和缓蚀行为[J]. 中国腐蚀与防护学报, 2015, 35(4): 305-310.
[11]	叶超, 杜楠, 田文明, 赵晴, 朱丽. pH值对304不锈钢在3.5%NaCl溶液中点蚀过程的影响[J]. 中国腐蚀与防护学报, 2015, 35(1): 38-42.
[12]	许洪梅, 柳伟, 曹立新, 苏革, 高荣杰. 304不锈钢表面ZnO/TiO₂复合薄膜的制备与光生阴极防腐蚀性能研究[J]. 中国腐蚀与防护学报, 2014, 34(6): 507-514.
[13]	田文明，杜楠，赵晴. 电子散斑干涉技术测量304不锈钢点蚀电位的方法研究[J]. 中国腐蚀与防护学报, 2012, 32(5): 431-436.
[14]	李季,赵林,李博文,郑丽群,韩恩厚. 304不锈钢点蚀的电化学噪声特征[J]. 中国腐蚀与防护学报, 2012, 32(3): 235-240.
[15]	王洪芬,王志奇,洪海霞,陈守刚,尹衍升. 铈掺杂TiO₂薄膜抗海水中硫酸盐还原菌的腐蚀性能研究[J]. 中国腐蚀与防护学报, 2010, 30(6): 481-486.

Viewed

Full text

Abstract

Cited

Shared

Discussed