304不锈钢在微生物介质中的腐蚀行为

闫林娜;尹衍升;常雪婷;程莎;马永

CORROSION BEHAVIOR OF 304 STAINLESS STEEL IN CULTURED MICROBIAL MEDIUM

;;;;

全文: PDF(1013 KB)

摘要: 利用间歇式方法培养海水中的细菌，用极化曲线和电化学阻抗谱研究304不锈钢在有菌和无菌培养基中的腐蚀行为。研究表明，前者的阳极极化电流密度大于后者，且随着培养时间的延长，电化学阻抗值在无菌培养基中先降低后升高，而在有菌培养基中一直降低。表明海水中的细菌对304不锈钢的腐蚀起到促进作用，诱导了不锈钢点蚀的发生。

关键词 ： 304不锈钢, 微生物腐蚀, 极化曲线, 电化学阻抗

Abstract：The bacteria in seawater were cultured in batch and the corrosion behavior of 304 stainless steel in the medium of marine microorganisms was investigated by polarization curves and electrochemical impedance spec?鄄troscopy， etc. Experimental results show that the stainless steel current density of anodic polarization in culture medium with bacteria is higher than that without bacteria， and the impedance value in medium without bacteria first decreases then increases， while in medium with bacteria decreases all through. In conclusion，the bacteria in seawater accelerates the corrosion of 304 stainless steel and induces pitting corrosion to the 304 stainless steel.

Key words： Stainless steel Microbiologically Influenced Corrosion polarization curves electrochemical impedance

收稿日期: 2006-05-25

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	闫林娜
	尹衍升
	常雪婷
	程莎
	马永
44.8K

引用本文:

闫林娜; 尹衍升; 常雪婷; 程莎; 马永 . 304不锈钢在微生物介质中的腐蚀行为[J]. 中国腐蚀与防护学报, 2008, 28(1): 34-37 .

链接本文:

https://www.jcscp.org/CN/Y2008/V28/I1/34

[1]Liu H F,Wang M F,Xu L M,et al.The role of Ca2+on microbio-logically induced corrosion of carbon steel[J].J.Chin.Soc.Cor-ros.Prot.,2004,24(1):45-47(刘宏芳,王梅芳,许立铭等.钙离子对碳钢微生物腐蚀的影响[J].中国腐蚀与防护学报,2004,24(1):45-47)
[2]Iwona B Beech,Jan Sunner.Biocorrosion:towards understanding interactions between biofilms and metals[J].Curr.Opin.Biotech-nol.,2004,15:181-186
[3]Baker PW,Ito K,Watanabe K.Marine prosthecate bacteria in-volved in the ennoblement of stainless steel[J].Environ.Microbi-ol,2003,5:925-932
[4]Kjellerup B V,Olesen B H,Nielsen J L,Frolund B,Odum S,Nielsen P H.Monitoring and characterisation of bacteria in cor-roding district heating systems using fluorescence in situ hybridis-ation and microautoradiography[J].Water.Sci.Technol.,2003,47:117-122
[5]Zhang T,Fang H H P,Ko B C B.Methanogen population in a ma-rine biofilm corrosive to mild steel[J].Appl.Microbiol.Biotech-nol.,2003,63:101-106
[6]Wang M F,Liu H F,Xu L M.Applied research on the competitive growth of bacteria in biological control of MIC[J].J.Chin.Soc.Corros.Prot.,2004,24(3):159-162(汪梅芳,刘宏芳,许立铭.细菌竞争生长在微生物腐蚀防治中的应用研究[J].中国腐蚀与防护学报,2004,24(3):159-162)
[7]Dong Z H,Guo X P,Liu H F,et al.Study on electrochemistry characteristics in MIC by wire beam electrodes[J].J.Chin.Soc.Corros.Prot.,2002,22(1):48-53(董泽华,郭兴蓬,刘宏芳等.用丝束电极研究SRB微生物诱导腐蚀的电化学特征[J].中国腐蚀与防护学报,2002,22(1):48-53)
[8]Beech I B.Corrosion oftechnical materialsin the presence ofbiofilms-current understanding and state-of-the-art methods of study[J].Int.Biodeterior.Biodegrad.,2004,53:177-183
[9]Sun C,Hai E H.Effects of SRB on corrosion of1Cr18Ni9Ti stain-less steel in soils of Cl-[J].J.Chin.Soc.Corros.Prot.,2003,23(1):46-51(孙成,韩恩厚.土壤中SRB及Cl-对1Cr18Ni9Ti不锈钢腐蚀的相互影响[J].中国腐蚀与防护学报,2003,23(1):46-51)
[10]Dexter S C,Ed.Biologically Induced Corrosion[M].Houston:Texas NACE,1986
[11]Zhang D Q,Liu W G,Lu D Q,et al.Corrosion behavior of carbon steel in cultured microbial medium of Huangpu river water[J].Corros.Prot.,2005,26(2):47-49(张大全,刘卫国,卢德强等.碳钢在黄浦江水培养微生物介质中的腐蚀行为[J].腐蚀与防护,2005,26(2):47-49)
[12]Liu H F,Xu L M,Zheng J S.Influence of SRB biofilm on corro-sion of carbon steel[J].J.Chin.Soc.Corros.Prot.,2000,20(1):41-46(刘宏芳,许立铭,郑家.SRB生物膜与碳钢腐蚀的关系[J].中国腐蚀与防护学报,2000,20(1):41-46)
[13]Li X B,Wang W,Wang J,et al.Effect of biofilms on metal corro-sion in sea water[J].Corros.Sci.Prot.Technol.,2002,14(4):219-222(李相波,王伟,王佳等.海水中微生物膜的生长对金属腐蚀过程的影响[J].腐蚀科学与防护技术,2002,14(4):219-222)

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[3]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[4]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[5]	李子运, 王贵, 罗思维, 邓培昌, 胡杰珍, 邓俊豪, 徐敬明. 热带海洋大气环境中EH36船板钢早期腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 463-468.
[6]	王玉, 吴佳佳, 张盾. 海水环境中异化铁还原菌所致金属材料腐蚀的研究进展[J]. 中国腐蚀与防护学报, 2020, 40(5): 389-397.
[7]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[8]	孙硕, 杨杰, 钱薪竹, 常人丽. Ni-Cr-P化学镀层的制备与电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(3): 273-280.
[9]	胥聪敏,罗立辉,王文渊,赵苗苗,田永强,宋鹏迪. D-tyrosine对碳钢表面铁细菌生物膜的杀菌增强作用机理研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 63-69.
[10]	卫晓阳,杨丽景,吕战鹏,郑必长,宋振纶. 磁场对纯Cu微生物腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 484-494.
[11]	骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[12]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[13]	达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[14]	吴堂清,周昭芬,王鑫铭,张德闯,尹付成,孙成. 微生物致裂的热力学和动力学分析[J]. 中国腐蚀与防护学报, 2019, 39(3): 227-234.
[15]	彭文山,侯健,丁康康,郭为民,邱日,许立坤. 深海环境中304不锈钢腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 145-151.

Viewed

Full text

Abstract

Cited

Shared

Discussed