STUDY ON ATMOSPHERIC CORROSION OF LOW ALLOY STEELS

Qingdong Zhong

上海市上海电力学院电化学室

Download:

PDF(133KB)
Export: BibTeX | EndNote (RIS)

Abstract The corrosion of 7 kinds of mild steel and low alloy steel in immersion-wet-dry cycle test environment and the electrochemical feature of rusted metals after test were studied by using EIS and SEM et al.The solution containing HSO-3 and Cl-,was used for wetting and immersion specimens at circumstance temperature 40℃ for 4 min respectively.The drying cycle was maintained for 12 min at temperature 12℃.The results indicated that,the weight loss all followed exponential decay function:Y=Y0+Ae-t/B.The corrosion rate of mild steel was 2.49 times than that of the most corrosion resistant low alloy after 120 h test.The results of electrochemical measurement showed that,the further corrosion rate would be controlled by cathodic diffusion process.The impedance of 7 kinds of steels after corrosion test was linear with the annual corrosion rate.

Key words: steel low alloy steel atmospheric corrosion

Received: 25 November 2002

ZTFLH:

TG172.3

Corresponding Authors: Qingdong Zhong

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Qingdong Zhong

Cite this article:

Qingdong Zhong. STUDY ON ATMOSPHERIC CORROSION OF LOW ALLOY STEELS. J Chin Soc Corr Pro, 2004, 24(3): 151-154 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2004/V24/I3/151

[1]CorvoF ,BetancourtN ,MendozaAR .Theinfluenceofairbornesalinityontheatmosphericcorrosionofsteel[J].Corros.Sci.,1995,37(12):1889
[2]CorvoF ,MendozaAR ,AutieM ,etal.Roleofwateradsorptionandsaltcontentinatmosphericcorrosionproductsofsteel[J].Corros.Sci.,1997,39(4):815
[3]MendozaAR ,CorvoF .Outdoorandindooratmosphericcorrosionofcarbonsteel[J].Corros.Sci.,1998,41(1):75
[4]OhSJ,CookDC ,TownsendHE .Atmosphericcorrosionofdiffer entsteelsinmarine,ruralandindustrialenvironments[J].Corros.Sci.,1999,41(9):1687
[5]MorcilloM ,ChicoB ,MariacaL ,etal.Salinityinmarineatmospher iccorrosion:itsdependenceonthewindregimeexistinginthesite[J].Corros.Sci.,2000,42(1):91
[6]ChungKW ,KimKB .Astudyoftheeffectofconcentrationbuild-upofelectrolyteontheatmosphericcorrosionofcarbonsteeldur ingdrying[J].Corros.Sci.,2000,42(3):517
[7]WeiBM .TheoryofMetalCorrosionandApplication[M ].Beijing:ChemicalIndustryPress,1991(魏宝明.金属腐蚀理论及应用[M ].北京:化学工业出版社,1991)
[8]XuNX ,ZhaoLY ,DingCH ,etal.Somefactorsaffectingdewingbehavioronmildsteelsurfaceduringatmosphericcorrosion[J].Corros.Prot.,2001,22(12):522(徐乃欣,赵灵源,丁翠红等.碳钢大气腐蚀时表面结露行为的某些影响因素[J].腐蚀与防护,2001,22(12):522)
[9]XuNX ,ZhaoLY ,DingCH ,etal.Anovellaboratorytechniqueforobservingdewformationatearlystageinatmosphericcorrosion[J].J .Chin.Soc.Corros.Prot.,2001,21(5):301(徐乃欣,赵灵源,丁翠红等.研究大气腐蚀金属表面结露行为的新技术[J].中国腐蚀与防护学报,2001,21(5):301)
[10]ZhangCD ,XuNX ,DingCH ,etal.Electrochemicaltechniqueforinvestigatingthinfilmrustpreventiveoil[J].J .Chin.Soc.Corros.Prot.,1991,11(2):263(张承典,徐乃欣,丁翠红等.研究薄层防锈油的电化学技术[J].中国腐蚀与防护学报,1991,11(2):263)
[11]ZouMP ,LiX ,ZhongQD ,etal.Influenceofsurfacecontamina tiononatmosphericcorrosionperformanceofcold-rolledsteelplates[J].Corros.Prot.,2002,23(5):196(邹美平,郦希,钟庆东等.表面污染物对冷轧低碳钢板耐大气腐蚀性能的影响[J].腐蚀与防护,2002,23(5):196)

