| A Study on the Selective Dissolution Behavior of Duplex Stainless Steel in Systems Containing Nitric Acid |
| Yan Fu |
| 厦门大学化学系固体表面物理化学国家重点实验室 |
|
|
|
|
Abstract Duplex stainless steel is composed of ferritic and austenitic phases, which have different crystal structure and element component, thus in different solutions, ferrite and austenite demonstrate different dissolutio rate, that is , selective dissolution. In this investigation, the potentiodnamic polarization experiment was carried in nitric acid and hydrochloric acid mixture, and mixture of nitric acid and sodium chloride, nitric acid and ferrite chloride as well. After the experiments, SEM and EDS were used to distinguish and analyze the morphology differencs of the two phases. The results show that in the solutions containing nitric acid, adding hydrochloric acid and sodium chloride will enhance the selective dissolution of two phases, while adding low concentration of ferrite chloride will decrease the corrosion difference between ferrite and austenite, but the phenomena vanish with the increasing of the concentration of ferrite chloride.
|
|
Received: 08 October 2003
|
|
|
|
Corresponding Authors:
Yan Fu
|
[1]FourieJW ,RobinsonFPA .Mechanisticaspectsofselectivecorro sionofa20%Crduplexstainlesssteelinacidchloridemixtures[A].ProceedingofInternationalConferenceonStainlessSteels1991[C].Chiba,ISIJ ,1991,111-117
[2]SridharN ,KoltsJ .Effectsofnitrogenontheselectivedissolutionofaduplexstainlesssteel[J].Corrosion,1987,43:648
[3]SymniotisE .Galvaniceffectsontheactivedissolutionofduplexstainlesssteels[J].Corrosion,1990,46:2
[4]WuJ .Developmentofdomesticandoverseaduplexstainlesssteels[J].CorrosionandProtectionofOilChemicalEngineering,1996,13(1):6(吴玖.国内外双相不锈钢的发展[J].石油化工腐蚀与防护,1996,13(1):6)
[5]QinZR ,LiLS ,LiuDJ .Investigationofnewtypeanti-nitricacidstainlesssteelsforbumpuse[J].DevelopmentandApplicationofMaterials,1995,10(5):8(秦紫瑞,李隆盛,刘德经.耐浓硝酸泵用新型不锈钢的研究[J].材料开发与应用,1995,10(5):8)
[6]WeiGS ,QinZR ,FengXY .Therelationshipbetweentheimpacttoughness.Corrosionresistanceandfracturemodeofcaststainlesssteelusedforconcentratednitricacid[J].JournalofQingdaoUni versity,1998,13(3):56(魏广升,秦紫瑞,冯秀英.耐浓硝酸铸造不锈钢冲击韧性、耐蚀性与断口形貌的关系[J].青岛大学学报,1998,13(3):56)
[7]XiaoGF ,LiuJL ,.Corrosionofnitrophosphateplant&itsanticor rosionmeasures[J].PhosphateandCompoundFertilizer,2001,16(3):37(肖观发,刘金亮.硝酸磷肥装置的腐蚀与防腐蚀措施[J].磷肥与复肥,2001,16(3):37)
[8]FuY ,ShaoMH ,LinCJ.Measurementsofthepotentialdistribu tionofduplexstainlesssteel’smicrostucture[A].TheProceedingof11thConferenceofChineseElectrochemistrySocietyC007[C].Nanjing,2001(付燕,邵敏华,林昌健.双相不锈钢显微组织电位分布的测量[A].第十一次全国电化学会议论文C007[C]南京,2001
[9]TsaiWenta,LinCJ,CaiKM .SelectiveCorrosioninDuplexStain lessSteel,CorrosionandIt’sControl[M ].Beijing:ChemicalIndus tryPress,2002,10(蔡文达,林昌健,蔡坤铭.双相不锈钢中相之优选腐蚀性质研究,腐蚀与控制[M].北京:化学工业出版社,2002,10)
[10]TsaiWenta,CaiKM ,LinCJ ,etal.Selectivedissolutioninduplexstainlesssteel[J].Electrochemistry,2003,9(2):1707 |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|