氢对纯铁钝化膜电子性质的影响

曾一民;乔利杰;杨迈之;褚武扬

北京科技大学材料物理系

Effect of Hydrogen on Electronic Properties of Passive Film on Pure Iron

;;;

北京科技大学材料物理系

全文: PDF(205 KB)

摘要: 采用电化学、光电化学和交流阻抗等方法研究了氢对纯铁钝化膜形成过程和电子性质的影响。结果表明氢的存在会延长钝化膜的形成，增加稳态钝化条件下的溶解速率；氢能提高钝化膜光电流、降低禁带宽度；氢促使钝化膜的电容和掺杂浓度升高，并降低膜的平带电位。

关键词 ：纯铁, 钝化, 光电化学, 交流阻抗

Abstract：Pure iron membranes were pre-charged with hydrogen at various current densities.Effect of hydrogen on the film formation process on iron was studied by electrochemical methods. It showed that charged hydrogen delays the film formation and enhances the dissolution rate at passive state. After hydrogen injection and film formation at different passivation potentials, the AC impedance of the passive film has been measured. The results revealed that the capacitance and adulterated concentration of the film is increased, but the flat band potential is decreased by intrinsic hydrogen. Photoelectrochemical test indicated that hydrogen does not change the semiconductor types of the film, but enhances the photocurrent and reduces forbidden band gap. The results are discussed in relation to semiconductor model, and it was found that hydrogen influences the electronic properties mainly through changing the composition of passive film.

Key words： pure iron sulfuric acid photoelectric chemistry impendance

收稿日期: 1999-04-26

ZTFLH:

TG174.5

通讯作者: 曾一民

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	曾一民
	乔利杰
	杨迈之
	褚武扬
44.8K

引用本文:

曾一民; 乔利杰; 杨迈之; 褚武扬 . 氢对纯铁钝化膜电子性质的影响[J]. 中国腐蚀与防护学报, 2000, 20(2): 74-80 .
. Effect of Hydrogen on Electronic Properties of Passive Film on Pure Iron. J Chin Soc Corr Pro, 2000, 20(2): 74-80 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2000/V20/I2/74

[1 ]褚武扬 ,氢损伤与滞后断裂 [M].北京 :冶金工业出版社 ,1 988
[2 ]HaseawaM .OsawaM .Anomalouscorrosionofaustenticstainlesssteelexposedathightemperatureandpressure[J] Cor rosion ,1 980 ,36 :6 7.
[3]乔利杰 ,缪辉俊 ,褚武扬氢、应力和腐蚀三者对奥氏体不锈钢的协同作用 [J] 中国科学 ,A ,1 996 ,1 2 :1 2 1 8
[4 ]胡小丽 ,黄震中 ,乔利杰 ,褚武扬氢和应力对阳极溶解的影响 [J] 中国腐蚀与防护学报 ,1 996 ,1 6 :1 87
[5 ]ChuWY ,LiuTW ,HsiaoCM MechanismofSCCofsteelinH2 S [J] Corrosion ,1 981 ,1 6 :32 0
[6 ]乔利杰 ,徐荣杰 ,褚武扬 ,肖纪美氢对黄铜应力腐蚀开裂敏感性的影响 [J] 中国腐蚀与防护学报 ,1 995 ,1 5 :6 1
[7]MurphyOJ ,BockrisJO SIMSevidenceconcerningwaterinpassivelayer[J] JElectrochemSoc ,1 982 ,1 2 9:2 1 49
[8]BonifaceAO ,WelwilleBN Kineticsofformationofpassiveoxidefilmsoncorrosion resistantFe Crthinfilms[J] JElectrochemSoc ,1 984,1 31 :2 34 .
[9]MurphyOJ ,PouTE ,BockrisJOM ,TongsonLL ,Investigationoftheanodicallyformedpassivefilmonironbysec ondaryionmassspectroscopy[J] JElectrochemSoc ,1 984,1 31 :2 785 .
[1 0 ]乔利杰 ,曾一民 ,褚武扬氢对 31 0不锈钢点蚀敏感性的影响 [J] 中国腐蚀与防护学报 ,1 998,1 5 :6 1
[1 1 ]FrelicherM ,GoffA ,JovancicevicV .In :FromentM ,ed .Passivityofmetalsandsemiconductors [C] AmsterdamElse vier,1 983.P477.
[1 2 ]TsuruT ,HaruyamaS JJapanInstMet,1 986 ,2 7:382
[1 3]吴浩青电化学动力学 [M] 北京 :高等教育出版社 ,1 998
[1 4]PyunSu Il,LimC ,OrianiRA Theroleofhydrogeninthepittingofpassivatingfilmsonpureiron[J] CorrosSci,1 992 ,33:437
[1 5 ]GerischerH .Modelsforthediscussionofthephoto electrochemicalresponseofoxidelayersonmetals[J] CorrosionScience ,1 989,2 9:2 5 7.
[1 6 ]SchmukiP BohniH Aphoto electrochemicalinvestigationofpassivefilmformedbyalternatingvoltagepassivation[J] JElectrochemSoc ,1 993,1 40 L1 1 9
[1 7]FellerHG ,VhilgHH RelationofelectronconfigurationtopassivityinCr Ni Fealloys[J] JElectrochemSoc ,1 96 0 ,1 0 7:86 4
[1 8]KeddenM ,MahosOS ,TakenoutiH Reactionmodelforirondissolutionstudiedbyelectrodeimpedence[J] JElec trochemSoc ,1 981 ,1 2 8:2 5 7
[1 9]曾一民 ,乔利杰 ,褚武扬氢对 31 0不锈钢钝化膜的影响 [J] 中国腐蚀与防护学报 ,1 999,1 9( 4) :2 33