[1]	DAI Ting, GU Yanhong, GAO Hui, LIU Kailong, XIE Xiaohui, JIAO Xiangdong. Electrochemical Performance of Underwater Friction Stud Welding Joint in CO₂ Saturated NaCl Solution[J]. 中国腐蚀与防护学报, 2021, 41(1): 87-95.
[2]	TANG Rongmao, ZHU Yichen, LIU Guangming, LIU Yongqiang, LIU Xin, PEI Feng. Gray Correlative Degree Analysis of Q235 Steel/conductive Concrete Corrosion in Three Typical Soil Environments[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	RAN Dou, MENG Huimin, LIU Xing, LI Quande, GONG Xiufang, NI Rong, JIANG Ying, GONG Xianlong, DAI Jun, LONG Bin. Effect of pH on Corrosion Behavior of 14Cr12Ni3WMoV Stainless Steel in Chlorine-containing Solutions[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[4]	BAI Yunlong, SHEN Guoliang, QIN Qingyu, WEI Boxin, YU Changkun, XU Jin, SUN Cheng. Effect of Thiourea Imidazoline Quaternary Ammonium Salt Corrosion Inhibitor on Corrosion of X80 Pipeline Steel[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[5]	ZUO Yong, CAO Mingpeng, SHEN Miao, YANG Xinmei. Effect of Mg on Corrosion of 316H Stainless Steel in Molten Salts MgCl₂-NaCl-KCl[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[6]	WANG Xintong, CHEN Xu, HAN Zhenze, LI Chengyuan, WANG Qishan. Stress Corrosion Cracking Behavior of 2205 Duplex Stainless Steel in 3.5%NaCl Solution with Sulfate Reducing Bacteria[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[7]	ZHANG Hao, DU Nan, ZHOU Wenjie, WANG Shuaixing, ZHAO Qing. Effect of Fe³⁺ on Pitting Corrosion of Stainless Steel in Simulated Seawater[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[8]	WANG Lei, DONG Junhua, HAN Da, LIANG Jiankun, LI Quan, KE Wei. Phenonmenon of Cu Segregation in Cu-containing steel During Soaking at 1150 ℃[J]. 中国腐蚀与防护学报, 2020, 40(6): 545-552.
[9]	LIU Xiao, WANG Hai, ZHU Zhongliang, LI Ruitao, CHEN Zhenyu, FANG Xudong, XU Fanghong, ZHANG Naiqiang. Oxidation Characteristics of Austenitic Heat-resistant Steel HR3C and Sanicro25 in Supercritical Water for Power Station[J]. 中国腐蚀与防护学报, 2020, 40(6): 529-538.
[10]	MA Mingwei, ZHAO Zhihao, JING Siwen, YU Wenfeng, GU Yien, WANG Xu, WU Ming. Corrosion Behavior of 17-4 PH Stainless Steel in Simulated Seawater Containing SRB[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[11]	AI Fangfang, CHEN Yiqing, ZHONG Bin, LI Lin, GAO Peng, SHAN Hongyu, SU Xiandong. Stress Corrosion Cracking Behavior of T95 Oil Well Pipe Steel in Sour Environment[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.
[12]	LI Ziyun, WANG Gui, LUO Siwei, DENG Peichang, HU Jiezhen, DENG Junhao, XU Jingming. Early Corrosion Behavior of EH36 Ship Plate Steel in Tropical Marine Atmosphere[J]. 中国腐蚀与防护学报, 2020, 40(5): 463-468.
[13]	LI Lin, CHEN Yiqing, GAO Peng, AI Fangfang, ZHONG Bin, SAN Hongyu, YANG Ying. Corrosion Resistance of Various Bridge Steels in Deicing Salt Environments[J]. 中国腐蚀与防护学报, 2020, 40(5): 448-454.
[14]	ZHAI Sixin, YANG Xingyun, YANG Jilan, GU Jianfeng. Corrosion Properties of Quenching-Partitioning-Tempering Steel in Simulated Seawater[J]. 中国腐蚀与防护学报, 2020, 40(5): 398-408.
[15]	DAI Mingjie, LIU Jing, HUANG Feng, HU Qian, LI Shuang. Pitting Corrosion Behavior of X100 Pipeline Steel in a Simulated Acidic Soil Solution under Fluctuated Cathodic Protection Potentials Based on Orthogonal Method[J]. 中国腐蚀与防护学报, 2020, 40(5): 425-431.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed