高频脉冲电沉积镍钴合金镀层的硬度研究

许韵华1;曹克宁2;杨玉国1;赵宇1;宫晓静

1.北京交通大学理学院北京 100044
2.北京卫星制造厂北京 100081

MICROHARDNESS OF Ni-Co ALLOY PLATED BY HIGH FREQUENCY PULSE CURRENTS

XU Yunhua¹;CAO Kening²;YANG Yuguo¹;ZHAO Yu¹; GONG Xiaojing¹

1.School of Sciences; Beijing Jiaotong University; Beijing 100044
2.Beijing Spacecrafts; Beijing 100081

全文: PDF(1286 KB)

摘要:

在硫酸盐电解液中，采用脉冲电源电沉积了镍钴合金。研究了电解液中CoSO₄的浓度及脉冲参数对镀层中Co含量和镀层显微硬度的影响。采用SEM和XRD研究了镀层的表面形貌和微观结构。结果表明，镀层中的Co含量对镀层硬度有显著影响，当Co含量小于55 mass%时，镀层的硬度随着Co含量的增加递增。Co含量较低时，合金由面心立方结构（fcc）的固溶体组成。

关键词 ：高频, 镍钴合金, 显微硬度, 微观结构

Abstract：

Ni-Co alloys were deposited by applying current pulses from a sulfate electrolyte. The effect of the ionic concentration of cobalt in the electrolyte and pulse parameters on the cobalt content in the deposits and the microhardness of the deposits were studied. The morphologies and metallic phases of the alloys were analysed by scanning electron microscope(SEM) and X-ray diffraction(XRD). The results indicated that the cobalt content in alloy deposits had a strong effect on its hardness, and the increase of cobalt content resulted in increasing of the hardness of the deposits. At low cobalt content, pure face centered cubic (fcc) structure was identified.

Key words： High frequency Ni-Co alloys Microhardness Microstructure

收稿日期: 2007-07-02

ZTFLH:

TQ153.2

基金资助:

国家重点基础研究发展规划项目（2007CB714705）

通讯作者: 许韵华 E-mail: yhxu@bjtu.edu.cn

Corresponding author: XU Yunhua E-mail: yhxu@bjtu.edu.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	曹克宁
44.8K

引用本文:

许韵华曹克宁杨玉国赵宇宫晓静. 高频脉冲电沉积镍钴合金镀层的硬度研究[J]. 中国腐蚀与防护学报, 2009, 29(2): 141-144.
CAO Ke-Ning. MICROHARDNESS OF Ni-Co ALLOY PLATED BY HIGH FREQUENCY PULSE CURRENTS. J Chin Soc Corr Pro, 2009, 29(2): 141-144.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2009/V29/I2/141

[1] Wu G, Li N，Zhou D, et al. Electrodeposited Co-Ni-Al$_{2}$O$_{3}$ composite coatings[J].Surf. Coat. Technol., 2004, 176(1): 157-164
[2] Benea L, Bonora P L, Borello A, et al. Wear corrosion properties of nano-structured SiC-nickel composite coatings obtained by electroplating[J]. Wear, 2002, 249: 995-1003 \vskip 1mm
[3] Golodnitsky D, Gudin D V, Volyanuk G A. Cathode process in nickel-cobalt alloy deposition from sulfamate electrolytes-application to electroforming[J]. Pla. Surf. Finish., 1998, 85(2):65-73
[4] Myung N V, Nobe K. Electrodeposited iron group thin-film alloys structure-property relationships[J].J. Electrochim. Soc., 2001, 148(3): 136-144
[5] Golodnitsky D, Gudin N V, Volyanuk G A. Study of nickel-cobalt alloy electrodeposition from a sulfamate electrolyte with different anion additives[J]. J. Electrochim. Soc., 2000, 147(11): 4156-4163
[6] Wuhan Research Institute of Materials Protection. Analysis of Electrolyte in Common Use (Third Edition)[M]. Beijing: China Machine Press, 1993: 146
    (武汉材料保护研究所主编．常用电镀溶液的分析(第三版)[M]. 北京:机械工业出版社. 1993: 146)
[7] Xiao Z B, Li Z l, Dai N Z, et al. Anomalous codeposition of alloys[J]. Mater.Prot., 2000, 33 (7): 19-20
    (肖卓炳, 李则林, 戴年珍等.合金异常共沉积研究[J]. 材料保护, 2000, 33(7): 19-20)
[8] Meenu S, Ezhil S V, William Grips V K, et al.Corrosion resistance and microstructure of electrodeposited nickel-cobalt alloy coatings [J]．Surf. Coat. Technol., 2006,201(6): 3051-3060
[9] Xiang G P , Zhou E B.Study of Ni-Co alloy pulse-plating[J]. Electroplat. Finish., 1994,13(2): 8-10
    (向过朴, 周恩彪. 脉冲电镀Ni-Co合金的研究[J].电镀与涂饰, 1994, 13(2): 8-10)
[10] Ghosh S K,Grover A K, Dey G K, et al. Nanocrystalline Ni-Cu alloy plating by pulse electrolysis[J]. Surf. Coat. Technol., 2000, 126(1): 48-63
[11] Tury B, Roy S. Ni-Co alloys plated by pulse currents [J]. Surf. Coat. Technol.，2006, 200(24): 6713-6717

