西部地区水工混凝土长期腐蚀产物与腐蚀机理

高小建;马保国;赵志曼

武汉理工大学硅酸盐材料工程教育部重点实验室

ON ATTACK PRODUCT AND CORROSION MECHANISM OF HYDRAULIC CONCRETE AFTER LONG-TERM EXPOSURE TO NATURAL ENVIRONMENT IN WESTERN CHINA

Xiaojian Gao;Baoguo Ma;

武汉理工大学硅酸盐材料工程教育部重点实验室

全文: PDF(153 KB)

摘要: 对西部某水坝廊道运行6年的混凝土受腐蚀状况进行调研、取样，采用XRD、SEM、EDAX和激光Raman光谱等方法进行分析.结果表明，低温、高湿、硫酸盐和碳酸盐长期共同作用下混凝土的腐蚀产物是由硅灰石膏、钙矾石、石膏和方解石组成的一种稀泥状混合物.证实了在我国西部水工环境下混凝土可能发生TSA硫酸盐侵蚀，并探讨了这种侵蚀的发生机理.

关键词 ：混凝土坝, 硫酸盐, 碳酸盐, TSA侵蚀, 西部地区

Abstract：A site investigation was made on one deteriorated concrete with 6 year s age,and this concrete component was located in one tunnel of one concrete dam in Western China.Some samples were taken from the attacked concrete and were a nalyzed with XRD,SEM-EDAX and Laser Raman Spectroscopy methods.As a result,it is shown that a mushy mixture consisting of thaumasite,ettringite,gypsum and calcite occurs in the residual concrete exposed to low temperature,high humidit y,sulfate and carbonate for a long time.It is validated that the thaumasite fo rm of sulfate attack may occur in hydraulic concrete structures in Western China .In addition,the corrosion mechanism is also discussed.

Key words： concrete dam sulfate carbonate thaumasite form of sulfate attack Western China

收稿日期: 2004-03-26

ZTFLH:

TU528

通讯作者: 高小建 E-mail: xjgao2002@yahoo.com.cn

Corresponding author: Xiaojian Gao E-mail: xjgao2002@yahoo.com.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	高小建
	马保国
	赵志曼
44.8K

引用本文:

高小建; 马保国; 赵志曼 . 西部地区水工混凝土长期腐蚀产物与腐蚀机理[J]. 中国腐蚀与防护学报, 2005, 25(5): 299-302 .
Xiaojian Gao, Baoguo Ma. ON ATTACK PRODUCT AND CORROSION MECHANISM OF HYDRAULIC CONCRETE AFTER LONG-TERM EXPOSURE TO NATURAL ENVIRONMENT IN WESTERN CHINA. J Chin Soc Corr Pro, 2005, 25(5): 299-302 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I5/299

[1]Thaumasite Expert Group.The Thaumasite Form of Sulfate At-tack:Risks,Diagnosis,Remedial Works and Guidance on New Con-struction[R].London:Department of the Environment,Transportand the Regions,1999
[2]Norah C.The occurrence of thaumasite in modern construction-areview[J].Cem.Concr.Composites,2002,24(4):393-402
[3]Wang Z F.Sulfate attack and protection of hydraulic concrete[J].Northwest Water Power,1994,(2):34-43(王再芳.水工混凝土硫酸盐侵蚀与防护[J].西北水电,1994,(2):34-43)
[4]Romer M,Holzer L,Pfiffner M.Swiss tunnel structures:concretedamage by formation of thaumasite[J].Cem.Concr.Composites,2003,25(8):1111-1117
[5]Hartshorn S A,Sharp J H,Swamy R N.Thaumasite formation inPortland-limestone cement pastes[J].Cem.Concr.Res.,1999,29(8):1331-1340
[6]Yu H F,Sui W,et al.On attack product and corrosion mechanism ofordinarily concrete after long term exposure to salt lakes[J].J.Chin.Ceramic Soc.,2003,31(5):434-440(余红发,孙伟等.盐湖地区混凝土的长期腐蚀产物与腐蚀机理[J].硅酸盐学报,2003,31(5):434-440)
[7]Irassar E F,Bonavetti V L,González M.Microstructural study ofsulfate attack on ordinary and limestone Portland cements at ambi-ent temperature[J].Cem.Concr.Res.,2003,33(1):31-41
[8]Sahu S,Exline D L,Nelson M P.Identification of thaumasite in con-crete by Raman chemical imaging[J].Cem.Concr.Composites,2002,24(3):347-350
[9]Brough A R,Atkinson A.Micro-Raman spectroscopy of thauma-site[J].Cem.Concr.Res.,2001,31(3):421-424

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[3]	陈旭, 李帅兵, 郑忠硕, 肖继博, 明男希, 何川. X70管线钢在大庆土壤环境中微生物腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 175-181.
[4]	陈旭,马炯,李鑫,吴明,宋博. 温度与SRB协同作用下X70钢在海泥模拟溶液中应力腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 477-483.
[5]	戚鹏, 万逸, 曾艳, 郑来宝, 张盾. 海洋环境中硫酸盐还原菌的快速测定方法研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 387-394.
[6]	吴堂清,周昭芬,王鑫铭,张德闯,尹付成,孙成. 微生物致裂的热力学和动力学分析[J]. 中国腐蚀与防护学报, 2019, 39(3): 227-234.
[7]	李鑫,陈旭,宋武琦,杨佳星,吴明. pH值对X70钢在海泥模拟溶液中微生物腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 565-572.
[8]	管方, 翟晓凡, 段继周, 侯保荣. 阴极极化对硫酸盐还原菌腐蚀影响的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(1): 1-10.
[9]	于利宝, 闫茂成, 王彬彬, 舒韵, 许进, 孙成. 酸性土壤环境中Q235钢的微生物腐蚀行为[J]. 中国腐蚀与防护学报, 2018, 38(1): 10-17.
[10]	梅朦, 郑红艾, 陈惠达, 张鸣, 张大全. 硫酸盐还原菌对Cu在循环冷却水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 533-539.
[11]	杜开发,王彬,甘复兴,汪的华. 铜锡合金阳极在熔融碳酸盐中氧化膜的形成及其防护性能[J]. 中国腐蚀与防护学报, 2017, 37(5): 421-427.
[12]	滕彧,陈旭,何川,王义闯,王冰. 显微组织对X70钢在含有硫酸盐还原菌的3.5%NaCl溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(2): 168-174.
[13]	吕亚林,郑碧娟,刘宏伟,熊福平,刘宏芳,胡裕龙. 磁场对硫酸盐还原菌生物膜在304不锈钢表面吸附性能的影响[J]. 中国腐蚀与防护学报, 2016, 36(6): 652-658.
[14]	罗金恒,胥聪敏,杨东平. SRB作用下X100管线钢在酸性土壤环境中的应力腐蚀开裂行为[J]. 中国腐蚀与防护学报, 2016, 36(4): 321-327.
[15]	宋博强,陈旭,马贵阳,刘睿. SRB对X70管线钢在近中性pH溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(3): 212-218.

Viewed

Full text

Abstract

Cited

Shared

Discussed