利用IRAS研究锌表面在湿干交替条件下的腐蚀行为

张学元;韩恩厚;Dan Persson

中科院金属所金属腐蚀与防护国家重点实验室

IN-SITU INFRARED REFLECTION ABSORPTION SPECTROSCOPY STUDIES OF CONFINED ZINC SURFACES EXPOSED UNDER PERIODIC WET-DRY CONDITIONS

Xueyun Zhang;Enhou Han;

中科院金属所金属腐蚀与防护国家重点实验室

全文: PDF(148 KB)

摘要: 设计了一套原位红外反射吸收电池,可以研究Zn在干湿交替条件下的腐蚀过程和溶液在Zn表面的挥发过程,结果表明溶液在Zn表面的挥发主要有三个阶段.局部Zn表面在1%NaCl溶液中浸泡1 h后在湿度为50%的净化空气中干燥23 h的周期性湿干交替试验,腐蚀产物主要是ZnO,腐蚀产物的量在初期随着周期(d)的增大而线性增加.在23 h 的干燥过程中,Zn的腐蚀速率随着干燥时间的增加而降低.

关键词 ：红外反射吸收光谱, 锌, 腐蚀

Abstract：In-situ infrared reflection absorption spectroscopy (IRAS) was a very powerful tool for studies of corrosion processes of the confi ned metals in the atmosphere.In this paper,an in-situ IRAS cell was set up and t he corrosion process of zinc and water evaporation in the drying process on the confined zinc surface exposure under periodic wet dry conditions was studied by in-situ IRAS.The water thickness on the confined surface of zinc could be calcul ated according to the optical index.The corrosion product formed in the initial stage of the confined zinc in the purified air with the relative humidity of 50% mainly was ZnO,The amount of corrosion product on the confined zinc surface inc reased linearly with day,the corrosion rate decreased with time during each dryi ng process.

Key words： infrared reflection absorption spectroscopy zinc corro sion

收稿日期: 2000-09-16

ZTFLH:

TG172

通讯作者: 张学元

Corresponding author: Xueyun Zhang

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张学元
	韩恩厚
	Dan Persson
44.8K

引用本文:

张学元; 韩恩厚; Dan Persson . 利用IRAS研究锌表面在湿干交替条件下的腐蚀行为[J]. 中国腐蚀与防护学报, 2002, 22(1): 32-36 .
Xueyun Zhang, Enhou Han. IN-SITU INFRARED REFLECTION ABSORPTION SPECTROSCOPY STUDIES OF CONFINED ZINC SURFACES EXPOSED UNDER PERIODIC WET-DRY CONDITIONS. J Chin Soc Corr Pro, 2002, 22(1): 32-36 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2002/V22/I1/32

[1]ZhuFeng.Atmosphericcorrosionofprecoatedsteelinaconfineden vironment[A].Stockholm:RoyalInstituteofTechnology,2000.
[2]ZhuF ,HedlundS ,ThierryD .Applicationofelectrochemicalimpedancespectroscopytostudytheperforationcorrosionofautomotivematerials[J],Br.Corros.J.,1996,31:113
[3]GamalAhmedE1-Mahdy,AtsushiNishikata,TooruTsuru.Elec trochemicalcorrosionmonitoringofgalvanizedsteelundercyclicwet-dryconditions[J].Corros.Sci.,2000,42:183
[4]PersssonD .Surfacefilmformationduringmetal-atmosphereinter action[A].Stockholm:RoyalInstituteofTechnology,1994.
[5]AastrupT ,PerssonD ,OdnevallWallinderI ,LeygrafC .Insituin fraredreflectionabsorptionspectroscopystudiesofsulfuriconplat inumandpalladium[J].J.Electrochem.Soc.,1998,145:487
[6]ZhuFeng,ZhangXueyuan,PerssonDan,ThierryDominique.Insituinfraredreflectionabsorptionspectroscopystudiesofconfinedzincsurfacesunderperiodicwet-dryconditions[J].ElectrochemicalandSolid-StateLetters,2001,4(5):B19-B22.
[7]PerssonD ,LeygrafC .Insituinfraredreflectionabsorptionspec troscopyforstudiesofatmosphericcorrosion[J].J .Electrochem.Soc.,1993,140:1256
[8]ZhuF ,PerssonD ,ThierryD ,TaxenC .Formationofcorrosionproductsonopenandconfinedzincsurfacesexposedtoperiodicwet dryconditions[J].Corrosion,tobepreparing
[9]WangGuangyong,WangHaijiang,LiXinglian,YinYaode.Corro sionandProtectionintheNaturalEnvironment[M ].Beijing:Chem icalIndustryHouse,1997.
(王光雍,王海江,李兴濂,银耀德.自然环境的腐蚀与防护[M ].北京:化学工业出版社,1997.)

