AIR OXIDATION OF Fe-Y ALLOYS AT 800℃

J Chin Soc Corr Pro

2010, Vol. 30

Issue (6): 453-456 DOI:

Research Articles

Current Issue | Archive | Adv Search

AIR OXIDATION OF Fe-Y ALLOYS AT 800℃

FU Guangyan, YANG Ningning, WANG Yanyan

School of Mechanical Engineering, Shenyang University of Chemical Technology, Shenyang 110142

Download:

PDF(1074KB)
Export: BibTeX | EndNote (RIS)

Abstract The oxidation behavior of Fe-5Y and Fe-10Y alloys was studied at 800℃ in air. The results indicate that the scaling kinetics is not irregular. The oxidation rate of Fe-10Y alloy is higher than Fe-5Y alloy. The scale formed on Fe-10Y alloy is substantially similar to that on Fe-5Y, also with severe internal oxidation. A single Y₂O₃ layer was not formed on the surface of alloy. These results were examined by taking into account the presence of intermetallic compounds in the alloys and the low ability of diffusion of yttrium in iron.

Key words: Fe-Y alloy oxidation oxidation scale high temperature oxidation

Received: 12 October 2009

ZTFLH:

TG 172.82

Corresponding Authors: FU Guangyan E-mail: Fu_guangyan@126.com

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	YANG Ning-Ning

Cite this article:

FU Guangyan, YANG Ningning, WANG Yanyan. AIR OXIDATION OF Fe-Y ALLOYS AT 800℃. J Chin Soc Corr Pro, 2010, 30(6): 453-456.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2010/V30/I6/453

[1] Cueff R, Buscail H, Caudron E, et al.Oxidation of alumina formers at 1173K: effect of yttrium ion implantation and yttrium alloying addition [J]. Corros. Sci.,2003, 45(8): 1815-1831

[2] Yu K, Li W X, Wang R C, et al. Effects of rare earth elements on the corrosion property of AZ31 magnesium alloy [J].Mater. Prot., 2007, 40(11): 6-11

    (余琨, 黎文献, 王日初等. 稀土Ce和Nd对AZ31镁合金耐蚀性能的影响 [J]. 材料保护, 2007, 40(11): 6-11)

[3] Fu G Y, Niu Y. Sulfidation of a Co-15Ce alloy in H₂-H₂S gas mixtures at 800℃ [J]. Corros. Sci. Prot. Technol.,1997, 9(4): 265-269

    (付广艳, 牛焱. Co-15Ce合金在800℃不同硫压下的硫化 [J]. 腐蚀科学与防护技术, 1997, 9(4): 265-269)

[4] Fu G Y, Niu Y. Corrosion of Fe-30Ce alloy in H₂/H₂S mixed gas [J]. Rare. Earths., 1998, 19(4): 20-23

    (付广艳, 牛焱. Fe-30Ce合金在H₂/H₂S混合气体中的腐蚀 [J]. 稀土, 1998, 19(4): 20-23)

[5] Li M S. High Temperature Oxidation of Metals [M]. Beijing: Metallurgical Industry Press. 2001

    (李美栓. 金属的高温氧化 [M]. 北京: 冶金工业出版社, 2001)

[6] Zhai J K. High Temperature Corrosion of Metals [M]. Beijing:Beihang University Press. 1994

    (翟金坤. 金属高温腐蚀 [M]. 北京: 北京航空航天大学出版社, 1994)

[7] Zeng C L,Wang W, Wu W T.Oxidation of Fe-Y alloys at 600~800℃ in air [J]. Corros. Sci.Prot. Technol., 1999，11(5): 257-263

    (曾潮流, 王文, 吴维. Fe-Y合金在600~800℃空气中的氧化行为 [J]. 腐蚀科学与防护技术, 1999, 11(5): 257-263)

[8] Niu Y, Wu W T, Yan R Y. Corrosion of Fe-Y alloys in H₂-CO₂-H₂S gas mixtures at 600~800℃ [J].Corros. Sci. Prot. Technol., 1998, 10(3): 125-134

    (牛焱, 吴维tao, 晏人芸. Fe-Y合金在600$\sim$800℃ H₂-CO₂-H₂S中的腐蚀 [J]. 腐蚀科学与防护技术, 1998, 10(3): 125-134)