[1]	李聪玮, 杜双明, 曾志琳, 刘二勇, 王飞虎, 马付良. 电流密度对Ni-Co-B镀层微观结构及磨蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 439-447.
[2]	闻洋, 熊林, 陈伟, 薛刚, 宋文学. 干湿循环下聚乙烯醇纤维混凝土抗Cl^-渗透性能研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 381-388.
[3]	姜冬雪,付颖,张峻巍,张伟,辛丽,朱圣龙,王福会. 钛合金表面Al₂O₃陶瓷膜制备及性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.
[4]	魏欣欣,张波,马秀良. FeCr₁₅Ni₁₅单晶600 ℃下热生长氧化膜的TEM观察[J]. 中国腐蚀与防护学报, 2019, 39(5): 417-422.
[5]	于美,魏新帝,范世洋,刘建华,李松梅,钟锦岩. 应力作用下2297铝锂合金腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 439-445.
[6]	史昆玉,张进中,张毅,万毅. Nb₂N涂层制备及其耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[7]	张志英, 汤迦南, 余杰, 王旭东, 黄罗超, 邹俊文, 唐浩, 张继康, 陈亚涛, 程东鹏. 铜基非晶合金复合材料在NaCl溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 478-486.
[8]	樊志民, 于锦, 宋影伟, 单大勇, 韩恩厚. 镁合金点蚀的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(4): 317-325.
[9]	李越, 王剑, 张勇, 白晋钢, 胡亚迪, 乔永锋, 张彩丽, 韩培德. 2205双相不锈钢密闭容器中高温初始氧化过程分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 296-302.
[10]	白强,邹妍,孔祥峰,高杨,刘岩,董胜. 奥氏体焊条水下湿法焊接CCSE40钢在海水中的腐蚀电化学行为研究[J]. 中国腐蚀与防护学报, 2016, 36(5): 427-432.
[11]	文丽娟, 高志明, 刘洋洋, 林峰. 阴极保护电位对Q235钢氢脆敏感性和力学性能的影响[J]. 中国腐蚀与防护学报, 2013, 33(4): 271-276.
[12]	杨英,董瑜亮,高立军,宫骏,姜辛,孙超. 氮气流量及后续热处理对多弧离子镀制备Ti₂AlN涂层的影响规律[J]. 中国腐蚀与防护学报, 2012, 32(1): 1-6.
[13]	李红; 张波; 王俭秋; 韩恩厚; 柯伟 . 合金元素Sb和Mn对Zn腐蚀的影响[J]. 中国腐蚀与防护学报, 2008, 28(5): 257-264 .
[14]	韩树民; 郑炀曾; 于升学 . 锌铝铬转化膜微观结构与成膜机理研究[J]. 中国腐蚀与防护学报, 2002, 22(5): 269-273 .
[15]	齐慧滨; 庞洪梅; 何业东; 王德仁 . 弥散氧化物微晶涂层的高温氧化性能[J]. 中国腐蚀与防护学报, 2002, 22(2): 72-78 .

Viewed

Full text

Abstract

Cited

Shared

Discussed