STUDY OF Ni-P AND Ni-P-PTFE COATINGS ON CARBON STEEL VIA ELECTROLESS DEPOSITION

LIU Xuezhong, LI Chao, WANG Jianfei, TIAN Jintao, YIN Yansheng

Institute of Materials Science and Engineering, Ocean University of China, Qingdao 266100

Download:

PDF(1520KB)
Export: BibTeX | EndNote (RIS)

Abstract The Ni-P and Ni-P-PTFE coatings were experimentally electroless deposited on the surface of carbon steel in the present study. The key preparing process was explored and the as-prepared coatings of Ni-P and Ni-P-PTFE were then characterized using SEM, EDS and XRD. The electrochemical polarization curves and the weight increases of the coated samples in the seawater were conducted to assess the anti-corrosion behaviors of the two coatings. The results indicated that the Ni-P and Ni-P-PTFE coatings have been successfully electroless deposited on the surface of carbon steel. The surface microstructure observations showed that the Ni-P coating was smooth and compact rather than the Ni-P-PTFE coating. Although the results from polarization curves and weight gains indicated that the Ni-P-PTFE coating had anti-corrosion behavior slightly poorer than the Ni-P coating due to the presence of the composite interface in the Ni-P-PTFE coating, the two coatings prepared in this study could provide carbon steel with valuable protection from seawater attack.

Key words: carbon steel electroless deposition Ni-P Ni-P-PTFE

Received: 09 April 2009

ZTFLH:

TG178

Corresponding Authors: TIAN Jintao E-mail: jttian@ouc.edu.cn

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	LIU Hua-Zhong
	YUN Yan-Sheng
	TIAN Jin-Shou
	LI Tiao
	YU Jian-Fei

Cite this article:

LIU Xuezhong, LI Chao, WANG Jianfei, TIAN Jintao, YIN Yansheng. STUDY OF Ni-P AND Ni-P-PTFE COATINGS ON CARBON STEEL VIA ELECTROLESS DEPOSITION. J Chin Soc Corr Pro, 2010, 30(5): 379-382.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2010/V30/I5/379

[1] Wang Q Z, Du M. Corrosion and Protection Technology of Metal in the Sea [M]. Qingdao: Ocean University of Qingdao Press, 2001 (王庆璋, 杜敏. 海洋腐蚀与防护技术 [M]. 青岛：青岛海洋大学出版社，2001) [2] Little B J, Lee J S, Ray R I. The influence of marine biofilms on corrosion: a concise review [J]. Electrochim. Acta, 2008, 54(1): 2-7 [3] Wang D, Bierwagen G P. Sol-gel coatings on metals for corrosion protection [J]. Prog. Org. Coat., 2009, 64(4): 327-338 [4] Peeters P, Hoorn G, Daenen T. Properties of electroless and electroplated Ni-P and its application in microgalvanics [J].Electrochim. Acta, 2001, 47(9): 161-169 [5] Miyake T, Kume M, Yamaguchi K. Electrodeposition of Cu/Ni-P multilayers by a single bath technique [J]. Thin Solid Films, 2001, 397(1-2): 83-89 [6] Gu C, Lian J, Li G, et al. High corrosion-resistant Ni-P/Ni/Ni-P multilayer coatings on steel [J]. Surf. Coat. Technol., 2005,197(1): 61-67 [7] Zhang Y Z, Wu Y Y. Characterization of electroless Ni-P-PTFE composite deposits [J]. J. Mater. Sci. Lett., 1998, 17(2): 119-122 [8] Ger M, Hou K. The friction and wear of Ni-P-PTFE composite deposits and water lubrication [J]. Mater. Chem. Phys.,2002, 77(3): 755-764 [9] Zhao Q. Effect of surface free energy of graded Ni-P-PTFE coatings on bacterial adhesion [J]. Surf. Coat.Technol., 2004, 185(2-3): 199-204 [10] Zhao Q, Liu Y. Modification of stainless steel surfaces by electroless Ni-P and small amount of PTFE to minimize bacterial adhesion [J]. J. Food Eng., 2006, 72: 266-272

