7075铝合金氢脆敏感性与Mg-H相互作用

张宇,宋仁国,唐普洪

浙江工业大学机械制造及自动化教育部重点实验室杭州 310014

HYDROGEN EMBRITTLEMENT SUSCEPTIBILITY AND Mg-H INTERACTION IN 7075 ALUMINUM ALLOY

ZHANG Yu, SONG Renguo, TANG Puhong

Key Laboratory of Mechanical Manufacture and Automation of Ministry of Education, Zhejiang University of Technology, Hangzhou 310014

全文: PDF(1425 KB)

摘要: 利用阴极渗氢法、定氢仪、电子拉伸实验机、能谱（EDS）和扫描电镜（SEM）等方法研究了“双峰”时效下7075铝合金的晶界偏析行为、氢脆（HE）敏感性以及Mg-H相互作用。结果表明：充氢前后合金的强度等性能具有时效“双峰”特征；第二峰处合金强度的下降量明显比第一峰的小，且第二峰时合金具有高强、低HE敏感性等优异性能；在阴极渗氢过程中Mg与H之间存在着相互作用。最后，对Mg-H相互作用机制进行了探讨。

关键词 ： 7075铝合金, 晶界偏析, 氢脆, Mg-H相互作用

Abstract：Grain boundary segregation, hydrogen embrittlement susceptibility and Mg-H interaction of 7075 aluminum alloys with double-peak aged were studied by means of cathodic H-permeation, hydrogen determinator, electronic tensile machine， energy dispersive X-ray spectrometer (EDS) and scanning electron microscopy (SEM). The results showed that both before and after hydrogen charging, the strength and etc. all had double peaks; the decline of second peak strength was smaller than the first peak, also it had excellent performance like high-strength and low- HE-susceptibility at the second peak; there may exist Mg-H interaction during the hydrogen charging process. Finally, the Mg-H interaction mechanism is discussed.

Key words： 7075 aluminum alloy grain boundary segregation hydrogen embrittlement Mg-H interaction

收稿日期: 2009-08-11

ZTFLH:

TG178

基金资助:

国家自然科学基金项目(50771093)资助

通讯作者: 宋仁国 E-mail: songrg@hotmail.com

Corresponding author: SONG Renguo E-mail: songrg@hotmail.com

作者简介: 张宇，男，1985年生，硕士生，研究方向为7xxx系铝合金和金属表面处理

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张宇
44.8K

引用本文:

张宇,宋仁国,唐普洪. 7075铝合金氢脆敏感性与Mg-H相互作用[J]. 中国腐蚀与防护学报, 2010, 30(5): 364-368.
ZHANG Yu. HYDROGEN EMBRITTLEMENT SUSCEPTIBILITY AND Mg-H INTERACTION IN 7075 ALUMINUM ALLOY. J Chin Soc Corr Pro, 2010, 30(5): 364-368.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2010/V30/I5/364

[1] Song R G, Zeng M G,Zhang J B. Investigation of relation between grain boundary segregation and behavior of stress corrosion and corrosion fatigue in7075 aluminium alloy [J]. J. Chin. Soc. Corros. Prot., 1996, 16(1): 1-8 (宋仁国, 曾梅光, 张金宝. 7050铝合金晶界偏析与应力腐蚀、腐蚀疲劳行为的研究 [J]. 中国腐蚀与防护学报, 1996, 16(1): 1-8) [2] Ashish Thakur, Raman R, Malhotra S N. Hydrogen embrittlement studies of aged and retrogressed-reaged Al-Zn-Mg alloys [J]. Mater. Chem.Phys., 2007, 101: 441-447 [3] Takano N. Hydrogen diffusion and embrittlement in 7075 aluminum alloy [J]. Mater. Sci. Eng., 2008, A 483-484: 336-339 [4] Song R G, Zeng M G. Hydrogen embrittlement of high strength aluminium alloys [J]. Mater. Sci. Eng., 1995, 13(1): 63-65 (宋仁国, 曾梅光. 高强度铝合金的氢脆 [J]. 材料科学工程,1995, 13(1): 63-65) [5] Song R G, Tseng M K, Zhang B J, et al. Grain boundary segregation and hydrogen-induced fracture in 7050 aluminum alloys [J]. Acta Metall.Mater., 1996, 45: 84-89 [6] Yan D J. Analysis about strengthening mechanism from the ageing process of 7475 Al alloy [J]. J. Mater.Eng., 1991, 2(7): 15-20 (阎大京. 从7475铝合金的时效看Al-Zn-Mg-Cu系合金的强化 [J]. 材料工程, 1991, 2(7): 15-20) [7] Song R G, Zhang J B, Zeng M G. Investigation of stress corrosion susceptibility for 7175 aluminiun alloy double peak aged [J]. Trans. Met. Heat Treat., 1996, 17(2): 51-54 (宋仁国, 张宝金, 曾梅光等. 7175铝合金时效“双峰”应力腐蚀敏感性的研究 [J]. 金属热处理学报, 1996, 17(2): 51-54\par

[1]	赵东杨, 周宇, 王冬颖, 那铎. 磷化处理对核主泵螺栓断裂行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 539-544.
[2]	张琦超, 黄彦良, 许勇, 杨丹, 路东柱. 高放射性核废料钛储罐深地质环境中氢吸收及氢脆研究进展[J]. 中国腐蚀与防护学报, 2020, 40(6): 485-494.
[3]	周宇, 张海兵, 杜敏, 马力. 模拟深海环境中阴极极化对1000 MPa级高强钢氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 409-415.
[4]	赵晋斌,赵起越,陈林恒,黄运华,程学群,李晓刚. 不同表面处理方式对300M钢在青岛海洋大气环境下腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 504-510.
[5]	任建平,宋仁国. 双级时效对7050铝合金力学性能及氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 359-366.
[6]	童海生,孙彦辉,宿彦京,庞晓露,高克玮. 海工结构用2205双相不锈钢氢致开裂行为研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 130-137.
[7]	柯书忠, 刘静, 黄峰, 王贞, 毕云杰. 预应变对DP600钢氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2018, 38(5): 424-430.
[8]	李腾, 金伟良, 许晨, 毛江鸿. 电化学修复过程中钢筋析氢稳态临界电流密度测定实验方法[J]. 中国腐蚀与防护学报, 2017, 37(4): 382-388.
[9]	刘德强,柯黎明,徐卫平,邢丽,毛育青. 7075厚板铝合金搅拌摩擦焊接头晶间腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(3): 293-299.
[10]	王廷勇,马兰英,汪相辰,张海兵,陈凯,闫永贵. 某核电站凝汽器在海水中阴极保护参数的研究及应用[J]. 中国腐蚀与防护学报, 2016, 36(6): 624-630.
[11]	张体明, 赵卫民, 郭望, 王勇. 阴极保护下X65钢在模拟海水中的氢脆敏感性研究[J]. 中国腐蚀与防护学报, 2014, 34(4): 315-320.
[12]	郝文魁, 刘智勇, 张新, 杜翠薇, 李晓刚, 刘翔. H₂S浓度对35CrMo钢应力腐蚀开裂的影响[J]. 中国腐蚀与防护学报, 2013, 33(5): 357-362.
[13]	李成杰,杜敏. 深海钢铁材料的阴极保护技术研究及发展[J]. 中国腐蚀与防护学报, 2013, 33(1): 10-16.
[14]	林召强,马力,闫永贵. 阴极极化对高强度船体结构钢焊缝氢脆敏感性的影响[J]. 中国腐蚀与防护学报, 2011, 31(1): 46-50.
[15]	栾国红,付瑞东,董春林,何淼,康举. 中性盐雾下7075铝合金搅拌摩擦焊焊缝的腐蚀行为[J]. 中国腐蚀与防护学报, 2010, 30(3): 236-240.

Viewed

Full text

Abstract

Cited

Shared

Discussed