| 食品包装用镀锡薄钢板的腐蚀机理研究进展 |
夏大海1,2( ), 宋诗哲1,2, 王吉会1(), 高志明1, 胡文彬1 |
1 天津大学材料科学与工程学院 天津市材料复合与功能化重点实验室 天津 300350
2 中国科学院金属研究所 中国科学院核用材料与安全评价重点实验室 沈阳 110016 |
|
| Research Progress on Corrosion Mechanism of Tinned Steel Sheet Used for Food Parkaging |
| Dahai XIA1,2(), Shizhe SONG1,2, Jihui WANG1(), Zhimng GAO1, Wenbin HU1 |
1 Tianjin Key Laboratory of Composite and Functional Materials, School of Materials Science and Engineering, Tianjin University, Tianjin 300350, China
2 CAS Key Laboratory of Nuclear Materials and Safety Assessment, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China |
引用本文:
夏大海, 宋诗哲, 王吉会, 高志明, 胡文彬. 食品包装用镀锡薄钢板的腐蚀机理研究进展[J]. 中国腐蚀与防护学报, 2017, 37(6): 513-518.
Dahai XIA,
Shizhe SONG,
Jihui WANG,
Zhimng GAO,
Wenbin HU.
Research Progress on Corrosion Mechanism of Tinned Steel Sheet Used for Food Parkaging. Journal of Chinese Society for Corrosion and protection, 2017, 37(6): 513-518.
链接本文:
https://www.jcscp.org/CN/10.11902/1005.4537.2016.225
或
https://www.jcscp.org/CN/Y2017/V37/I6/513
|
| [1] | Han Z W.Electrochemical analysis of metal/coatings’ degradation under food package environment [D]. Tianjin: Tianjin University, 2011(韩哲文. 食品包装环境下金属/涂层体系失效过程的电化学研究 [D]. 天津: 天津大学, 2011) | | [2] | Li N, Li D Y.Development of tin electroplated steel plate[J]. Mater. Prot., 2000, 33(5): 16(李宁, 黎德育. 罐用镀锡薄钢板的发展[J]. 材料保护, 2000, 33(5): 16) | | [3] | Xia D H.Deterioration process and corrosion detection of metal packaging Materials [D]. Tianjin: Tianjin University, 2012(夏大海. 金属包装材料的腐蚀失效过程和腐蚀检测 [D]. 天津: 天津大学, 2012) | | [4] | Huag J G, Li N, Wu L, et al.The thickness and structure of the Sn-Fe alloy in tinplate and their corrosion resistance [A]. Proceedings of the National Electronic Electroplating Workshop in 2001[C]. Suzhou, 2001(黄久贵, 李宁, 吴林等. 镀锡钢板锡铁合金层的厚度与结构及其耐蚀性 [A]. 2001年全国电子电镀年会论文集[C]. 苏州, 2001) | | [5] | Xia D H, Song S Z, Wang J H, et al.Corrosion detection of metal cans for beverage packaging[J]. CIESC J., 2012, 63: 1797(夏大海, 宋诗哲, 王吉会等. 饮料金属包装实罐产品的腐蚀检测[J]. 化工学报, 2012, 63: 1797) | | [6] | Xia D H, Song S Z, Gong W Q, et al.Detection of corrosion-induced metal release from tinplate cans using a novel electrochemical sensor and inductively coupled plasma mass spectrometer[J]. J. Food Eng., 2012, 113: 11 | | [7] | Zhang X, Boelen B, Beentjes P, et al.Influence of uniaxial deformation on the corrosion performance of pre-coated packaging steel[J]. Prog. Org. Coat., 2007, 60: 335 | | [8] | Barone C, Bolzoni L, Caruso G, et al.Food Packaging Hygiene[M]. Cham: Springer, 2015 | | [9] | Robertson G L.Food Packaging: Principles and Practice [M]. Boca Raton: CRC Press, 2016 | | [10] | Che Y, Han Z W, Luo B, et al.Corrosion mechanism differences of tinplate in aerated and deaerated citric acid solution[J]. Int. J. Electrochem. Sci., 2012, 7: 9997 | | [11] | Xia D H, Song S Z, Wang J H, et al.Corrosion behavior of tinplates in a functional beverage[J]. Acta Phys.-Chim. Sin., 2012, 28: 121(夏大海, 宋诗哲, 王吉会等.镀锡薄钢板在功能饮料中的腐蚀行为[J]. 物理化学学报, 2012, 28: 121) | | [12] | Wang J H, Fu C W, Gao Z M, et al.Corrosion process detection of tinplate in deaerated functional beverage by EIS[J]. Trans. Tianjin Univ., 2013, 19: 235 | | [13] | Xia D H, Wang J H, Song S Z, et al. The corrosion behavior of lacquered tinplate in functional beverage [J]. Adv. Mat. Res., 2011, 233-235: 1747 | | [14] | Xia D H, Song S Z, Wang J H, et al.Corrosion behavior of tinplate in NaCl solution[J]. Trans. Nonferrous Met. Soc. China, 2012, 22: 717 | | [15] | Patrick G W.Internal corrosion of tinplate food containers[J]. Anti-Corros. Met. Mater., 1976, 23: 9 | | [16] | Palmieri A, Montanari A, Fasanaro G.De-tinning corrosion of cans filled with tomato products[J]. Corros. Eng. Sci. Technol.,2004, 39: 198 | | [17] | Zurlini C, Montanari A, Squitieri G, et al.Shelf-life study of lacquered canned tomato: Influence of different variables of the process/product [A]. Paper Presented at the Asian Steel Packaging Conference[C]. Kuala Lumpur, 2010 | | [18] | Xia D H, Song S Z, Wang J Q, et al.Research progress on sulfur-induced corrosion of alloys 690 and 800 in high temperature and high pressure water[J]. Acta Metall. Sin., 2017, 53: 1541(夏大海, 宋诗哲, 王俭秋等. 690和800合金在高温高压水中硫致腐蚀失效研究进展[J]. 金属学报, 2017, 53: 1541) | | [19] | Choudhary L, Macdonald D D, Alfantazi A.Role of thiosulfate in the corrosion of steels: A review[J]. Corrosion, 2015, 71: 1147 | | [20] | Kontominas M G, Prodromidis M I, Paleologos E K, et al.Investigation of fish product-metal container interaction using scanning electron microscopy-X-ray microanalysis[J]. Food Chem., 2006, 98: 225 | | [21] | Zhou C, Wang J H, Song S Z, et al.Degradation mechanism of lacquered tinplate in energy drink by in-situ EIS and EN[J]. J. Wuhan Univ. Technol.(Mater. Sci. Ed.), 2013, 28: 367 | | [22] | Xia D, Wang J H, Jiang Y X, et al.Corrosion behavior of novolac epoxy coated tinplate in energy drink[J]. J. Tianjin Univ.(Sci. Technol.), 2013, 46: 503(夏大海, 王吉会, 蒋宇轩等. 环氧酚醛/镀锡薄钢板体系在功能饮料中的腐蚀行为[J]. 天津大学学报(自然科学与工程技术版),2013, 6: 503) | | [23] | Boelen B, Den Hartog H, Van Der Weijde H. Product performance of polymer coated packaging steel, study of the mechanism of defect growth in cans[J]. Prog. Org. Coat., 2004, 50: 40 | | [24] | Bastos A C, Sim?es A M P. Effect of uniaxial strain on the protective properties of coil-coatings[J]. Prog. Org. Coat., 2003, 46: 220 | | [25] | Zhou D, Wang J, Han Z, et al.Corrosion behavior of tinplate in aerated and deaerated NaCl solution[J]. Int. J. Electrochem. Sci., 2017, 12: 639 | | [26] | MontanariA, Pezzani A, Cassarà A, et al. Quality of organic coatings for food cans: Evaluation techniques and prospects of improvement[J]. Prog. Org. Coat., 1996, 29: 159 | | [27] | Xia D H, Song S Z, Wang J H, et al.Fast evaluation of degradation degree of organic coatings by analyzing electrochemical impedance spectroscopy data[J]. Trans. Tianjin Univ., 2012, 18: 15 | | [28] | Mahdavian M, Attar M M.Another approach in analysis of paint coatings with EIS measurement: Phase angle at high frequencies[J]. Corros. Sci., 2006, 48: 4152 | | [29] | Bovard F S, Burleigh T D, Smith A T.Electrochemical impedance spectroscopy of electrocoatedaluminium food cans[J]. Electrochim. Acta, 1995, 40: 201 | | [30] | Bastidas J M, Caba?es J M, Cataliá R.Evaluation of prolonged exposure of lacquered tinplate cans to a citrate buffer solution using electrochemical techniques[J]. Prog. Org. Coat., 1997, 30: 9 | | [31] | De Vooys A, Boelen B, Penning J P, et al.Improving coating resistance to acetic acid sterilisation: An EIS approach[J]. Prog. Org. Coat., 2009, 65: 30 | | [32] | Scantlebury J D, Gali? K.The application of AC impedance to study the performance of lacquered aluminium specimens in acetic acid solution[J]. Prog. Org. Coat., 1997, 31: 201 | | [33] | Barilli F, Fragni R, Gelati S, et al.Study on the adhesion of different types of lacquers used in food packaging[J]. Prog. Org. Coat.,2003, 46: 91 | | [34] | Catalá R, Caba?es J M, Bastidas J M.An impedance study on the corrosion properties of lacquered tinplate cans in contact with tuna and mussels in pickled sauce[J]. Corros. Sci., 1998, 40: 1455 | | [35] | Pournaras A V, Prodromidis M I, Katsoulidis A P, et al.Evaluation of lacquered tinplated cans containing octopus in brine by employing X-ray microanalysis and electrochemical impedance spectroscopy[J]. J. Food Eng., 2008, 86: 460 | | [36] | Xia D H, Song S Z, Behnamian Y.Detection of corrosion degradation using electrochemical noise (EN): Review of signal processing methods for identifying corrosion forms[J]. Corros. Eng. Sci. Technol., 2016, 51: 527 | | [37] | Zhang T, Yang Y G, Shao Y W, et al.Advances of the analysis methodology for electrochemical noise[J]. J. Chin. Soc. Corros. Prot., 2014, 34: 1(张涛, 杨延格, 邵亚薇等. 电化学噪声分析方法的研究进展[J]. 中国腐蚀与防护学报, 2014, 34: 1) | | [38] | Doherty M, Sykes J M.Micro-cells beneath organic lacquers: A study using scanning Kelvin probe and scanning acoustic microscopy[J]. Corros. Sci., 2004, 46: 1265 | | [39] | Reddy B, Sykes J M.Degradation of organic coatings in a corrosive environment: A study by scanning Kelvin probe and scanning acoustic microscope[J]. Prog. Org. Coat., 2005, 52: 280 | | [40] | Reddy B, Doherty M, Sykes J M.Breakdown of organic coatings in corrosive environments examined by scanning Kelvin probe and scanning acoustic microscopy[J]. Electrochim. Acta, 2004, 49: 2965 | | [41] | Doherty M, Sykes J M.A quantitative study of blister growth on lacquered food cans by scanning acoustic microscopy[J]. Corros.Sci., 2008, 50: 2755 | | [42] | Sykes J M, Doherty M.Interpretation of scanning kelvin probe potential maps for coated steel using semi-quantitative current density maps[J]. Corros. Sci., 2008, 50: 2773 | | [43] | Lyon S B, Bingham R, Mills D J.Advances in corrosion protection by organic coatings: What we know and what we would like to know[J]. Prog. Org. Coat., 2017, 102: 2 | | [44] | Blunden S, Wallace T.Tin in canned food: a review and understanding of occurrence and effect[J]. Food Chem. Toxi., 2003, 41: 1651 |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|