热处理对FeAl-Cr₃C₂复合涂层微观结构的影响

陈瑶¹,张洪华^1,²,杨干兰^1,²,向军淮^1,²(

)

1 江西科技师范大学材料与机电学院南昌 330013
2 江西科技师范大学江西省材料表面工程重点实验室南昌 330013

Influence of Heat Treatment on Microstructure of Composite Coatings of FeAl-Cr₃C₂

Yao CHEN¹,Honghua ZHANG^1,²,Ganlan YANG^1,²,Junhuai XIANG^1,²(

)

1 School of Materials and Mechanical & Electrical Engineering, Jiangxi Science and Technology Normal University, Nanchang 330013, China;
2 Jiangxi Key Laboratory of Surface Engineering, Jiangxi Science and Technology Normal University, Nanchang 330013, China

全文: PDF(924 KB) HTML

摘要:

利用超音速火焰喷涂 (HVOF) 方法在304钢上制备了厚度约为30 μm的Fe40Al-50%Cr₃C₂涂层,采用XRD,SEM/EDS分析其在阶梯温度退火后的微观结构演化行为。退火前涂层的表面十分粗糙,成分分布很不均匀,主要由Fe、Al和Fe-Al金属间化合物以及少量的Fe、Al的氧化物组成,涂层的最外层存在较多大块Fe颗粒,靠近基体部分存在少量的Al颗粒。经过真空退火处理之后,涂层的成分均匀性有了很大的改善,但是涂层中的一些孔洞依然存在。随着真空退火温度从700 ℃升高到900 ℃,涂层中大块Fe、Al颗粒逐渐消失,Fe、Al扩散反应更加充分,涂层中形成了更多的Fe-Al金属间化合物。

关键词 ：热喷涂, 退火, 金属间化合物

Abstract：

Composite coatings of Fe40Al-50%Cr₃C₂ with the thickness of 30 μm were prepared by high velocity oxygen-fuel (HVOF) technology on 304 steel. The change of its microstructure by heat treatment at different temperatures was studied by means of XRD and SEM/EDS. The surface of the coating is very rough and the element distribution is inhomogeneous before the heat treatment. The composition of the coating is mainly composed of Fe, Al, intermetallics plus a little oxide of Fe and Al. A large amount of particles of Fe with big size are present in the outer layer, while a few particles of Al are present in the inner layer. The homogeneity of the coating has great change after vacuum annealing, though some holes still exist in the coating. With the increase of the annealing temperature from 700 ℃ to 900 ℃, the pure Fe and Al particles of big size disappear gradually due to their full diffusion and thereby formation of more intermetallics.

Key words： thermal spraying anneal intermetallic

收稿日期: 2016-10-01

基金资助:江西省自然科学基金 (20132BAB206015和20122BAB216018) 及江西省教育厅科技研究青年基金(GJJ150811)

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	陈瑶
	张洪华
	杨干兰
	向军淮
44.8K

引用本文:

陈瑶,张洪华,杨干兰,向军淮. 热处理对FeAl-Cr₃C₂复合涂层微观结构的影响[J]. 中国腐蚀与防护学报, 2017, 37(1): 58-62.
Yao CHEN, Honghua ZHANG, Ganlan YANG, Junhuai XIANG. Influence of Heat Treatment on Microstructure of Composite Coatings of FeAl-Cr₃C₂. Journal of Chinese Society for Corrosion and protection, 2017, 37(1): 58-62.

链接本文:

https://www.jcscp.org/CN/10.11902/1005.4537.2016.193 或 https://www.jcscp.org/CN/Y2017/V37/I1/58

图1 热喷涂粉末及涂层的XRD谱

图2 Fe40Al-50%Cr3C2涂层在不同温度热处理前后的XRD谱

图3 喷涂态Fe40Al-50%Cr3C2涂层的表面形貌和面扫描元素分布图

图4 Fe40Al-50%Cr3C2涂层经不同温度热处理后表面和截面的SEM像

[1]	Chen Y, Chu M Y, Wang L J, et al.Microstructure and performance of Cr2AlC coatings deposited by HVOF spraying[J]. Chin. J. Rare Met., 2012, 36: 568
[1]	(陈洋, 储茂友, 王力军等. 超音速火焰喷涂制备Cr2AlC涂层组织性能研究[J]. 稀有金属, 2012, 36: 568)
[2]	Wang G, Miao D D, Xiao P, et al.Microstructure and corrosion behavior of Fe-based amorphous alloy coatings by high velocity oxy fuel spraying[J]. Funct. Mater., 2014, 45: 21123
[2]	(王刚, 缪丹丹, 肖平等. 超音速火焰喷涂制备Fe基非晶合金涂层的组织与腐蚀性能研究[J]. 功能材料, 2014, 45: 21123)
[3]	Zamanzade M, Vehoff H, Barnoush A.Effect of chromium on elastic and plastic deformation of Fe3Al intermetallics[J]. Intermetallics, 2013, 41: 28
[4]	Zhang H H, Xiang J H, Wang W, et al.High temperature oxidation of coatings prepared on Fe-15Cu-10Al alloys with controlled microstructures[J]. Adv. Sci. Lett., 2012, 14: 352
[5]	Lee S E, Jung S, Jang O J, et al.Oxidation behavior of Fe-15Cr-4Al alloy at high temperatures[J]. Sci. Adv. Mater., 2015, 7: 1475
[6]	Nakamura R, Takasawa K, Yamazaki Y, et al.Single-phase interdiffusion in the B2 type intermetallic compounds NiAl, CoAl and FeAl[J]. Intermetallics, 2002, 10: 195
[7]	Houngniou C, Chevalier S, Larpin J P.High-temperature-oxidation behavior of iron-aluminide diffusion coatings[J]. Oxid. Met., 2006, 65: 409
[8]	Xiang J H, Zhu X H, Chen G, et al.Oxidation behavior of Fe40AlxWC composite coatings obtained by high-velocity oxygen fuel thermal spray[J]. Trans. Nonferrous Met. Soc. China, 2009, 19: 1545
[9]	Guilemany J M, Cinca N, Dosta S, et al.High-temperature oxidation of Fe40Al coatings obtained by HVOF thermal spray[J]. Intermetallics, 2007, 15: 1384
[10]	Guilemany J M, Lima C R C, Cinca N, et al. Studies of Fe-40Al coatings obtained by high velocity oxy-fuel[J]. Surf. Coat. Technol., 2006, 201: 2072
[11]	Meng X J, Liu X B, Liu H Q, et al.Effects of heat treatment on microstructure and performance of NiCr/Cr3C2-WS2 composite coatings[J]. Trans. Mater. Heat Treat., 2013, 34(S2): 188
[11]	(孟祥军, 刘秀波, 刘海青等. 热处理对NiCr/Cr3C2-WS2复合涂层组织与性能的影响[J]. 材料热处理学报, 2013, 34(S2): 188)
[12]	Sun W C, Zhang F, Zhang P, et al.Influence of heat treatment on microstructure and wear resistance of HVOF WC-17Co coatings[J]. J. China Coal Soc., 2015, 40: 476
[12]	(孙万昌, 张峰, 张佩等. 热处理对HVOF WC-17Co涂层组织结构及耐磨性能的影响[J]. 煤炭学报, 2015, 40: 476)
[13]	Liu Q N, Liu Y, Li F, et al.Effect of heat treatment on micro-structure and wear behaviors of iron-base amorphous alloy coatings[J]. Mater. Sci. Eng. Powder Metall., 2012, 17: 586
[13]	(刘倩楠, 刘咏, 李飞等. 热处理对Fe基非晶合金涂层的相组成及摩擦磨损行为的影响[J]. 粉末冶金材料科学与工程, 2012, 17: 586)
[14]	Ma X, Li Q A, Jing X T.Influence of heat treatment on microstructure and corrosion resistance of Mg-10Gd-2.5Nd-0.5Zr alloy[J]. J. Chin. Soc. Corros. Prot., 2016, 36: 143
[14]	(马旭, 李全安, 井晓天. 热处理对Mg-10Gd-2.5Nd-0.5Zr合金组织和耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2016, 36: 143)
[15]	Fan Z S, Pan J G, Sun D B, et al.Influence of heat treatment on phase structure and wear characteristics of iron base amorphous alloy coatings[J]. Trans. Mater. Heat Treat., 2008, 29(1): 120
[15]	(樊自拴, 潘继岗, 孙冬柏等. 热处理对铁基非晶合金涂层相组成及磨损性能的影响[J]. 材料热处理学报, 2008, 29(1): 120)

[1]	张志英, 汤迦南, 余杰, 王旭东, 黄罗超, 邹俊文, 唐浩, 张继康, 陈亚涛, 程东鹏. 铜基非晶合金复合材料在NaCl溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 478-486.
[2]	隋佳利,李相波,林志峰,詹天荣. 两种热喷涂锌铝涂层在低温海水介质中防腐性能研究[J]. 中国腐蚀与防护学报, 2016, 36(5): 471-475.
[3]	李明菲,彭晓,王福会. 新型细晶Ni₃Al涂层的高温氧化行为[J]. 中国腐蚀与防护学报, 2011, 31(6): 414-418.
[4]	王帅波尹衍升刘涛滕少磊. 超疏水膜改性Fe₃Al在海水中的腐蚀行为[J]. 中国腐蚀与防护学报, 2009, 29(2): 137-140.
[5]	张仕臻; 郭建亭; 任维丽; 周文龙 . 稀土元素对NiAl/CrMo(Hf)共晶合金氧化性能影响[J]. 中国腐蚀与防护学报, 2005, 25(2): 110-114 .
[6]	孟凡军 . 高速电喷涂Fe-Al在800℃下的氧化性能[J]. 中国腐蚀与防护学报, 2004, 24(6): 368-371 .
[7]	李志林 . 电脉冲对不锈钢形变马氏体及其耐蚀性的影响[J]. 中国腐蚀与防护学报, 2004, 24(6): 372-375 .
[8]	沈勇 . 高铌TiAl基合金高温抗氧化性能研究[J]. 中国腐蚀与防护学报, 2004, 24(4): 203-207 .
[9]	张亦良; 王慕; 孙耀峰 . 用热喷涂技术防止湿硫化氢应力腐蚀[J]. 中国腐蚀与防护学报, 2003, 23(4): 243-247 .
[10]	胡津; 罗仁胜; 费维东 . 退火处理对SiCw/Al复合材料应力腐蚀开裂行为的影响*[J]. 中国腐蚀与防护学报, 1999, 19(5): 296-300 .
[11]	曾潮流; Rizzo.FC; 吴维tao . 两相NiAl-Fe金属间化合物的高温氧化行为研究[J]. 中国腐蚀与防护学报, 1999, 19(1): 39-44 .
[12]	唐兆麟;王福会;吴维. TiAlCr涂层对TiAl金属间化合物抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 1998, 18(1): 35-40.
[13]	唐兆麟;王福会;吴维. TiAl金属间化合物的熔盐热腐蚀行为[J]. 中国腐蚀与防护学报, 1997, 17(3): 233-237.
[14]	徐颂波;陈俊明. Ni_3Al(B)系金属间化合物在Li_2CO_3-K_2CO_3熔盐中的腐蚀电化学行为[J]. 中国腐蚀与防护学报, 1995, 15(3): 161-166.
[15]	陈俊明;徐颂波. Ni_3Al(B)系金属间化合物在LiCl-KCl熔盐中的腐蚀电化学行为[J]. 中国腐蚀与防护学报, 1995, 15(3): 167-172.

Viewed

Full text

Abstract

Cited

Shared

Discussed