[1]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[3]	何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[4]	张瑞,李雨,关蕾,王冠,王福雨. 热处理对激光选区熔化Ti6Al4V合金电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 588-594.
[5]	孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.
[6]	严少坤,郑大江,韦江,宋光铃,周廉. 钝性纯Ti在人工海水中的电化学活化行为研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 123-129.
[7]	丰涵,宋志刚,吴晓涵,李惠,郑文杰,朱玉亮. 022Cr25Ni7Mo4N双相不锈钢选择性腐蚀行为与两相组织的关系研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 138-144.
[8]	刘东,向红亮,刘春育. 含Ag抗菌双相不锈钢表面腐蚀产物的XPS分析[J]. 中国腐蚀与防护学报, 2018, 38(6): 533-542.
[9]	刘明,程学群,李晓刚,卢天健. 低合金钢筋在水泥萃取液中钝化膜的耐蚀机理研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 558-564.
[10]	赵小燕, 刘希武, 崔新安, 于凤昌. 304L不锈钢在稀硝酸环境下的腐蚀研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 455-462.
[11]	廖梓含, 宋博, 任泽, 何川, 陈旭. X70钢及其焊缝在Na₂CO₃+NaHCO₃溶液中电化学腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(2): 158-166.
[12]	宋久龙, 陈文革, 雷楠楠. T2铜及QCr0.5铜合金无铬复配钼酸盐钝化研究[J]. 中国腐蚀与防护学报, 2018, 38(2): 210-218.
[13]	李广宇, 雷明凯. γ_Ν相在硼酸溶液中钝化膜的组成及其半导体特性研究[J]. 中国腐蚀与防护学报, 2018, 38(1): 47-53.
[14]	严寒, 赵晴, 杜楠, 胡彦卿, 王力强, 王帅星. 镀锌层三价铬钝化成膜过程及耐蚀性研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 547-553.
[15]	杜开发,王彬,甘复兴,汪的华. 铜锡合金阳极在熔融碳酸盐中氧化膜的形成及其防护性能[J]. 中国腐蚀与防护学报, 2017, 37(5): 421-427.

Viewed

Full text

Abstract

Cited

Shared

Discussed