[1]	师超,邵亚薇,熊义,刘光明,俞跃龙,杨志广,许传钦. 硅烷偶联剂改性磷酸锌对环氧涂层防腐性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 38-44.
[2]	赵书彦,童鑫红,刘福春,翁金钰,韩恩厚,郦晓慧,杨林. 环氧富锌涂层防腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 563-570.
[3]	赖德林,孔纲,车淳山. 硅酸盐封闭对TiO₂转化膜耐蚀性的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 607-614.
[4]	严寒, 赵晴, 杜楠, 胡彦卿, 王力强, 王帅星. 镀锌层三价铬钝化成膜过程及耐蚀性研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 547-553.
[5]	孟晓波,蒋武斌,廖永力,李锐海,郑志军,高岩. 输电杆塔材料在模拟工业环境中的大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 460-466.
[6]	牛振国, 郭浦山, 叶宏, 杨丽景, 许赪, 宋振纶. Zn-7Mg合金热处理显微组织演变及耐蚀性能研究[J]. 中国腐蚀与防护学报, 2017, 37(4): 347-353.
[7]	李庆鹏,许茜,刘建国,严川伟,张亮,殷跃军,韩长智. 水性无铬达克罗涂料的制备与性能研究[J]. 中国腐蚀与防护学报, 2016, 36(6): 559-565.
[8]	耿振伟,肖代红. Zn对挤压态Mg-13Gd-2Cu合金的显微组织及腐蚀性能影响[J]. 中国腐蚀与防护学报, 2016, 36(6): 595-603.
[9]	隋佳利,李相波,林志峰,詹天荣. 两种热喷涂锌铝涂层在低温海水介质中防腐性能研究[J]. 中国腐蚀与防护学报, 2016, 36(5): 471-475.
[10]	周兵, 唐囡, 张颖君, 毛亮, 王艳秋, 邵亚薇, 孟国哲. 镀锌钢表面高附着环氧清漆的研究[J]. 中国腐蚀与防护学报, 2015, 35(5): 455-460.
[11]	曾宪光,郑兴文,龚敏,范金龙,陈雪丹. 碳钢和镀锌钢在都江堰大气环境中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2015, 35(3): 271-278.
[12]	钟西舟, 王振尧, 刘艳洁, 王彬彬, 白芳, 窦志宏. 镀锌钢在模拟海洋大气环境下的腐蚀行为[J]. 中国腐蚀与防护学报, 2015, 35(2): 151-155.
[13]	郑敏聪, 李建华, 聂新辉, 李博文, 台闯. 镀锌钢接地材料在酸性土壤中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2015, 35(1): 27-32.
[14]	赵晓宏, 郭泉忠, 杜克勤, 郭兴华, 王勇. 不同涂层处理的汽车紧固件用ST12冷轧钢与SS400热轧钢的电偶腐蚀行为研究[J]. 中国腐蚀与防护学报, 2015, 35(1): 86-90.
[15]	海正银, 王辉, 辛长胜, 蔡敏, 秦博, 陈童. 加锌对690合金在高温水中形成的氧化膜的影响[J]. 中国腐蚀与防护学报, 2014, 34(6): 532-536.

Viewed

Full text

Abstract

Cited

Shared

Discussed