铝基体上电沉积聚苯胺膜及其耐蚀性

徐国荣;周光喜;易清风;任凤莲

湖南科技大学南校区化学化工学院；中南大学化学化工学院

Study on Preparation and Corrosion Resistance of Conductive Polyaniline Coating on Aluminum by Electropolymerization

;;;

湖南科技大学南校区化学化工学院；中南大学化学化工学院

全文: PDF(1205 KB)

摘要: 探讨了电化学方法在Al基体上沉积聚苯胺膜的控制工艺，研究了聚苯胺膜的耐蚀性。结果表明，Al基体上沉积一层Ni后，可用电化学方法沉积聚苯胺膜。循环伏安法的扫描电位上限、恒电流法的电流密度、恒电位法的电位范围和电解质的酸度均影响苯胺的聚合速度和聚苯胺膜的物理性能。动电位极化曲线表明，在0.5 mol/L NaCl溶液中，用各种电化学方法沉积聚苯胺膜的Al样品，其点腐蚀电位比无膜时有所升高。Al基体表面覆盖导电聚苯胺膜以后，其耐蚀性能得到提高。

关键词 ：铝, 聚苯胺, 电化学法, 耐蚀性

Abstract：Polyaniline （PANI） films are deposited on aluminum substrate through electrochemical process and the corrosion resistance of PANI films is studied. The results show metallic nickel of nonelectrolytic deposition on the aluminum surface can catalyze electropolymerization of aniline.The proper upper scanning potential through cyclic voltammetry is not more than 0.7 V（vs. Hg/Hg2SO4）； the polymerization potential range through potentio?鄄static is between 0 and 0.45 V（vs. Hg/Hg2SO4）； the current density through galvanostatic is not more than 0.3 mA/cm2；the proper electrolytic pH value is at range of 2 to 3.The potentiodynamic polarization curves in 0.5 mol/L sodium chloride solution show that the pitting corrosion potentials of aluminum electrodes coated with PANI through cyclic voltammetry，potentiostatic or galvanostatic method shift toward positive direction as compared with pure aluminum electrode.The PANI coating could improve the pitting corrosion resistance of aluminum and its alloy.

Key words：

收稿日期: 2006-07-18

通讯作者: 徐国荣 E-mail: xuguorong@126.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	徐国荣
	周光喜
	易清风
	任凤莲
44.8K

引用本文:

徐国荣; 周光喜; 易清风; 任凤莲 . 铝基体上电沉积聚苯胺膜及其耐蚀性[J]. 中国腐蚀与防护学报, 2008, 28(1): 11-15 .
. Study on Preparation and Corrosion Resistance of Conductive Polyaniline Coating on Aluminum by Electropolymerization. J Chin Soc Corr Pro, 2008, 28(1): 11-15 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2008/V28/I1/11

[1]Zhang H,Yu Z M,Sun W C.Interface microstructure and corro-sion resistance of electrodeposited Cr coating on aluminum over-laid LY12[J].Corros.Sci.Prot.Technol.,2003,23(6):352-355(张慧,于志明,孙伟成.包铝LY12铝合金表面镀铬层的界面显微组织及耐蚀性能[J].腐蚀科学与防护技术,2003,23(6):352-355)
[2]Li G Q,Li D,Li J Q,et al.Cerium conversion coatings formed on anodized aluminum by cathodic electrolysis[J].J.Chin.Soc.Corros.Prot.,2001,21(3):150-157(李国强,李荻,李久青.铝阳极氧化膜上阴极电解沉积的稀土铈转化膜[J].中国腐蚀与防护学报,2001,21(3):150-157)
[3]Long X Q,Shao R K.Investigation of corrosion-resistance of chemical conversion film and phosphating primer on2024Alu-minium alloy[J].J.Chin.Soc.Corros.Prot.,2003,23(3):56-159(隆小庆,邵荣宽.2024铝合金化学转化膜与磷化底漆耐蚀性的研究[J].中国腐蚀与防护学报,2003,23(3):157-159)
[4]Xin T Z,Zhao W S,Liu J C,Characteristics and principle analysis of micro arc oxidation on Al alloy surface[J].Surf.Technol.2006,35(1):14-17(辛铁柱,赵万生,刘晋春.铝合金微弧氧化过程的特性研究及机理分析[J].表面技术,2006,35(1):14-17)
[5]Deberry D W.Modification of the electrochemical and corrosion behavior of stainless steel with electroactive coating[J].J.Elec-trochem.Soc.,1985,132(5):1022-1026
[6]Jing X L,Wang Y Y,Qiang J F.Anti-corrosion property of e-meraldine base form of polyaniline[J].J.Chin.Soc.Corros.Prot.,2004,24(5):301-305(井新利,王杨勇,强军锋.本征态聚苯胺的防腐性能[J].中国腐蚀与防护学报,2004,24(5):301-305)
[7]Jiang Y F,Zhai C Q,Guo X W,et al.Growth of polyaniline film on AZ91magnesium alloy surface[J].Mater.Rev.,2003,17(4):70-72(蒋永锋,翟春泉,郭兴伍等.聚苯胺膜在AZ91镁合金表面的生长过程[J].材料导报,2003,17(4):70-72)
[8]Wang S L,Long J M,Wang J.Corrosion resistance of polyaniline coating on low carbon steel[J].Corros.Prot.,2004,25(4):142-145(王少龙,龙晋明,王静.低碳钢基体上电沉积聚苯胺膜及耐蚀性研究[J].腐蚀与防护,2004,25(4):142-145)
[9]Pournaghi-Azar M H,Ramzmi-Nerbin H.Voltammetric behaviour and electrocatalytic activity of the aluminum electrode modified with nickel and nickel hexacyanoferrate films,prepared by elec-troless deposition[J].J.Electroanal.Chem.,1998,456:83-90
[10]Thompson G E.Porous anodic alumina:fabrication,characteriza-tion and applications[J].Thin Solid Films,1997,297:192-201
[11]Lai X J,Zuo L Cui.One-step synthesis of oriented polyaniline nanorods through electrochemical deposition[J].Polym.Bull.,2006,online
[12]Wen J B,Zhou H H,Li S L,et al.Growth process of nano-fibrous polyaniline film on stainless Steel[J].Acta Phys.Chim.Sin.,2006,22(1):106-109(温靖邦,周海晖,李松林等.纳米纤维聚苯胺膜在不锈钢电极表面的生长过程[J].物理化学学报,2006,22(1):106-109)
[13]Dong P,Zhou J Z,Xi Y Y,et al.The growth mechanism of elec-trosynthesized polyaniline nanotubules in aluminua template[J].Acta Phys.Chim.Sin.,2004,20(5):454-458(董平,周剑章,席燕燕等.聚苯胺纳米管在阳极氧化铝模板中电聚合的生长机理[J].物理化学学报,2004,20(5):454-458)

[1]	黄鹏, 高荣杰, 刘文斌, 尹续保. 盐溶液刻蚀-氟化处理制备X65管线钢镀镍超双疏表面及其耐蚀性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[3]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[4]	包任, 周根树, 李宏伟. 恒电位脉冲电沉积高锡青铜耐蚀镀层工艺研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 585-591.
[5]	刘海霞, 黄峰, 袁玮, 胡骞, 刘静. 690 MPa级高强贝氏体钢在模拟乡村大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 416-424.
[6]	李聪玮, 杜双明, 曾志琳, 刘二勇, 王飞虎, 马付良. 电流密度对Ni-Co-B镀层微观结构及磨蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 439-447.
[7]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[8]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[9]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[10]	王乐,易丹青,刘会群,蒋龙,冯春. Ru对Ti-6Al-4V合金腐蚀行为的影响及机理研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 25-30.
[11]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[12]	姜冬雪,付颖,张峻巍,张伟,辛丽,朱圣龙,王福会. 钛合金表面Al₂O₃陶瓷膜制备及性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 469-476.
[13]	余春堂,阳颖飞,鲍泽斌,朱圣龙. 先进高温热障涂层用高性能粘接层制备及研究进展[J]. 中国腐蚀与防护学报, 2019, 39(5): 395-403.
[14]	肖金涛,陈妍,邢明秀,鞠鹏飞,孟引根,王芳. 工艺参数对2195铝锂合金阳极氧化膜的耐蚀性影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 431-438.
[15]	于美,魏新帝,范世洋,刘建华,李松梅,钟锦岩. 应力作用下2297铝锂合金腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 439-445.

Viewed

Full text

Abstract

Cited

Shared

Discussed