暴露1年的耐大气腐蚀用钢表面锈层分析

中国腐蚀与防护学报

2001, Vol. 21

Issue (5): 297-300

研究报告

本期目录 | 过刊浏览

暴露1年的耐大气腐蚀用钢表面锈层分析

张全成;吴建生;陈家光

上海交通大学材料学院

ANALYSIS ON THE CORROSION RUST OFWEATHERING STEEL EXPOSED IN ATMOSPHERE

;;

上海交通大学材料学院

全文: PDF(120 KB)

摘要: 测量了碳钢和耐候钢在上海地区大气中的腐蚀速率，分析测定了锈层的相组成以及合金元素的分布.结果表明，腐蚀1年的碳钢表面锈层没有分层现象，且锈层中存在着较多的孔洞和裂纹；耐候钢的表面锈层已经产生了明显的分层现象，内锈层主要有α-FeOOH和γ-FeOOH 构成，外锈层有γ-FeOOH和FeO构成.在内锈层中存在着裂纹，裂纹处产生了Cr元素的富集现象.

关键词 ：大气腐蚀, 耐候钢, 内锈层, FeOOH

Abstract：Corrosion of carbon steel and the weathering steel in marine atmosphere during different time was compared,the morphology of rust layer was observed,and the distribution of the alloy elements in the rus t layer was determined.The results show that corrosion rust of weathering steel exposed in the atmosphere for 1 year consisted of inner layer and outer layer ob viously, the former is composed of α-FeOOH mainly,and the latter is of α-FeO OH and a little FeO.There are some cracks distributed in the inner layer,where contains richer alloy elements compared to the substrate steel.

Key words： atmospheric corrosion weathering steel inner rust laye r FeOOH

收稿日期: 2000-04-24

ZTFLH:

TG172.3+1

通讯作者: 张全成 E-mail: zhangquancheng@sohu.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张全成
	吴建生
	陈家光
44.8K

引用本文:

张全成; 吴建生; 陈家光 . 暴露1年的耐大气腐蚀用钢表面锈层分析[J]. 中国腐蚀与防护学报, 2001, 21(5): 297-300 .

链接本文:

https://www.jcscp.org/CN/Y2001/V21/I5/297

[1]VaccariJohnA .Weathingresistanceofironandsteels[J].MaterialsEngineering(Cleveland),1974,79:60～63
[2]JohnsonJB ,ElliottP ,etal.Short-termatmosphericcorrosionofsteelattwoweatherandpollutionmonitoredsites[J].Corro sionScience,1997,17:691～700
[3]SouthwellCR ,BultmanJD ,etal.Corrosionofmetalsintropicalenvironments[A].EmDashFinalReportof16-yearExpo sures
[4]LiangCF ,HouWT .Theinfluenceofalloyingelementsontheatmosphericcorrosionresistanceofcarbonsteelandlowalloysteel[J].JournalofChineseSocietyforCorrosionandProtection,1997,17:87～92(梁彩凤,候文泰.合金元素对碳钢和低合金钢在大气中耐腐蚀性的影响[J].中国腐蚀与防护学报,1997,17:87～92)
[5]KaescheH .MetallicCorros.[M ].Berlin,Germany:NationalAssociationofCorrosionEngineers,1985:8
[6]WangXY ,WangGY ,etal.Theinfluenceofenvironmentelementsontheatmosphericcorrosionofcarbonsteelandlowalloysteel[J].JournalofChineseSocietyforCorrosionandProtection,1995,15:124～127(汪轩义,王光雍等.环境因素对碳钢和低合金钢大气腐蚀的影响[J].中国腐蚀与防护学报,1995,15:124～127)
[7]HouWY ,YuJD ,etal.Theatmosphericcorrosionofcarbonsteelandlowalloysteel[J].JournalofChineseSocietyforCorrosionandProtection,1993,13:291～301(候文泰,于敬敦等.碳钢及低合金钢的大气腐蚀[J].中国腐蚀与防护学报,1993,13:291～301)
[8]YamashitaM ,MiyukiH ,etal.Thelongtermgrowthoftheprotecturerustlayerformedonweatheringsteelbyatmospherecor rosionduringaquarterofacenter[J].Br.Corro.J.,1994,2:283
[9]SeiJOh,CookDC ,TownsendHE .Atmosphericcorrosionofdifferentsteelsinmarine、ruralandindustrialenvironments[J].CorrosionScience,1998,41:1687～1702
[10]KaescheH .MetallicCorros.[M].Berlin,Germany:NationalAssociationofCorrosionEngineers,1985:8～9

[1]	范益,陈林恒,蔡佳兴,代芹芹,马宏驰,程学群. 热轧AH36船板钢在室内仓储条件下的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 10-16.
[2]	潘成成,马超,夏大海. EBSD技术研究金属材料晶体取向对大气腐蚀萌生的影响机理[J]. 中国腐蚀与防护学报, 2019, 39(6): 495-503.
[3]	赵晋斌,赵起越,陈林恒,黄运华,程学群,李晓刚. 不同表面处理方式对300M钢在青岛海洋大气环境下腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 504-510.
[4]	邓俊豪,胡杰珍,邓培昌,王贵,吴敬权,王坤. 氧化皮对SPHC热轧钢板在热带海洋大气环境中初期腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 331-337.
[5]	孙永伟,钟玉平,王灵水,范芳雄,陈亚涛. 低合金高强度钢的耐模拟工业大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 274-280.
[6]	王力, 郭春云, 肖葵, 吐尔逊·斯拉依丁, 董超芳, 李晓刚. Q235和Q450钢在吐鲁番干热大气环境中长周期暴晒时的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 431-437.
[7]	王越, 刘子利, 刘希琴, 章守东, 田青超. 热轧态Cr、Ni微合金化高强度耐候钢组织与耐蚀性能[J]. 中国腐蚀与防护学报, 2018, 38(1): 39-46.
[8]	王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO₃溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[9]	张新新,高志明,胡文彬,伍志鹏,韩连恒,卢丽花,修妍,夏大海. Q235钢在薄液膜下腐蚀行为与图像信息的相关性研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 444-450.
[10]	张鑫,戴念维,杨燕,张俊喜. 模拟工业环境下直流电场对金属Zn腐蚀机理的影响[J]. 中国腐蚀与防护学报, 2017, 37(5): 451-459.
[11]	孟晓波,蒋武斌,廖永力,李锐海,郑志军,高岩. 输电杆塔材料在模拟工业环境中的大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 460-466.
[12]	谭何灵,周成,刘希辉,曹国明,张菁. Cr对Q420钢在高盐度大气环境下耐蚀性的影响[J]. 中国腐蚀与防护学报, 2017, 37(3): 267-372.
[13]	孙霜青,郑弃非,李春玲,王秀民,胡松青. 腐蚀产物对纯Al 8A06长期大气腐蚀行为影响的研究[J]. 中国腐蚀与防护学报, 2017, 37(2): 110-116.
[14]	张飘飘,杨忠民,陈颖,王慧敏. 含铬耐候钢在模拟海洋大气环境中的腐蚀行为[J]. 中国腐蚀与防护学报, 2017, 37(2): 93-100.
[15]	白子恒,黄运华,李晓刚,杨浪,董超芳,颜利丹,肖葵. 硫硼酸阳极氧化处理的7050铝合金在工业海洋大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(6): 580-586.

Viewed

Full text

Abstract

Cited

Shared

Discussed