THE ENVIRONMENT OF ATMOSPHERIC CORROSION AND ENVIRONMENTAL FACTORS FUZZY CLUSTERING ANALYZE

Lunwu Zhang;Xuehua Wang;Xianhe Feng

中国兵器工业第五研究所国防科技工业自然环境实验中心

Download:

PDF(111KB)
Export: BibTeX | EndNote (RIS)

Abstract Using more than ten years environmental factors dat a of China atmospheric corrosion test networks,adopting the method of fuzzy clus tering analyze,the environment of eight atmospheric corrosion test sites was cla ssified,the relativity of seventeen environmental factors was evaluated.The resu lt indicates:the environment of China atmospheric corrosion test networks is ver y representative and the common and different characteristic among environmental factors was showed.

Key words: atmospheric corrosion environmental factors fuzzy clus tering analyze

Received: 30 August 2001

ZTFLH:	TG172.3
	O159

Corresponding Authors: Luwu Zhang

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Lunwu Zhang
	Xuehua Wang
	Xianhe Feng

Cite this article:

Lunwu Zhang; Xuehua Wang; Xianhe Feng. THE ENVIRONMENT OF ATMOSPHERIC CORROSION AND ENVIRONMENTAL FACTORS FUZZY CLUSTERING ANALYZE. J Chin Soc Corr Pro, 2003, 23(2): 112-115 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2003/V23/I2/112

[1]WangGuangyong,etal.CorrosionandProtectionofNaturalEnvironment[M].Beijing:ChemicalIndustryPublishingHouse,1997(王光雍等.自然环境的腐蚀与防护[M].北京:化学工业出版社,1997)
[2]TianYuee,JinLei,WangXuehua.ChangingregulationsofmeteorologicalfactorsoftheatmosphericcorrosiontestsitesinChina[J].Corros.Sci.Prote.Technol.,1995,7(3):196(田月娥,金蕾,汪学华.我国大气腐蚀试验站气象因素变化规律[J].腐蚀科学与防护技术,1995,7(3):196)
[3]FengDeyi,LouShibo,etal.FuzzyMathematicsMethodandApplication[M].Beijing:EarthquakePublisher,1983(冯德益,楼世博等.模糊数学方法与应用[M].北京:地震出版社,1983)

[1]	FAN Yi,CHEN Linheng,CAI Jiaxing,DAi Qinqin,MA Hongchi,CHENG Xuequn. Corrosion Behavior of Hot-rolled AH36 Plate in Indoor Storage Environment[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[2]	PAN Chengcheng,MA Chao,XIA Dahai. Estimation for Relevance of Atmospheric Corrosion Initiation with Surface Texture of Several Metallic Materials by Electron Backscattering Diffraction[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[3]	ZHAO Jinbin,ZHAO Qiyue,CHEN Linheng,HUANG Yunhua,CHENG Xuequn,LI Xiaogang. Effect of Different Surface Treatments on Corrosion Behavior of 300M Steel in Qingdao Marine Atmosphere[J]. 中国腐蚀与防护学报, 2019, 39(6): 504-510.
[4]	DENG Junhao,HU Jiezhen,DENG Peichang,WANG Gui,WU Jingquan,WANG Kun. Effect of Oxide Scales on Initial Corrosion Behavior of SPHC Hot Rolled Steel in Tropical Marine Atmosphere[J]. 中国腐蚀与防护学报, 2019, 39(4): 331-337.
[5]	Yongwei SUN,Yuping ZHONG,Lingshui WANG,Fangxiong FAN,Yatao CHEN. Corrosion Behavior of Low-alloy High Strength Steels in a Simulated Common SO₂-containing Atmosphere[J]. 中国腐蚀与防护学报, 2019, 39(3): 274-280.
[6]	Li WANG, Chunyun GUO, Kui XIAO, Tuerxun·Silayiding, Chaofang DONG, Xiaogang LI. Corrosion Behavior of Carbon Steels Q235 and Q450 in Dry Hot Atmosphere at Turpan District for Four Years[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[7]	Jun WANG, Chao FENG, Bicao PENG, Yi XIE, Minghua ZHANG, Tangqing WU. Corrosion Behavior of Weld Joint of S450EW Steel in NaHSO₃ Solution[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[8]	Xinxin ZHANG,Zhiming GAO,Wenbin HU,Zhipeng WU,Lianheng HAN,Lihua LU,Yan XIU,Dahai XIA. Correlation Between Corrosion Behavior and Image Information of Q235 Steel Beneath Thin Electrolyte Film[J]. 中国腐蚀与防护学报, 2017, 37(5): 444-450.
[9]	Xin ZHANG,Nianwei DAI,Yan YANG,Junxi ZHANG. Effect of Direct Current Electric Field on Corrosion Mechanism of Zn Exposed to Simulated Industrial Environment[J]. 中国腐蚀与防护学报, 2017, 37(5): 451-459.
[10]	Xiaobo MENG,Wubin JIANG,Yongli LIAO,Ruihai LI,Zhijun ZHENG,Yan GAO. Investigation on Atmospheric Corrosion Behavior of Transmission Tower Materials in Simulated Industrial Environments[J]. 中国腐蚀与防护学报, 2017, 37(5): 460-466.
[11]	Shuangqing SUN,Qifei ZHENG,Chunling LI,Xiumin WANG,Songqing HU. Effect of Corrosion Products on Long-term Atmospheric Corrosion of Pure Aluminum 8A06[J]. 中国腐蚀与防护学报, 2017, 37(2): 110-116.
[12]	Ziheng BAI,Yunhua HUANG,Xiaogang LI,Lang YANG,Chaofang DONG,Lidan YAN,Kui XIAO. Environmental Corrosion in Industrial-marine Atmosphere at Qingdao of 7050 Al-alloy Anodized in Boric- and Sulfuric-acid Electrolyte[J]. 中国腐蚀与防护学报, 2016, 36(6): 580-586.
[13]	Dongliang LI,Guiqin FU,Miaoyong ZHU. Effect of Si on Corrosion Behavior of Model Bridge Steels by Alternative Wetting/drying Test in an Artificial Medium Simulated Hot and Humid Atmosphere of Marine and Industrial Area[J]. 中国腐蚀与防护学报, 2016, 36(5): 433-440.
[14]	Chuan WANG,Gongwang CAO,Chen PAN,Zhenyao WANG,Miaoran LIU. Atmospheric Corrosion of Carbon Steel and Weathering Steel in Three Environments[J]. 中国腐蚀与防护学报, 2016, 36(1): 39-46.
[15]	Yanjie LIU,Zhenyao WANG,Wei KE. Characterization of Corrosion Products on Pure Al Exposed in Atmospheres at Typical Rural, Industrial and Coastal Areas in China[J]. 中国腐蚀与防护学报, 2016, 36(1): 47-51.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed