两相Ag-Y合金在高-低氧压下的高温氧化

牛炎;宋尽霞

沈阳中科院金属研究所

OXIDATION OF Ag-8Y DUAL-PHASE ALLOY in 105 and 10-15 Pa OXYGEN at 700℃

;

沈阳中科院金属研究所

全文: PDF(203 KB)

摘要: 研究了含8 mass%Y的Ag-Y合金在105 Pa和10-15 Pa两个氧压于700℃的氧化.结果表明，在105 Pa的氧化很快，并遵循近似的抛物线规律；10-15 Pa的氧化则很慢且偏离抛物线规律.在高氧压仅发生Y的原位内氧化，这主要是氧快速向内渗透而没有Y明显地向外扩散所致；在低氧压则生成含Ag颗粒的Y2O3外氧化层，而其Y的内氧化层则远较高氧压者薄.内氧化Y2O3颗粒沿深度而变化，近表面处小并呈圆球状，随深度增加逐渐变大并拉长；在深处呈针状且垂直合金表面.此外，在两种氧压下合金最表面有Ag层或分散的Ag 颗粒生成.

关键词 ：两相合金, 氧化, Ag-8Y

Abstract：The oxidation of a silver-based alloy Ag-8Y was studied in 105 Pa and 10-1 5 Pa oxygen at 700℃.The oxidation rate under high P(O2) is very fast and f ollows approximately parabolic rate law,however under low P(O2) is much sl ower and quite irregular with large deviations from parabolic behavior.Under hig h P(O2) the alloy experiences only an internal oxidation of Y without any significant outward Y diffusion,as a result of a fast oxygen penetration.Under l ow P(O2)the alloy forms an almost continuous Y2O3 layer containing Ag particles,plus an internal oxidation zone of Y much thinner than under high P (O2).In both cases pure Ag metal appears on the top surface as a continuous layer for high P(O2) and as separate particles for low P(O2).The int ernal Y2O3 particles in the matrix change shape with depth,being small and g lobular close to the alloy surface but larger and acicular,elongated nearly perp endicularly to the alloy surface,at larger depths.

Key words： dual-phase alloys oxidation Ag-8Y

收稿日期: 2000-04-17

ZTFLH:

TG172.82

通讯作者: 牛炎

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	牛炎
	宋尽霞
44.8K

引用本文:

牛炎; 宋尽霞 . 两相Ag-Y合金在高-低氧压下的高温氧化[J]. 中国腐蚀与防护学报, 2001, 21(4): 200-205 .
. OXIDATION OF Ag-8Y DUAL-PHASE ALLOY in 105 and 10-15 Pa OXYGEN at 700℃. J Chin Soc Corr Pro, 2001, 21(4): 200-205 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2001/V21/I4/200

[1]LangL .Ed.TheRoleofActiveElementsintheOxidationBehaviorofHighTemperatureMetalsandAlloys[M].London:El sevierAppliedScience,1989
[2]MassalskiT .BinaryAlloysPhaseDiagrams[M ],Warrendale:ASM ,USA ,1990
[3]GesmundoF ,VianiF ,NiuY .Theinternaloxidationoftwo- phasebinaryalloysunderlowoxidantpressures[J].Oxid.Met.,1996,45:51
[4]GesmundoF ,VianiF ,NiuY .Theinternaloxidationoftwo-phasebinaryalloysbeneathanexternalscaleofthelessstableox ide[J].Oxid.Met.,1997,47:355
[5]KofstadP .HighTemperatureCorrosion[M ].London:ElsevierAppliedScience,1988
[6]VerfurthJE ,RappRA .Thesolubilityanddiffusivityofoxygeninsilverandcopperfrominternaloxidationmeasurements[J].Trans.Met.Soc.AIME ,1964,230:1310
[7]GaskellDR .IntroductiontotheThermodynamicsofMaterials[M ].Washington:Taylor&Francis,1995
[8]WuWT ,YanRY ,NiuY ,GesmundoF .TheoxidationofaCo-15wt%Yalloyunderlowoxygenpressuresat600～800℃[J].Corros.Sci.,1997,39:1831
[9]NiuY ,YanRY ,FuGY ,WuWT ,GesmundoF .TheoxidationoftwoFe-Yalloysunderlowoxygenpressuresat600～800℃[J].Oxid.Met.,1998,49:91
[10]FuGY ,NiuY ,WuWT ,GesmundoF .TheoxidationofaCo-15wt%Cealloyunderlowoxygenpressuresat600～800℃[J].Corros.Sci.,1998,40:1215
[11]NiuY ,LiYS ,GesmundoF ,VianiF .TheoxidationofaCo-15wt% yttriumalloyin1atmO2 at600～800℃[J].Inter metallics,2000,8:293
[12]NiuY ,GesmundoF ,VianiF ,WuWT .Theairoxidationoftwo-phaseCu-Agalloysat650～750℃[J].Oxid.Met.,1997,47:21
[13]DouglassDL .Oxid.Met.,1995,44:81
[14]BohmG ,KahlweitM .UberdieInnereoxydationvonmetallegierungen[J].ActaMet.,1964,12:641
[15]GuruswamyS ,ParkSM ,HirthJP ,RappRA .InternaloxidationofAg-Inalloys:stressreliefandtheinfluenceofimposedstrain[J].Oxid.Met.,1986,26:77

[1]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[2]	刘晓, 王海, 朱忠亮, 李瑞涛, 陈震宇, 方旭东, 徐芳泓, 张乃强. 电站用奥氏体耐热钢HR3C与Sanicro25在超临界水中的氧化特性[J]. 中国腐蚀与防护学报, 2020, 40(6): 529-538.
[3]	谢冬柏, 洪昊, 王文, 彭晓, 多树旺. 模拟燃烧环境介质和温度对不锈钢表面氧化物形态的影响研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 358-366.
[4]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[5]	王廷勇, 董如意, 许实, 王辉. 石墨烯改性Ti/IrTaSnSb-G金属氧化物阳极在低温和低盐NaCl溶液中的电化学性能[J]. 中国腐蚀与防护学报, 2020, 40(3): 289-294.
[6]	方旭东, 刘晓, 徐芳泓, 李瑞涛, 朱忠亮, 张乃强. 超超临界电站国产奥氏体钢C-HRA-5在超临界水中的氧化特性[J]. 中国腐蚀与防护学报, 2020, 40(3): 266-272.
[7]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[8]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[9]	郑艳欣, 刘颖, 宋青松, 郑峰, 贾玉川, 韩培德. 含铁铜基陶瓷复合材料高温氧化行为与耐磨性研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 191-198.
[10]	范益,陈林恒,蔡佳兴,代芹芹,马宏驰,程学群. 热轧AH36船板钢在室内仓储条件下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[11]	徐勋虎,何翠群,向军淮,王玲,张洪华,郑晓冬. Co-20Re-25Cr-1Si合金在0.1 MPa纯O₂中的高温氧化行为[J]. 中国腐蚀与防护学报, 2020, 40(1): 75-80.
[12]	姜冬雪,付颖,张峻巍,张伟,辛丽,朱圣龙,王福会. 钛合金表面Al₂O₃陶瓷膜制备及性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.
[13]	王毅,张盾. 铋系可见光催化海洋防污材料研究进展[J]. 中国腐蚀与防护学报, 2019, 39(5): 375-386.
[14]	魏欣欣,张波,马秀良. FeCr₁₅Ni₁₅单晶600 ℃下热生长氧化膜的TEM观察[J]. 中国腐蚀与防护学报, 2019, 39(5): 417-422.
[15]	肖金涛,陈妍,邢明秀,鞠鹏飞,孟引根,王芳. 工艺参数对2195铝锂合金阳极氧化膜的耐蚀性影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 431-438.

Viewed

Full text

Abstract

Cited

Shared

Discussed