| HIGH TEMPERATURE OXIDATION BEHAVIOR OF Fe40Al/TiC COMPOSITES |
| ;;;;; |
| 浙江大学材料与化工学院材料系 |
|
Cite this article:
;. HIGH TEMPERATURE OXIDATION BEHAVIOR OF Fe40Al/TiC COMPOSITES. J Chin Soc Corr Pro, 2007, 27(4): 242-246 .
|
|
|
Abstract TiC matrix Fe40Al intermetallic composites were made by spontaneous infiltration. The oxidation ki?鄄netics of Fe40Al/80vol%-88vol%TiC composites were investigated by means of conducting the oxidation experi?鄄ments in air at temperature of 700 ℃ ~ 1100 ℃ for up to 65 hours， and measuring the variations of the weight gains of the composites with the oxidation times. The microstructure evolution of the composites during the oxida?鄄tion processing was studied by using SEM/EDS and XRD. The effect of the surface roughness of the composites on the oxidation behavior was also studied. The results show that， the weight gain data were fitted a power type law with the oxidation time with power coefficients ranging 0.63 ~ 0.75， the oxidation rate decreased with in?鄄creasing the oxidation time. The oxidation layer was mainly composed of dense crystalline TiO2， the crystalline size of TiO2 was effected by the oxidation temperature and the surface roughness of the composites.
|
|
Received: 28 February 2006
|
|
|
[1]Durlu N.Titanium carbide based composites for high temperature application[J].J.Eur.Ceram.Soc.,1999,19:2415-2419
[2]Plucknett K P,Becher P F,Waters S B.Flexure strength of melt-infiltration-processed titanium carbide/nickel aluminide compos-ites[J].J.Am.Ceram.Soc.,1998,81(7):1839-1844
[3]Holleck H.Constitutional aspects in the development of new hard materials[A].In Science of Hard Materials[C].Viswanadham P K,Rowcliff D G,Gurland J,ed.New York:Plenum Press,1981
[4]Farooq T,Davies T J.Tungsten carbides hardmetals cemented with ferroalloys[J].The Int.J.Pow.Metall.,1991,27(4):347-355
[5]Becher P F,Plucknett K P.Properties of Ni3Al-bonded titanium carbide ceramics[J].J.Eur.Ceram.Soc.,1998,18:395-400
[6]Krasnowski M,Witek A,Kulik T.The FeAl-30%TiC nanocom-posite produced by mechanical alloying and hot-pressing consoli-dation[J].Intermetallics,2002,10:371-376
[7]Gao M X,Oliveira F J,Pan Y,et al.Strength improvement and fracture mechanism in Fe40Al/TiC composites with high content of TiC[J].Intermetallics,2005,13:460-466
[8]Gao M X,Pan Y,Oliveira F J,et al.Interpenetrating microstruc-ture and fracture mechanism of NiAl/TiC composites by pressure-less melt infiltration[J].Mater.Letters,2004,58:1761-1765
[9]Gao MX,Pan Y,Oliveira F J,Baptista J L,Vieira J M.High strength TiC matrix Fe28Al toughened composites prepared by spontaneous melt infiltration[J].J.Eur.Ceram.Soc.,2006,3853-3859
[10]Chen G L,Lin J P.Structure Materials of Ordered Intermetallics[M].Beijing:Metallurgical Industry Press,Oct.1999(陈国良,林均品著.有序金属间化合物结构材料[M].北京:冶金工业出版社,1999)
[11]Meng F J,Xu B S,Zhu S,et al.Oxidation behavior of Fe-Al coatings produced by high velocity arc spraying at800℃[J].J.Chin.Soc.Corros.Prot.,2004,24(6):368-371(孟凡军,徐滨士,朱胜等.高速电弧喷涂Fe-Al涂层在800℃下的氧化性能[J].中国腐蚀与防护学报,2004,24(6):368-371)
[12]Li M J,Sun X F,Guan H R,et al.High temperature oxidation behavior of(Ni,Pd)Al coating[J].J.Chin.Soc.Corros.Prot.,2003,23(1):13-16(李猛进,孙晓峰,管恒荣等.(Ni,Pd)Al涂层的高温氧化[J].中国腐蚀与防护学报,2003,23(1):13-16)
[13]Wu P F,Li M C,Shen J N,et al.Photo-electrochemical anticor-rosion effect of anodic TiO2films[J].J.Chin.Soc.Corros.Prot.,2005,25(1):54-57(武朋飞,李谋成,沈嘉年等.阳极氧化二氧化钛薄膜的光电化学防腐蚀特性[J].中国腐蚀与防护学报,2005,25(1):54-57)
[14]Montealegre M A,González-Carrasco J L,Mu(oz-Morris M A.Oxidation behaviour of Fe40Al alloy strip[J].Intermetallics,2001,9(6):487-492 |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|