[1]	HUANG Peng, GAO Rongjie, LIU Wenbin, YIN Xubao. Fabrication of Superamphiphobic Surface for Nickel-plate on Pipeline Steel by Salt Solution Etching and Its Anti-corrosion Properties[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	ZHANG Chen, LU Yuan, ZHAO Jingmao. Synergistic Inhibition Effect of Imidazoline Ammonium Salt and Three Cationic Surfactants in H₂S/CO₂ Brine Solution[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[3]	YANG Yinchu,FU Xiuqing,LIU Lin,MA Wenke,SHEN Moqi. Electrochemical Corrosion of Ni-P-BN(h)-Al₂O₃ Composite Coating Deposited by Spray Electrodeposition[J]. 中国腐蚀与防护学报, 2020, 40(1): 57-62.
[4]	Ping XU,Shuo ZHANG,Shuai SI,Yajun ZHANG,Changzheng WANG. Corrosion Mechanism of Carbon Steel Induced by Protein and Polysaccharide-the Main Components of EPS[J]. 中国腐蚀与防护学报, 2019, 39(2): 176-184.
[5]	Xiankang ZHONG,Junying HU. Corrosion Behavior of X65 Carbon Steel in CO₂Containing Liquids with Constant pH and Ferrous Ion Concentration[J]. 中国腐蚀与防护学报, 2018, 38(6): 573-578.
[6]	Li WANG, Chunyun GUO, Kui XIAO, Tuerxun·Silayiding, Chaofang DONG, Xiaogang LI. Corrosion Behavior of Carbon Steels Q235 and Q450 in Dry Hot Atmosphere at Turpan District for Four Years[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[7]	Yue QIAO, Zhiping ZHU, Lei YANG, Zhifeng LIU. Monitoring and Simulated Experiments of Oxidation-Reduction Potential of Boiler Feedwater at High Temperatures[J]. 中国腐蚀与防护学报, 2018, 38(5): 487-494.
[8]	Wanjun PENG, Jiheng DING, Hao CHEN, Haibin YU. Corrosion Inhibition of Bio-based Inhibitor Furfuryl Glycidyl Ether[J]. 中国腐蚀与防护学报, 2018, 38(3): 303-308.
[9]	Guofu OU, Lulu ZHAO, Kai WANG, Kuanxin WANG, Haozhe JIN. Dew-Point Corrosion Behavior of 10^# Carbon Steel inHCl-H₂O Environment[J]. 中国腐蚀与防护学报, 2018, 38(1): 33-38.
[10]	Jie ZHANG, Xiuhua HU, Chuanbo ZHENG, Jizhou DUAN, Baorong HOU. Influence of Calcareous Deposit on Corrosion Behavior of Q235 Carbon Steel in Marine Microalgae Containing Medium[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[11]	Xiaobo MENG,Wubin JIANG,Yongli LIAO,Ruihai LI,Zhijun ZHENG,Yan GAO. Investigation on Atmospheric Corrosion Behavior of Transmission Tower Materials in Simulated Industrial Environments[J]. 中国腐蚀与防护学报, 2017, 37(5): 460-466.
[12]	Qingli CHENG,Bin TAO,Shuan LIU,Quanzhen LIU,Weihua ZHANG,Songbai TIAN,Liping WANG. Corrosion Behaviour of Q235B Carbon Steel in Sediment Water From Crude Oil[J]. 中国腐蚀与防护学报, 2017, 37(2): 126-134.
[13]	Yongsheng HAO,Abdullahi SANI Luqman,Lixin SONG,Guobao XU,Tiejun GE,Qinghong FANG. Corrosion Inhibition Effect of Phytic Acid Conversion Coating Formed on Q235 Carbon Steel in Acidic and Neutral Solutions[J]. 中国腐蚀与防护学报, 2016, 36(6): 549-558.
[14]	Jihui WANG,Huajie YAN,Wenbin HU. Preparation and Inhibition Behavior of Molybdate Intercalated ZnAlCe-hydrotalcite[J]. 中国腐蚀与防护学报, 2016, 36(6): 637-644.
[15]	Hongwei LIU,Fuping XIONG,Yalin LV,Chengxuan GE,Hongfang LIU,Yulong HU. CO₂ Corrosion Inhibition of Carbon Steel by Dodecylamine under Flow Conditions[J]. 中国腐蚀与防护学报, 2016, 36(6): 645-651.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed