N80钢在模拟深层气井水溶液中的CO2腐蚀行为

中国腐蚀与防护学报

2007, Vol. 27

Issue (1): 8-13

研究报告

本期目录 | 过刊浏览

N80钢在模拟深层气井水溶液中的CO2腐蚀行为

马文海;裴晓含;高飞;高纯良

大庆油田公司采油工程研究院采气工艺研究室

Corrosion Behavior of N80 Steel in Simulated Water from deep Gaswell Containing Carbon Dioxide

;;;

大庆油田公司采油工程研究院采气工艺研究室

全文: PDF(2263 KB)

摘要: 利用高压釜、扫描电镜（SEM）和X-射线衍射（XRD）等手段，研究了温度、CO2分压、Cl-浓度、pH值和流速等因素对N80钢在模拟深层气井水溶液中腐蚀行为的影响.结果表明，温度对腐蚀速率的影响很大，随着温度的升高，腐蚀速率先增大后减小，80℃时腐蚀速率达到最大值，生成的腐蚀产物主要为FeCO3；降低溶液pH值、增加溶液中的Cl-浓度、提高CO2分压以及介质的流速，均加剧了N80钢的腐蚀.

关键词 ： CO2腐蚀, N80钢, 腐蚀速率, 腐蚀产物膜

Abstract：Factors influencing corrosion rate of N80 steel in carbon dioxide environment were studied using autoclave,SEM and XRD.The results indicated that the temperature remarkably affects the characterization of corrosion product,and the corrosion rate increases along with the increasing of temperature up to 80℃,then reduces dramatically due to the formation of a protective layer on the surface of steel.Corrosion product was proved to be FeCO3 in higher temperature.Corrosion will be aggravated by reducing pH value and increasing the Cl- concentration,CO2 partial pressure and the flow velocity of solution.

Key words： CO2 Corrosion N80 steel Corrosion rate Corrosion products

收稿日期: 2006-05-29

ZTFLH:

TG172

通讯作者: 马文海 E-mail: mawenhai@petrochina.com.cn;soso.0123@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	马文海
	裴晓含
	高飞
	高纯良
44.8K

引用本文:

马文海; 裴晓含; 高飞; 高纯良 . N80钢在模拟深层气井水溶液中的CO2腐蚀行为[J]. 中国腐蚀与防护学报, 2007, 27(1): 8-13 .
. Corrosion Behavior of N80 Steel in Simulated Water from deep Gaswell Containing Carbon Dioxide. J Chin Soc Corr Pro, 2007, 27(1): 8-13 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2007/V27/I1/8

[1]Heuer J K,Stubbins J F.An XPS characterization of FeCO3filmsfrom CO2corrosion[J].Corros.Sci.,1999,41(7):1231-1243
[2]Li J.Study on the corrosion behavior and mechanism of tubular steelin carbon dioxide environment[D].Beijing:USTB Doctor Disserta-tion,2000(李静.油管钢CO2腐蚀行为与机理研究[D].北京:北京科技大学博士学位论文,2000)
[3]Zhao J M,Gu M G,Zuo Y.Influencing factors on corrosion of mildsteel in carbon dioxide environment[J].J.Beijing Univ.Chem.Technol.,2005,32(5):71-74(赵景茂,顾明广,左禹.碳钢在二氧化碳溶液中腐蚀影响因素的研究[J].北京化工大学学报,2005,32(5):71-74)
[4]Li C F,Wang B,Zhang Y.Reseach progress of CO2corrosion in oil/gas field exploitation[J].J.Southwest Petroleum Institute,2004,26(2):42-45(李春福,王斌,张颖等.油气田开发中CO2腐蚀研究进展[J].西南石油学院学报,2004,26(2):42-45)
[5]De Waard.Predictive model for CO2corrosion engineering in wetnatural gas pipelines[J].Corrosion,1991,47(12):977-985
[6]Lopez D A,Perez T,Simison S N.The influence of microstructureand chemical composition carbon and low alloy steels in CO2corro-sion.A state-of-the-art appraisal[J].Mater.Des.,2003,24(8):561-575
[7]Wu S L,Cui Z D,He F,Bai Z Q,Zhu S L,Yang X J.Characteriza-tion of the surface film formed from carbon dioxide corrosion on N80steel[J].Mater.Lett.,2004,58(6):1076-1081
[8]Lin G F,Bai QZ,Zhao X W,Zheng MS,Lu MX.Effect of tempera-ture on scales of carbon dioxide corrosion products[J].Acta PetroleiSin.,2004,25(3):101-105(林冠发,白真权,赵新伟,郑茂盛,路民旭.温度对二氧化碳腐蚀产物膜形貌特征的影响[J].石油学报,2004,25(3):101-105)
[9]Wan L P,Meng Y F,Liang F S.Carbon dioxide corrosion and its in-fluence factors in oil/gas field exploitation[J].Total Corrosion andControl,2003,17(2):14-17(万里平,孟英峰,梁发书.油气田开发中的二氧化碳腐蚀及影响因素[J].全面腐蚀控制,2003,17(2):14-17)
[10]Li Q A,Zhang Q,Wen J B,Bai Z Q.Prediction and prevention ofCO2corrosion of oil tubular goods[J].Corros.Sci..Prot.Technol.,2004,16(6):381-384(李全安,张清,文九巴,白真权.CO2对油气管材的腐蚀规律及预测防护[J].腐蚀科学与防护技术,2004,16(6):381-384)
[11]Mao X,Liu X,Revie R W.Pitting corrosion of pipeline steel in di-lute bicarbonate solution with chloride ions[J].Corrosion,1994,50(9):651-657

[1]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[2]	白海涛, 杨敏, 董小卫, 马云, 王瑞. CO₂腐蚀产物膜的研究进展[J]. 中国腐蚀与防护学报, 2020, 40(4): 295-301.
[3]	赵国仙,黄静,薛艳. 某油田地面集输管道用材腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 557-562.
[4]	孙永伟,钟玉平,王灵水,范芳雄,陈亚涛. 低合金高强度钢的耐模拟工业大气腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 274-280.
[5]	刘丽,于思荣. 添加Gd对AM60镁合金耐腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 185-191.
[6]	黄博博,刘平,刘新宽,梅品修,陈小红. 新型HSn70-1铜网衣两年期海水腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 594-600.
[7]	李洋, 李承媛, 陈旭, 杨佳星, 王欣彤, 明男希, 韩镇泽. 超级13Cr不锈钢在海洋油气田环境中腐蚀行为灰关联分析[J]. 中国腐蚀与防护学报, 2018, 38(5): 471-477.
[8]	鲍明昱, 任呈强, 胡静思, 刘博, 李佳蒙, 王丰, 刘丽, 郭小阳. 油气管材应力诱导腐蚀电化学行为探讨[J]. 中国腐蚀与防护学报, 2017, 37(6): 504-512.
[9]	韩帅豪,岑宏宇,陈振宇,邱于兵,郭兴蓬. 原油与高压CO₂共存条件下咪唑啉缓蚀剂的作用行为研究[J]. 中国腐蚀与防护学报, 2017, 37(3): 221-226.
[10]	宋丰轩,赵启忠,李飞龙,任月路,黄奎,张新明. 不同时效态7050铝合金板材腐蚀速率测量[J]. 中国腐蚀与防护学报, 2017, 37(3): 287-292.
[11]	朱明,余勇,张慧慧. L245钢在不同温度下的油气田模拟水中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(3): 300-304.
[12]	张子阳,王善林,章恒瑜,柯黎明. AZ31镁合金搅拌摩擦焊接头腐蚀行为[J]. 中国腐蚀与防护学报, 2017, 37(2): 117-125.
[13]	白强,邹妍,孔祥峰,高杨,刘岩,董胜. 奥氏体焊条水下湿法焊接CCSE40钢在海水中的腐蚀电化学行为研究[J]. 中国腐蚀与防护学报, 2016, 36(5): 427-432.
[14]	张弟,梁平,张云霞,史艳华,秦华. 库尔勒土壤模拟溶液中形成的腐蚀产物膜对X80钢点蚀行为的影响[J]. 中国腐蚀与防护学报, 2016, 36(4): 313-320.
[15]	王春霞,陈敬平,张晓红,王赪胤. 溴化N-辛烷异喹啉在盐酸溶液中对Q235碳钢的缓蚀行为[J]. 中国腐蚀与防护学报, 2016, 36(3): 245-252.

Viewed

Full text

Abstract

Cited

Shared

Discussed