[1]	WEI Zheng, MA Baoji, LI Long, LIU Xiaofeng, LI Hui. Effect of Ultrasonic Rolling Pretreatment on Corrosion Resistance of Micro-arc Oxidation Coating of Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[2]	LIU Xiao, WANG Hai, ZHU Zhongliang, LI Ruitao, CHEN Zhenyu, FANG Xudong, XU Fanghong, ZHANG Naiqiang. Oxidation Characteristics of Austenitic Heat-resistant Steel HR3C and Sanicro25 in Supercritical Water for Power Station[J]. 中国腐蚀与防护学报, 2020, 40(6): 529-538.
[3]	XIE Dongbai, HONG Hao, WANG Wen, PENG Xiao, DUO Shuwang. Oxidation Behavior of Stainless Steel 1Cr11Ni2W2MoV in a Simulated Kerosene Combustion Environment[J]. 中国腐蚀与防护学报, 2020, 40(4): 358-366.
[4]	CAO Jingyi, FANG Zhigang, CHEN Jinhui, CHEN Zhixiong, YIN Wenchang, YANG Yange, ZHANG Wei. Preparation and Properties of Micro-arc Oxide Film with Single Dense Layer on Surface of 5083 Aluminum Alloy[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[5]	FANG Xudong, LIU Xiao, XU Fanghong, LI Ruitao, ZHU Zhongliang, ZHANG Naiqiang. Oxidation Behavior in Supercritical Water of Domestic Austenitic Steel C-HRA-5 for Uultra-supercritical Power Stations[J]. 中国腐蚀与防护学报, 2020, 40(3): 266-272.
[6]	ZHENG Yanxin, LIU Ying, SONG Qingsong, ZHENG Feng, JIA Yuchuan, HAN Peide. High-temperature Oxidation Behavior and Wear Resistance of Copper-based Composites with Reinforcers of C, ZrSiO₄ and Fe[J]. 中国腐蚀与防护学报, 2020, 40(2): 191-198.
[7]	XU Xunhu,HE Cuiqun,XIANG Junhuai,WANG Ling,ZHANG Honghua,ZHENG Xiaodong. High Temperature Oxidation Behavior of Co-20Re-25Cr-1Si Alloy in 0.1 MPa Pure Oxygen[J]. 中国腐蚀与防护学报, 2020, 40(1): 75-80.
[8]	JIANG Dongxue,FU Ying,ZHANG Junwei,ZHANG Wei,XIN Li,ZHU Shenglong,WANG Fuhui. Preparation and Properties of Alumina Ceramic Film on Ti-alloy Surface[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.
[9]	XIAO Jintao,CHEN Yan,XING Mingxiu,JU Pengfei,MENG Yingen,WANG Fang. Effect of Process Parameters on Corrosion Resistance of Anodizing Film on 2195 Al-Li Alloy[J]. 中国腐蚀与防护学报, 2019, 39(5): 431-438.
[10]	AI Peng,LIU Lixiang,LI Xiaogang,JIANG Wentao. Influence of TiAlSiN Coatings on High Temperature Oxidation Resistance of γ-TiAl Based Alloys[J]. 中国腐蚀与防护学报, 2019, 39(4): 306-312.
[11]	Yunhai MA. Effect of Shot Peening on Oxidation Resistance of Super 304H Steel in Supercritical Steam[J]. 中国腐蚀与防护学报, 2019, 39(3): 245-252.
[12]	Junjie XIA,Hongzhi NIU,Min LIU,Huazhen CAO,Guoqu ZHENG,Liankui WU. Enhancement of High Temperature Oxidation Resistance of Ti48Al5Nb Alloy via Anodic Anodization in NH₄F Containing Ethylene Glycol[J]. 中国腐蚀与防护学报, 2019, 39(2): 96-105.
[13]	Dongbai XIE,Youyu ZHOU,Jintao LU,Wen WANG,Shenglong ZHU,Fuhui WANG. Effect of Al/Si Content on Corrosion of Ni-based Alloys in Supercritical Water[J]. 中国腐蚀与防护学报, 2019, 39(1): 68-76.
[14]	Ling WANG,Junhuai XIANG,Honghua ZHANG,Songlin QIN. High Temperature Oxidation Behavior of Three Co-20Re-xCr Alloys in 3.04×10^-5 Pa Oxygen at 1000 and 1100 ℃[J]. 中国腐蚀与防护学报, 2019, 39(1): 83-88.
[15]	Hao CHEN,Qing CHEN,Li XIN,Long SHI,Shenglong ZHU,Fuhui WANG. Preparation and High Temperature Corrosion Behavior of Aluminized Nanocrystalline Coating on DD98M Alloy[J]. 中国腐蚀与防护学报, 2019, 39(1): 59-67.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed