中国腐蚀与防护学报  2007, Vol. 27 Issue (5): 309-314     
  综述 本期目录 | 过刊浏览 |
热障涂层的性能评价
李美姮;管恒荣
RECENT DEVELOPMENT OF PERFORMANCE VALUATION ON THERMAL BARRIER COATINGS
;
全文: PDF(358 KB)  
摘要: 热障涂层用于涡轮发动机的热端部件可显著提高其使用温度,延长部件的使用寿命,并提高发动机的效率。文中对热障涂层的力学性能、抗氧化和抗热腐蚀、抗磨蚀和热学特性等性能的评价及性能判断与分析进行了综合回顾。
关键词 热障涂层隔热效果力学性能抗氧化抗磨蚀    
Abstract:Thermal barrier coatings (TBCs) have been increasingly used to extend the durability of aircraft gas turbine engine.This not only increases components lifetime,but also allows higher engine temperatures and there-fore better efficiency.The performance valuation and analysis was reviewed to the mechanics property,oxidation resistance, hot corrosion resistance, erosion resistance, and thermal property of thermal barrier coatings.
Key wordsthermal barrier coatings    thermal barrier effect    mechanical performance    oxidation resistance    ero-sio
收稿日期: 2006-02-20     
ZTFLH:  TG174.45  

引用本文:

李美姮; 管恒荣 . 热障涂层的性能评价[J]. 中国腐蚀与防护学报, 2007, 27(5): 309-314 .
. RECENT DEVELOPMENT OF PERFORMANCE VALUATION ON THERMAL BARRIER COATINGS. J Chin Soc Corr Pro, 2007, 27(5): 309-314 .

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2007/V27/I5/309

[1]Padture N P,Gell M,Jordan E H.Thermal barrier coatings forgas-turbine engine applications[J].Science,2002,296:280-284
[2]Xu H B,Gong S K,Liu F S.Recent development in materialsdesign of thermal barrier coatings for gas turbine[J].Acta Aero-nautica et Astronautica Sinica,2000,21(1):7-12(徐惠彬,宫声凯,刘福顺.航空发动机热障涂层材料体系的研究[J].航空学报,2000,21(1):7-12)
[3]Liu F S,Gong S K,Xu H B.Recent development in thermal bar-rier coatings prepared by EB-PVD[J].Acta Aeronautica et As-tronautica Sinica,2000,21(Supl.):30-34(刘福顺,宫声凯,徐惠彬.大功率EB-PVD陶瓷热障涂层的研究与应用[J].航空学报,2000,21(增刊):30-34)
[4]Li M F,Zhu J C,Xiang X H.et al.Progress in study on ceram-ic/metal high-temperature thermal barrier coatings[J].Mater.Rev.,2000,14(8):19-21(李明伟,朱景川,向兴华等.陶瓷/金属高温热障涂层研究进展[J].材料导报.2000,14(8):19-21)
[5]Zeng Z H,Guo Z,Wu S J.Functionally gradient material and itsdevelopment status and trend[J].Missiles and Space Vehicles,1996,220:60-67(曾昭焕,郭正,巫世杰.梯度功能材料及其研究现状与发展趋势[J].导弹与航天运载技术,1996,220:60-67)
[6]Hu C S,Wang F H,Wu W T.Review of progress in thermal bar-rier coatings[J].Corro.Sci.Prot.Technol.,2000,12(3):160-163(胡传顺,王福会,吴维.热障涂层研究进展[J].腐蚀科学与山文防护技术,2000,12(3):160-163)
[7]Dapkunas S J.Measurement methods and standards for processingand application of thermal barrier coatings[J].J.Thermal SprayTechnol.,1997,6(1):67-76
[8]BerndtCC.Tensileadhesiontestingmethodologyforthermallysprayedcoatings[J].J.Mater.Eng.,1990,12:151-158
[9]Berndt C C,Lin C K.Measurement of adhesion for thermally sprayedmaterials[J].J.Adhes.Sci.Technol.,1993,7:1235-1264
[10]Lhermitte-Sebire I,Colmet R,Naslain R.The adhesion betweenphysically vapour-deposited or chemically vapour-deposited alumi-na and TiC-coated cemented carbides as characterized by Augerelectron spectroscopy and scratch testing[J].Thin Solid Films,1986,138:221-233
[11]Steinmann P A,Tardy Y,Hintermann H E.Adhesion testing bythe scratch test method:The influence of intrinsic and extrinsic pa-rameters on the critical load[J].Thin Solid Films,1987,154:333-349
[12]Burnett P J,Rickerby D S.The relationship between hardnessand scratch adhesion[J].Thin Solid Films,1987,154:403-416
[13]Bull S J.Failure modes in scratch adhesion testing[J].Surf.Coat.Technol.,1991,50:25-32
[14]Jindal P C,Quinto D T,Wolfe G J.Adhesion measurements ofchemically vapor deposited and physically vapor deposited hardcoatings on WC-Co substrates[J].Thin Solid Films.1987,154:361-375
[15]Loubet J L.Boron-carbide coatings-correlation between mechan-ical-properties and LPCVD parameters values[A].In:Proc.16thLeeds-Lyon Symp.[C].On Tribo.,Dowson D,Taylor C M,GodetM,eds.,held at the Inst.Nation.Des Sci.Appl.,Lyon,France,1989,429
[16]Oliver W C,Pharr G M.An improved technique for determininghardness and elastic-modulus using load and displacement sensingindentation experiments[J].J.Mater.Res.,1992,7:1564-1583
[17]Marshall D B,Noma T,Evans A G.A simple method for deter-mining elastic-modulus to hardness ratios using Knoop indentationmeasurements[J].J.Am.Ceram.Soc.,1982,65:C175-176
[18]Fawcett N.A novel method for the measurement of Young's mod-ulus for thick-film resistor material by flexural testing of coatedbeams[J].Mater.Sci.Technol.,1998,9:2023-2026
[19]Chantikul P,Anstis G R,Lawn B R,et al.A critical evaluationof indentation techniques for measuring fracture toughness 2.Strength method[J].J.Am.Ceram.Soc.,1981,64:539-543
[20]Anstis G R,Chantikul P,Lawn B R,et al.A critical evaluationof indentation techniques for measuring fracture toughness 1.Directcrack measurements[J].J.Am.Ceram.Soc.,1981,64:533-538
[21]Shih T T.An evaluation of the chevron V-notched bend bar frac-ture toughness specimen[J].Engingeering Fracture Mechanics,1981,14(4):821-828
[22]Williams D P,Evans A G.A simple method for studying slow crackgrowth[J].J.Test.Eval.,1973,1(4):264-270
[23]Reece M J,Guiu F,Sammur M F R.Cyclic fatigue crack propa-gation in alumina under direct tension compression loading[J].J.Am.Ceram.Soc.,1989,72(2):348-352
[24]Suresh S.Mechanics and micromechanisms of fatigue crack-growthin brittle solids[J].Int.J.Fracture,1990,42(1):41-56
[25]ASTMStandard E399-74:Standard Method ofTest for Plane-StrainFracture Toughness of Metallic Materials[S].American Society ofTesting Materials,1974
[26]Simpson L A.Use of the notched-beam test for evaluation of frac-ture energies of ceramics[J].J.Am.Ceram.Soc.,1974,57:151-154
[27]GB4161-84:Chinese National Standard.Test Method forPlane-strain Fracture Toughness[S].Beijing:Standards Press ofChina,1985(GB4161-84.金属材料平面应变断裂韧度试验方法[S].北京:中国标准出版社,1985)
[28]Li M H,Sun X F,Gong S K,et al.Studies of microstructure andphase of EB-PVD TBCs exposed to elevated temperatures[J].J.Chin.Soc.Corros.Prot.,2002,22(2):105-110(李美女亘,孙晓峰,宫声凯.EB-PVD热障涂层高温氧化过程中的显微结构和相分析[J].中国腐蚀与防护学报,2002,22(2):105-110)
[29]Li M H,Zhang Z Y,Sun X F,et al.Oxidation behavior of sput-tered NiCrAlY coating[J].Surf.Coat.Technol.,2003,165:241-247
[30]Li M H,Zhang Z Y,Sun X F,et al.Oxidation and degradation ofEB-PVD thermal-barrier coatings[J].Oxidation of Metals,2002,58(5/6):499-512
[31]Li M H,Sun X F,Gong S K,et al.Phase transformation andbond coat oxidation behavior of EB-PVD thermal barrier coating[J].Surf.Coat.Technol.,2004,176:209-214
[32]Wu Y N,Wang F H,Huang W,et al.Oxidation behavior ofthermal barrier coatings obtained by detonation spraying[J].Surf.Coat.Technol.,2003,166:189-194
[33]Tolpygo V K,Clarke D R.Morphological evolution of thermal bar-rier coatings induced by cyclic oxidation[J].Surf.Coat.Technol.,2003,163-164:81-86
[34]Zhang D B,Gong S K,Xu H B,et al.Thermal cycling behaviorsof TBC on intermetallic Ni3Al based superalloy[J].Surf.Coat.Technol.,2003,168:78-83
[35]Miller R A,Lissler G W,Jobe J M.A hot dynamic seal rig formeasuring hypersonic engine seal durability and flow performancetechnical[J].NASA Lewis Research Center,1993,3295
[36]Jones R L.Experiences in seeking stabilizers for zirconia havinghot corrosion-resistance and high temperature tetragonal(t')sta-bility[P].NRL/MR/6170-96-7841,1996
[37]Roark R J,Young W C.Formulas for Stress and Strain[M].NewYork:McGraw-Hill Book Company,1982:516
[38]Rhys-Jones T,Toriz F C.Thermal barrier coatings for turbine ap-plications in aero engines[J].High Temperature Technology,1989,7(2):73-81
[39]Tabakoff W.Investigation of coatings at high temperature for usein turbomachinery[J].Surf.Coat.Technol.,1989,39/40:97-115
[40]Hanschuh R F.High temperature erosion of plasma sprayed par-tially stabilized zirconia in a simulated turbine environment[J].NASA,TP2406,Dec.1984
[41]Toriz F C,Thakker A B,Gupta S K.Thermal barrier coatings forjet engines[J].ASME,88-GT-279
[42]Davis A G,Boone D H,Levy AV.Erosion of ceramic thermalbarrier coatings[J].Wear,1986,110(2):101-116
[43]Eaton H E,Novak R C.Particulate erosion of plasma sprayed porousceramic[J].Surf.Coat.Technol.,1987,30:41-50
[44]Nicholls J R,Jaslier Y,Rickerby D S.Erosion and foreign objectdamage of thermal barrier coatings[J].Mater.Sci.Forum,1997,251-254:935-948
[45]Andersson C A,Lau S K,et al.Advanced ceramic coating devel-opment for industrialatility gas turbine applications[A].NASACR-165619,Final Report[C].1982:12
[46]Zhu D,Miller R A,Nagaraj B A,et al.Thermal conductivity ofEB-PVD thermal barrier coatings evaluated by a steady-state laserheat flux technique[J].Surf.Coat.Technol.,2001,138:1-8
[1] 余春堂,阳颖飞,鲍泽斌,朱圣龙. 先进高温热障涂层用高性能粘接层制备及研究进展[J]. 中国腐蚀与防护学报, 2019, 39(5): 395-403.
[2] 艾鹏,刘礼祥,李晓罡,姜文涛. TiAlSiN涂层对γ-TiAl基合金抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 306-312.
[3] 虞礼嘉,梁文萍,林浩,缪强,黄彪子,崔世宇. 激光重熔YSZ热障涂层950 ℃的热腐蚀行为[J]. 中国腐蚀与防护学报, 2019, 39(1): 77-82.
[4] 陈磊,裴志亮,肖金泉,宫骏,孙超. 磁过滤电弧离子镀制备TiAlN涂层的结构与性能表征[J]. 中国腐蚀与防护学报, 2017, 37(3): 241-246.
[5] 王喜忠,吴建颢,彭徽,郭洪波,宫声凯. 电子束物理气相沉积La2Ce2O7热障涂层的高温燃气热腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(1): 36-40.
[6] 李新慧,马文,尹轶川,马伯乐,白玉,贾瑞灵,董红英. 液相等离子喷涂SrZrO3热障涂层工艺的研究[J]. 中国腐蚀与防护学报, 2017, 37(1): 41-46.
[7] 蔡丽丽,马文,李新慧,尹轶川,马伯乐,白玉,王俊,董红英. (Gd0.7Sr0.3)ZrO3.35涂层的CaO-MgO-Al2O3-SiO2(CMAS) 腐蚀行为[J]. 中国腐蚀与防护学报, 2017, 37(1): 47-52.
[8] 张珊榕,董红英,马文,尹轶川,李新慧,白玉,贾瑞灵. 等离子喷涂SrZrO3热障涂层的CaO-MgO-Al2O3-SiO2 (CMAS) 腐蚀行为[J]. 中国腐蚀与防护学报, 2017, 37(1): 53-57.
[9] 陈琛, 郭洪波, 宫声凯. 横向梯度温度场下热障涂层的失效分析[J]. 中国腐蚀与防护学报, 2013, 33(5): 400-406.
[10] 吴进怡,罗琦,肖伟龙,柴柯,曹阳. 海水环境中弧菌对45钢腐蚀行为及力学性能的影响[J]. 中国腐蚀与防护学报, 2012, 32(4): 343-348.
[11] 任研研,郭宁,吴明铂. 渗硼提高炭材料抗氧化性研究进展[J]. 中国腐蚀与防护学报, 2012, 32(3): 183-188.
[12] 钟曼英. 氢对2(1/4)Cr-1Mo钢力学性能的影响[J]. 中国腐蚀与防护学报, 2011, 31(3): 236-239.
[13] 赵羽习,任海洋. 基于固结试验和接触理论分析的铁锈力学性能[J]. 中国腐蚀与防护学报, 2010, 30(5): 383-390.
[14] 肖伟龙,柴柯,杨雨辉,吴进怡. 25钢在热带海洋环境下海水中的微生物腐蚀及其对力学性能的影响[J]. 中国腐蚀与防护学报, 2010, 30(5): 359-363.
[15] 薛艳;赵国仙;董会;赵大伟. 5Cr油管电化学充氢后的力学行为[J]. 中国腐蚀与防护学报, 2010, 30(1): 89-92.